Corrosion-resistant and wear-resistant composite metal plate

A composite metal plate and composite metal technology, applied in metal processing equipment, auxiliary welding equipment, welding equipment, etc., can solve problems such as discomfort and wear resistance, and achieve the effect of good sealing effect, reduction of transverse cracks, and strong penetration ability.

Inactive Publication Date: 2014-12-03
SHANDONG UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In view of the existence of transverse microcracks on the surface of the existing surfacing wear-resistant composite plate, which is not suitable for the anti-wear problem under corrosive working conditions, the purpose of the present invention is to provide a corrosion-resistant and wear-resistant composite metal plate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Prepare surfacing welding flux-cored welding wire, the diameter of the welding wire is Ф2.8mm, the steel strip is SPCC with a thickness of 0.35mm, and the composition of the deposited metal of the flux-cored welding wire is 5.5% by mass percentage, C is 5.5%, Cr is 30%, and B is 2.5%, Si 2.5%, Mn 5.0%, Mo 3.0%, V 1.5%, Ti 0.6%, Al 1.5%, Mg 1.5%, and the rest are Fe and impurities that do not affect the performance of the powder.

[0028] (2) Select Q235 low-carbon steel plate as the substrate, the size of the substrate is 1m×2m, and the thickness is 8mm. The four sides of the substrate are rigidly fixed on the welding platform by mechanical clamping.

[0029] (3) Single gun surfacing welding, the first welding bead is located in the center of the substrate width, and the surfacing welding is along the length direction of the substrate. The welding torch does not swing horizontally during surfacing, and the width of the weld bead is 20mm. After the surfacing of the...

Embodiment 2

[0034] (1) Prepare surfacing flux-cored welding wire, the diameter of the welding wire is Ф3.2mm, the steel strip is SPCC with a thickness of 0.35mm, and the composition of the deposited metal of the flux-cored welding wire is 5.0% by mass percentage, C is 5.0%, Cr is 28%, and Si is 1.5%, Mn is 3.0%, Mo is 3.0%, V is 1.5%, Ti is 0.2%, Al is 2.5%, Mg is 2.0%, and the rest is Fe and impurities that do not affect the performance of the powder.

[0035] (2) Select Q345 steel plate as the substrate, the size of the substrate is 1m×2m, and the thickness is 12mm. The four sides of the substrate are rigidly fixed on the welding platform by mechanical clamping.

[0036] (3) Single gun surfacing welding, the first welding bead is located in the center of the substrate width, and the surfacing welding is along the length direction of the substrate. During surfacing welding, the welding torch swings laterally, the swing amplitude of the welding torch swing is 10mm, the swing frequency is...

Embodiment 3

[0041] (1) Prepare surfacing welding flux-cored welding wire, the diameter of the welding wire is Ф3.2mm, and the steel strip is SPCC with a thickness of 0.35mm. 2.5%, Si is 2.5%, Mn is 5.0%, Mo is 4.0%, V is 1.5%, Ti is 1.2%, Al is 2.5%, Mg is 2.0%, and the rest is Fe and impurities that do not affect the performance of the powder.

[0042] (2) Select Q345 steel plate as the substrate, the size of the substrate is 1m×2m, and the thickness is 20mm. The four sides of the substrate are rigidly fixed on the welding platform by mechanical clamping.

[0043] (3) Single gun surfacing welding, the first welding bead is located in the center of the substrate width, and the surfacing welding is along the length direction of the substrate. During surfacing welding, the welding torch swings laterally, the swing amplitude of the welding torch is 20mm, the swing frequency is 20 times / min, and the weld bead width is 50mm. After the surfacing of the first bead is completed, the other welds...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a corrosion-resistant and wear-resistant composite metal plate. A low-carbon steel plate or a low-alloy steel plate is taken as a base plate, a special corrosion-resistant and wear-resistant bead weld flux-cored wire is arranged at a bead weld composite layer on the surface of the base plate to obtain a corrosion-resistant and wear-resistant composite metal plate blank, and flaws on the surface of the leveled composite metal plate blank is sealed by a prepared special gap seal agent to obtain the corrosion-resistant and wear-resistant composite metal plate. The composite metal plate disclosed by the invention is few in transverse flaws, and high in bonding force between the bead weld layer and the base plate; and the gap seal agent effectively leaks into the transverse flaws, so that the corrosion resistance of the composite metal plate can be observably improved, and the service life of the composite metal plate under the corrosion work condition can be observably prolonged.

Description

technical field [0001] The invention relates to a composite material, in particular to a corrosion-resistant and wear-resistant composite metal plate. Background technique [0002] Metal wear is one of the main reasons for the failure of mechanical parts, and the loss is staggering. According to incomplete statistics of my country's metallurgy, coal, electric power and other industries, the annual wear loss is as high as 2 billion yuan. Therefore, the research and development of high-performance wear-resistant materials are valued by material workers. Cast wear-resistant parts and surfacing wear-resistant parts are commonly used wear-resistant materials in the industrial field. [0003] Cast wear-resistant parts are manufactured by casting technology. Generally, the overall composition is uniform. For example, high manganese steel, white cast iron, chromium-based anti-wear cast iron, etc. have better anti-wear properties. However, these materials also have some shortcoming...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K9/04B23K35/24B23K37/00
Inventor 孙俊生李宁洋栾守成孙逸群
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com