A kind of odor-cleaning all-dumb ultraviolet light curing coating and preparation method thereof
A technology of curing coatings and ultraviolet light, applied in polyester coatings, coatings, etc., can solve the problems of polluting the environment, failing to achieve clean taste, etc., achieving the effects of good acidity and alkalinity, increased adhesion, and low shrinkage rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0044] Embodiment 1: Pure odor full matt UV photocurable coating
[0045] The weight percentages of raw materials are shown in Table 1.
[0046] Table 1: Raw material ratio of embodiment 1
[0047] composition
Weight percentage (%)
6316 UV curable resin
31
DPGDA
29
HDDA
12
TMPTA
9.2
Organic matte powder RAD-2105
12
Wax powder 178-VF
1
Leveling agent TEGO-410
0.3
Photoinitiator
4.0
Defoamer BYK-055
0.5
Wetting and dispersing agent BYK-P-104
1.0
total
100
[0048] Preparation:
[0049] 1) First, mix 6316, DPGDA, HDDA, and TMPTA evenly, then disperse for 22 minutes with a disperser (Yixing Jingyi Machinery GFJ-B-75Kw);
[0050] 2) Then add wetting and dispersing agent and leveling agent to disperse at medium speed for 10 minutes under stirring, then add wax powder, organic matte powder and photoinitiator into the disp...
Embodiment 2
[0056] Embodiment 2: Pure and odorless UV light-cured coating
[0057] The weight percentage of raw materials is shown in Table 3.
[0058] Table 3: Raw material ratio of embodiment 2
[0059] composition
Weight percentage (%)
6316 UV curable resin
33
DPGDA
27.5
HDDA
10
TMPTA
9.2
Organic matte powder RAD-2105
13
Wax powder 178-VF
1.5
[0060] Leveling agent TEGO-410
0.3
Photoinitiator
4.0
Defoamer BYK-055
0.5
Wetting and dispersing agent BYK-P-104
1.0
total
100
[0061] Preparation:
[0062] 1) First, stir 6316, DPGDA, HDDA, TMPTA evenly and then disperse for 25 minutes;
[0063] 2) Then add wetting and dispersing agent and leveling agent to disperse at medium speed for 10 minutes under stirring, then add wax powder, matte powder and photoinitiator into the stirring disperser, stir evenly and disperse for...
Embodiment 3
[0069] Embodiment 3: pure odor full matt UV photocurable coating
[0070] The weight percentage of raw materials is shown in Table 5.
[0071] Table 5: Raw material ratio of embodiment 3
[0072] composition
Weight percentage (%)
6316 UV curable resin
29.2
DPGDA
29
HDDA
12
TMPTA
8
Organic matte powder RAD-2105
14
Wax powder 178-VF
2
Leveling agent TEGO-410
0.3
Photoinitiator
4.0
Defoamer BYK-055
0.5
Wetting and dispersing agent BYK-P-104
1.0
total
100
[0073] Preparation:
[0074] 1) First, stir 6316, DPGDA, HDDA, TMPTA evenly and then disperse for 20 minutes;
[0075] 2) Then add wetting and dispersing agent and leveling agent to disperse at medium speed for 10 minutes under stirring, then add wax powder, matte powder and photoinitiator into the stirring disperser, stir evenly and disperse at high speed for 22 mi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com