Net-flavor full-matt ultraviolet-curing coating and preparation method thereof

A technology of curing coatings and ultraviolet light, applied in polyester coatings, coatings, etc., can solve the problems of not being able to achieve clean smell, polluting the environment, etc., and achieve the effects of increasing adhesion, good acidity and alkalinity, and short construction period

Active Publication Date: 2013-02-13
濮阳展辰新材料有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The coating proposed in this patent has no residual irritating odor after curing, but it does not have the function of "clean odor" when it is painted, and it still pollutes the environment during the manufacturing process before curing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Net-flavor full-matt ultraviolet-curing coating and preparation method thereof
  • Net-flavor full-matt ultraviolet-curing coating and preparation method thereof
  • Net-flavor full-matt ultraviolet-curing coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment 1: Pure odor full matt UV photocurable coating

[0045] The weight percentages of raw materials are shown in Table 1.

[0046] Table 1: Raw material ratio of embodiment 1

[0047] composition

Weight percentage (%)

6316 UV curable resin

31

DPGDA

29

HDDA

12

TMPTA

9.2

Organic matte powder RAD-2105

12

Wax powder 178-VF

1

Leveling agent TEGO-410

0.3

Photoinitiator

4.0

Defoamer BYK-055

0.5

Wetting and dispersing agent BYK-P-104

1.0

total

100

[0048] Preparation:

[0049] 1) First, mix 6316, DPGDA, HDDA, and TMPTA evenly, then disperse for 22 minutes with a disperser (Yixing Jingyi Machinery GFJ-B-75Kw);

[0050] 2) Then add wetting and dispersing agent and leveling agent to disperse at medium speed for 10 minutes under stirring, then add wax powder, organic matte powder and photoinitiator into the disp...

Embodiment 2

[0056] Embodiment 2: Pure and odorless UV light-cured coating

[0057] The weight percentage of raw materials is shown in Table 3.

[0058] Table 3: Raw material ratio of embodiment 2

[0059] composition

Weight percentage (%)

6316 UV curable resin

33

DPGDA

27.5

HDDA

10

TMPTA

9.2

Organic matte powder RAD-2105

13

Wax powder 178-VF

1.5

[0060] Leveling agent TEGO-410

0.3

Photoinitiator

4.0

Defoamer BYK-055

0.5

Wetting and dispersing agent BYK-P-104

1.0

total

100

[0061] Preparation:

[0062] 1) First, stir 6316, DPGDA, HDDA, TMPTA evenly and then disperse for 25 minutes;

[0063] 2) Then add wetting and dispersing agent and leveling agent to disperse at medium speed for 10 minutes under stirring, then add wax powder, matte powder and photoinitiator into the stirring disperser, stir evenly and disperse for...

Embodiment 3

[0069] Embodiment 3: pure odor full matt UV photocurable coating

[0070] The weight percentage of raw materials is shown in Table 5.

[0071] Table 5: Raw material ratio of embodiment 3

[0072] composition

Weight percentage (%)

6316 UV curable resin

29.2

DPGDA

29

HDDA

12

TMPTA

8

Organic matte powder RAD-2105

14

Wax powder 178-VF

2

Leveling agent TEGO-410

0.3

Photoinitiator

4.0

Defoamer BYK-055

0.5

Wetting and dispersing agent BYK-P-104

1.0

total

100

[0073] Preparation:

[0074] 1) First, stir 6316, DPGDA, HDDA, TMPTA evenly and then disperse for 20 minutes;

[0075] 2) Then add wetting and dispersing agent and leveling agent to disperse at medium speed for 10 minutes under stirring, then add wax powder, matte powder and photoinitiator into the stirring disperser, stir evenly and disperse at high speed for 22 mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a net-flavor full-matt ultraviolet-curing coating, which is prepared from the following components by weight percentage: 20-35 percent of ultraviolet curing resin, 40-57 percent of reactive acrylate monomers, 8.0-14 percent of organic matt powder, 0.8-4.0 percent of wax powder, 3.0-10 percent of photoinitiator, 0.2-0.5 percent of defoamer, 0.2-1.0 percent of flatting agent and 0.5-2.0 percent of wetting dispersant. The method is as follows: ultraviolet curing modified polyester acrylic resin with 90-98 percent of solid content is adopted to obtain the moderate hardness of paint film; and three kinds of reactive monomers are combined, the total content percentage of the monomers in the coating is reduced, the adhesive force, the hardness, the hand feeling, the glossiness and the fullness of paint film are increased, and the problems of odor, luster and the like before and after construction are solved. The selected resin is resin with a low functional group, and the reactive monomers are N-contained monomers. The coating has the adhesive force to various base materials, has low odor and is full-matt.

Description

technical field [0001] The invention belongs to the field of coating compositions, and in particular relates to a coating composition containing organic macromolecules and a preparation method thereof. Background technique [0002] Due to the advantages of short recoating time, high production efficiency, and environmental protection, UV-curable coatings have developed rapidly. However, nitro coatings, unsaturated resin coatings, and polyurethane coatings are all inferior to UV light-curing coatings due to their environmental protection, efficiency, and production costs. Especially in terms of environmental protection, it is also inferior to UV light-curing coatings. Analysis and experimental testing of the formulations commonly used in the existing UV photocuring coating technology, combined with the experimental data of the market, can summarize the understanding of the regularity, that is, a formula composed of a variety of acrylic compounds, produced during the photocur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/06C09D7/12
Inventor 张君彭钧浪罗先平孙倩
Owner 濮阳展辰新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com