Anti-aging PC-PMMA plastic alloy

A technology of PC-PMMA and plastic alloy, which is applied in the field of plastic alloy, can solve the problems of poor anti-aging performance and achieve excellent thermal aging performance, hardness, not easy to scratch, and good fluidity

Inactive Publication Date: 2013-10-23
珠海新奥林科技园有限公司
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the current PC-PMMA plastic alloys have poor aging resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Each raw material was weighed according to the data corresponding to Example 1 in Table 1. Add each component into a high-speed mixer, control the rotation speed at 300-400 rpm at room temperature, mix for 5-10 minutes, take it out and transfer it to a screw extruder, extrude and granulate at a temperature of 235°C to obtain Anti-aging PC-PMMA plastic alloy.

[0020] Table 1: Anti-aging PC-PMMA plastic alloy formula table Unit: kg

[0021]

Example 1

Example 2

Example 3

Example 4

PC resin

100

100

100

100

PMMA resin

20

20

20

20

Compatibilizer SEBS-g-MAH

3

3

3

3

4,4'-Thiobis(6-tert-butyl-3-methylphenol)

0.4

0.8

/

0.5

1,1,3-tris(2-methyl-4-hydroxy-5-tert-butylphenyl)butane

0.4

/

0.8

0.5

Dioctadecyl Thiodipropionate

0.2

0.2

0.2

/

[0022] The PC resin is the injection molding grade PC resin of Teijin Comp...

Embodiment 2-4

[0026] Each raw material was weighed according to the data corresponding to Examples 2-4 in Table 1. The method described in Example 1 was used to prepare the anti-aging PC-PMMA plastic alloy.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
heat deflection temperatureaaaaaaaaaa
transmittivityaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-aging PC-PMMA plastic alloy composed of the components of, by weight: 100 parts of PC, 16-24 parts of PMMA, 2-4 parts of a compatibilizer, and 0.5-1.5 parts of an anti-aging agent. The anti-aging PC-PMMA plastic alloy provided by the invention has good filling mobility, excellent processing performance, high impact resistance, chemical resistance, high hardness, and scratch resistance. The anti-aging PC-PMMA plastic alloy provided by the invention can be used in communication device housing with high surface hardness and foodstuff packages with high requirement on surface gloss.

Description

technical field [0001] The invention relates to a plastic alloy, in particular to an anti-aging PC-PMMA plastic alloy. Background technique [0002] PMMA is a thermoplastic with excellent weather resistance, high surface hardness, good processing performance, high transparency, light transmittance as high as 91-93%, and 99% of visible light and ultraviolet light. 72%, light weight, with outstanding weather resistance. PC has poor fluidity, is prone to internal stress, is sensitive to notch impact, has poor wear resistance, and has a visible light transmittance of 88%, which can meet the transparency requirements. The heat distortion temperature is as high as 120-143°C, and it has good heat resistance. ; The molding shrinkage rate is only 0.5-0.7%, and the dimensional stability is good; and the impact strength of PC is high. The above two materials are favored by people because of their good light transmittance, flat and clean surface, and the blend has beautiful pearl lust...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L33/12C08K5/375C08K5/13C08K5/372
Inventor 黄美蓉
Owner 珠海新奥林科技园有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products