Rhodium reduction activation dissolution method

A technology of activator and rhodium waste, which is applied in the field of precious metal metallurgy, can solve the problems of slow dissolution speed and achieve the effects of low dissolution temperature, short process flow and simple operation

Active Publication Date: 2013-07-24
GUIYAN RESOURCE YIMEN
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The advantage of the electrochemical dissolution method is that no new impurities are introduced during the dissolution process, and the electrolyte can directly enter the subsequent refining process. The disadvantage is that the dissolution rate is slow

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rhodium reduction activation dissolution method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A, rhodium waste crushing and grinding: 100 grams of waste platinum catalytic network aqua regia insoluble residue, rhodium content is 82.23%, rhodium 82.23 grams, crushing and grinding with disc crusher, cross 300 mesh sieves.

[0025] B, mix with activator: the rhodium waste material after the crushing that step A makes is fully mixed with 300 grams of 200 mesh zinc powders.

[0026] C. Acid dissolution activation: In a closed 2L glass reactor, first add 800ml of industrial hydrochloric acid, the concentration of hydrochloric acid is 10mol / L, add the mixture while stirring, the stirring speed is 120 rpm, and the reaction rises to 95°C. Keep warm for 60 minutes.

[0027] D. Filtration: filter the solution after the reaction in step C to obtain a filter residue, wash the filter residue 8 times with hot water at 75° C. for 3 times to obtain a reduced and activated rhodium material.

[0028] E. Dissolution: Put the reduced and activated rhodium material obtained in step ...

Embodiment 2

[0030] A, rhodium waste crushing and grinding: 100 grams of organic rhodium waste slag, rhodium content is 18.67%, containing rhodium 18.67 grams, crushing and grinding with disc crusher, cross 280 mesh sieves.

[0031] B, mix with activator: the rhodium waste material after the crushing that step A makes is fully mixed with 200 grams of 250 mesh zinc powders.

[0032]C. Acid dissolution activation: In a closed 2L glass reactor, first add 500ml of industrial hydrochloric acid, the concentration of hydrochloric acid is 12mol / L, add the mixture while stirring, the stirring speed is 80 rpm, and the reaction rises to 60°C. Keep warm for 80 minutes.

[0033] D. Filtration: Filter the solution after the step C reaction is completed to obtain a filter residue, which is washed twice with hot water at 85°C 12 times the filter residue to obtain a reduced and activated rhodium material.

[0034] E. Dissolution: Put the reductively activated rhodium material obtained in step D into a gla...

Embodiment 3

[0036] A, rhodium waste crushing and grinding: coarse rhodium powder 100 grams, content 98.10%, containing 98.1 grams of rhodium, crushing and grinding with disc crusher, cross 200 mesh sieves.

[0037] B, mix with activator: the rhodium waste material after the crushing that step A makes is fully mixed with 500 grams of 300 mesh zinc powders.

[0038] C. Acid dissolution activation: In a closed 3L glass reactor, first add 1000ml of industrial hydrochloric acid, the concentration of hydrochloric acid is 11mol / L, add the mixture while stirring, the stirring speed is 80 rpm, and the reaction rises to 80°C. Keep warm for 40 minutes.

[0039] D. Filtration: filter the solution after the reaction in step C to obtain a filter residue, and wash the filter residue once with hot water at 80°C 10 times of the filter residue to obtain a reduced and activated rhodium material.

[0040] E. Dissolution: Put the reductively activated rhodium material obtained in step D into a glass reactor,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a rhodium reduction activation dissolution method, and relates to the technical field of noble metal metallurgy. The rhodium reduction activation dissolution method can be used for overcoming the defects of the prior art and aims at achieving a rhodium dissolution method which has the advantages of high dissolution efficiency, wet method normal-pressure dissolution, easiness for operation, short process flow, low production cost and wide rhodium waste dissolution range. The technical scheme is as follows: the rhodium reduction activation dissolution method comprises the following steps of: A, crushing and grinding rhodium wastes; B, mixing with an activating agent; C, carrying out acid-soluble activation; D, filtering; and E, dissolving. According to the invention, because zinc powder and a hydrochloric acid solution generate chemical reaction in the step C to generate H2, rhodium oxide contained in the solution can be reduced into metal rhodium through H2 at 100 DEG C, the dissolution activity of rhodium can not be reduced and can be enhanced so as to be favorable to subsequent dissolution, and the rhodium oxide is reduced into the metal rhodium without being dissolved by hydrochloric acid in the activated process. Thus, the rhodium reduction activation dissolution method disclosed by the invention has the advantages of high rhodium dissolution efficiency, rhodium normal-pressure dissolution, low dissolution temperature, easiness for operation, short process flow, low production cost and wide rhodium waste dissolution range.

Description

technical field [0001] The invention relates to the technical field of precious metal metallurgy, in particular to a method for dissolving rhodium. Background technique [0002] Platinum group metals have high melting point, high strength, stable electric heating, high resistance to spark erosion, excellent corrosion resistance, strong high temperature oxidation resistance, and good catalytic activity. They are widely used in automobile exhaust purification, chemical industry, aerospace, glass fiber In the fields of industry, electronics and electrical industries, although the dosage is small, it plays a key role and is known as "industrial vitamin". Among the six platinum group elements, the price of rhodium was the most expensive, reaching 2.5 million yuan / kg, and the price fluctuated greatly. The chemical properties of rhodium in the solution are very complicated. During the refining process, it is usually recovered at the end, so the production cycle is relatively short....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B7/00C22B11/00
CPCY02P10/20
Inventor 吴喜龙贺小塘韩守礼郭俊梅谭文进王欢李勇刘文李子璇赵雨李红梅缪海才
Owner GUIYAN RESOURCE YIMEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com