High-flowability long glass fiber reinforced nylon 6 material and preparation method thereof

A high fluidity, long glass fiber technology, applied in the field of polymer materials, can solve the problems of reducing the impact toughness and rigidity of materials, and shortening the length of glass fibers, so as to improve rigidity and strength, ensure effective length, and improve surface quality. Effect

Inactive Publication Date: 2013-04-03
HEFEI GENIUS NEW MATERIALS
View PDF11 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the glass fiber directly enters the twin-screw of the extruder from the fiber feeding port, the shearing in the screw increases, and the length of the glass fiber in the product becomes shorter, which greatly reduces the impact toughness and rigidity of the material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) A long glass fiber-reinforced nylon 6 material with high fluidity, the material has a cutting length of 11-13mm and a particle size of 3.5mm, including the following components by weight: high fluidity nylon 6: 700 parts, continuous Glass fiber: 300 parts, antioxidant: 9 parts, lubricant: 5 parts, compatibilizer: 4 parts; Among them, high fluidity nylon 6 resin, the melt index is 320g / 10min, the test condition is 230 ℃, 2.16Kg ;The continuous glass fiber is alkali-free continuous glass fiber, the fiber diameter is 17μm, and the linear density is 2400g / km; the antioxidant includes N,N'-bis-(3-(3,5-di-tert-butyl-4-hydroxy Phenyl)propionyl)hexamethylenediamine (anti-1098) and tris[2.4-di-tert-butylphenyl]phosphite (anti-168), the weight ratio of the two is 1:2; the lubricant includes ethylene-acrylic acid Copolymer wax (AC540A) and calcium stearate (CaSt), the weight ratio of the two is 1:1; the compatibilizer is 3-aminopropyltriethoxysilane (KH-550).

[0029] (2) A m...

Embodiment 2

[0037] (1) A long glass fiber-reinforced nylon 6 material with high fluidity, comprising the following components by weight: high fluidity nylon 6: 600 parts, continuous glass fiber: 400 parts, antioxidant: 9 parts, lubricated agent: 5 parts, compatibilizer: 4 parts;

[0038] Among them, the high fluidity nylon 6 resin has a melt index of 340g / 10min, and the test condition is 230°C, 2.16Kg; the continuous glass fiber is alkali-free continuous glass fiber, the fiber diameter is 17μm, and the linear density is 3200g / km; the antioxidant Including N,N'-bis-(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionyl)hexamethylenediamine (anti-1098) and tris[2.4-di-tert-butylphenyl] Phosphate (anti-168), the weight ratio of the two is 1:2; the lubricant includes ethylene-acrylic acid copolymer wax (AC540A) and silicone, the weight ratio of the two is 1:1; the compatibilizer is 3- Aminopropyltriethoxysilane (KH-550).

[0039] (2) A method for preparing a high-fluidity long glass fiber reinforc...

Embodiment 3

[0047] (1) A high-fluidity long glass fiber reinforced nylon 6 material, comprising the following components by weight: high-fluidity nylon 6: 500 parts, continuous glass fiber: 500 parts, antioxidant: 9 parts 、 Lubricant: 5 parts, compatibilizer: 4 parts;

[0048] Among them, the high fluidity PA6 resin has a melt index of 360g / 10min, and the test condition is 230°C, 2.16Kg; the continuous glass fiber is alkali-free continuous glass fiber, the fiber diameter is 17μm, and the linear density is 4800g / km; the antioxidant includes N,N'-bis-(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionyl)hexamethylenediamine (anti-1098) and tris[2.4-di-tert-butylphenyl]phosphite Esters (anti-168), the weight ratio of the two is 1:2; the lubricant includes pentaerythritol stearate (PETS) and calcium stearate (CaSt), the weight ratio of the two is 1:1; compatible The agent is 3-aminopropyltriethoxysilane (KH-550).

[0049] (2) A method for preparing a high-fluidity long glass fiber reinforced nylo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
linear densityaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-flowability long glass fiber reinforced nylon 6 material. The high-flowability long glass fiber reinforced nylon 6 material is prepared by the following ingredients in parts by weight: 500-700 parts of high-flowability nylon 6, 300-500 parts of continuous glass fiber, 6-10 parts of antioxidant, 4-8 parts of lubricant, and 3-6 parts of compatilizer. The high-flowability long glass fiber reinforced nylon 6 material has higher rigidity and strength, as well as excellent impact resistance property, the surface appearance of injection-moulded parts is good, the material can be directly formed by injection moulding, the production efficiency is high, and the used parts can be recycled after being ground.

Description

[0001] technical field [0002] The invention relates to the technical field of polymer materials, in particular to a high-fluidity long glass fiber reinforced nylon 6 material and a preparation method thereof. Background technique [0003] Polyamide resin is a chemical raw material with excellent performance and wide application. Because of its non-toxic, light weight, excellent mechanical strength, wear resistance and good corrosion resistance, it is widely used to replace copper and other metals in machinery and chemical industry. Manufacture of bearings, gears, pump blades and other parts in industries such as instrumentation, automobiles, etc., but in some parts with relatively high strength requirements, especially in the military and aerospace fields, nylon 6 raw materials are difficult to meet their use requirements, and its During use, due to water absorption, size deformation occurs. To solve this problem, domestic and foreign enterprises have reinforced and modifi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08K13/04C08K7/14B29B9/06B29C47/92B29C48/92
CPCB29B9/14B29B7/46B29B7/72B29B7/7461B29B7/90B29B9/06B29B9/12
Inventor 杨桂生蒋超杰孙利明
Owner HEFEI GENIUS NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com