Glass magnesium decorative board manufacturing process

A manufacturing process and decorative board technology, applied in the direction of lamination device, lamination auxiliary operation, lamination, etc., can solve the problems of easy-fading surface effect design, low surface bonding strength, insufficient clarity, etc., to achieve bright color, High surface bonding strength and good brightness

Active Publication Date: 2015-09-16
ZHEJIANG DILONG NEW MATERIAL
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the defects of low surface bonding strength, insufficient clarity, easy fading and single surface effect design in the prior art, this method provides an environmentally friendly, fireproof, waterproof, and corrosion-resistant glass magnesium board as the base material. Decorative board production and manufacturing process, thereby reducing the production cost of decorative boards, reducing the large consumption of forest resources, and protecting the favorable development of the ecological environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass magnesium decorative board manufacturing process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Example 1 A glass magnesium plate with a thickness of 5 mm is used as the base plate,

[0036] Follow the steps below:

[0037] Step (1): Configure the melamine resin adhesive:

[0038] The base material glue is composed of the following raw materials in the weight ratio: 140kg of formaldehyde solution with a concentration of 36.8% to 37.2% by weight, 110kg of melamine, 65kg of soft water, and 8kg of caprolactam;

[0039] The additives are added after the base glue is made, 0.65kg penetrating agent, 0.32kg antisticking agent, 0.48kg release agent, 0.48kg curing agent and 6.5kg brightening agent.

[0040] The penetrating agent is W7-320 penetrating agent produced by Germany Discovery Star, and its main component is surfactant; the curing agent is 710 curing agent produced by German Woods, and the main component is acidic substances; the release agent is 523 produced by German Woods Release agent, the cured plate is easy to separate from the stainless steel plate after...

Embodiment 2

[0055] Example 2 A glass magnesium plate with a thickness of 9 mm is used as the base material,

[0056] Follow the steps below:

[0057] Step (1): Configure the melamine resin adhesive:

[0058] The raw materials of the base glue are 120kg of 37% formaldehyde solution, 95kg of melamine, 60kg of soft water, and 6kg of caprolactam;

[0059] Auxiliaries are added after the base glue is made, 0.281kg penetrating agent, 0.14kg anti-sticking agent, 0.03kg release agent, 0.14kg curing agent and 0.281kg brightening agent.

[0060] The penetrating agent is alkylbenzene sulfonate; the anti-sticking agent is a solvent-based silicone release agent; the release agent is a purchased melamine resin release agent; the curing agent is a curing agent purchased from Hangzhou Linan Mingsheng Chemical Co., Ltd.; The brightener is phenylacetic acid.

[0061] The preparation method of melamine resin adhesive is to mix formaldehyde and soft water and adjust its pH value to between 9.0 and 9....

Embodiment 3

[0076] Example 3 A glass magnesium plate with a thickness of 12 millimeters is used as a substrate,

[0077] Next follow the steps below:

[0078] Step (1): Configure the melamine resin adhesive:

[0079] The raw materials of the base glue include 140kg of 37.2% formaldehyde solution, 115kg of melamine, 70kg of soft water, and 10kg of caprolactam;

[0080] The additives are added after the base material glue is made, 1kg penetrating agent, 0.67 kg anti-adhesive agent, 1 kg release agent, 0.35 kg curing agent and 3.35 kg brightening agent.

[0081] The penetrating agent is W7-320 penetrating agent produced by Germany Discovery Star, and its main component is surfactant; the curing agent is 710 curing agent produced by German Woods, and the main component is acidic substances; the release agent is 523 produced by German Woods Release agent, the cured plate is easy to separate from the stainless steel plate after pressing.

[0082] Configuration method Mix formaldehyde with so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a manufacturing process for a glass-magnesium decorative plate. The glass-magnesium decorative plate is composed of a substrate plate and melamine impregnated paper, wherein the substrate plate is a glass-magnesium flat plate; and the melamine impregnated paper is decorative paper impregnated by melamine glue. The manufacturing process disclosed by the invention comprises the following steps of: impregnating the high-brightness decorative paper, pre-processing the glass-magnesium flat plate, pressing and sticking the glass-magnesium flat plate at a high temperature, so as to obtain the glass-magnesium decorative plate. The manufacturing process disclosed by the invention is easy to operate. The surface of the manufactured decorative plate is attractive in color. The glass-magnesium decorative plate has the special performances of being environment-friendly, energy-saving, light in weight, fireproof and the like and is widely applied in public places, such as suspended ceilings, indoor partition walls and door plates, as well as applied in high-grade places, such as office buildings and entertainment places.

Description

technical field [0001] The invention belongs to the technical field of decorative materials, in particular to a manufacturing process of a glass magnesium decorative board. Background technique [0002] At present, most of the decorative board materials are made of wooden substrates with decorative paper or paint. The production principle is to compound the decorative paper on the surface of wood-based panels. The fire resistance, water resistance, anti-corrosion, environmental protection and robustness of the material. In addition, the large-scale production of wood-based decorative panels will consume a large amount of forest resources, seriously affecting the ecological development of human beings. At present, the price of wood-based substrates in the market continues to increase, and the shortage of resources will become more and more serious, resulting in the loss of wood-based substrates. Production costs continue to increase, therefore, it is necessary to find a base...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B37/06B32B37/10B32B38/16B32B38/18
Inventor 姜飞雄朱玉华方敏张海峰
Owner ZHEJIANG DILONG NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap