Adhesive tape used for solar cell assembly and preparation method thereof

A technology of solar cells and tapes, applied in the direction of electrical components, circuits, adhesives, etc., can solve the problems of affecting the sealing performance of adhesives, affecting the application effect, slow curing speed, etc., and achieve good initial adhesion, cost reduction, and easy bonding.

Inactive Publication Date: 2012-12-12
SUZHOU DATONG ADVANCED MATERIAL
View PDF2 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the use of silicone adhesives, there are some problems, such as easy to produce bubbles and bubbling problems during the production and use of silicone adhesives, which affect the sealing performance of the adhesive; slow curing speed and long time; and yellowing during storage , affect the application effect, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The adhesive coated on the front side of the adhesive tape substrate is mainly used for bonding. In parts by weight, the components and content of the adhesive are:

[0029] Ammonium Sulfate (APS)

0.5 parts

Methyl methacrylate (MMA)

8 servings

Butyl Acrylate (BA)

65 copies

Hydroxymethylacrylamide (HAM)

27 copies

complex emulsifier

1.5 servings

2-Acrylamido-2-methylpropanesulfonic acid (AMPS)

1.3 parts

[0030] tackifying resin

60 copies

Acrylic (AA)

0.5 parts

Hydroxyethyl Methacrylate (HEA)

0.9 parts

3-Methacryloxypropyltrimethoxysilane (MPTS)

2 copies

[0031]The binder is first prepared in a reactor equipped with a condenser, mechanical stirrer and dropping funnel, nitrogen inlet and outlet, and a thermometer. Adopt the pre-emulsification process, pass through the nitrogen protection, weigh the components according to the above formula: HAM, ...

Embodiment 2

[0034] 1. The adhesive coated on the front of the tape base material is mainly used for bonding. In parts by weight, the components and contents of the adhesive are:

[0035] Ammonium Sulfate (APS)

[0036] 3-Methacryloxypropyltrimethoxysilane (MPTS)

[0037] The binder is first prepared in a reactor equipped with a condenser, mechanical stirrer and dropping funnel, nitrogen inlet and outlet, and a thermometer. Weigh the components according to the above formula: HAM, BA, MMA, AA, HEA, AMPS, SDS, OP-10 and 300ml of deionized water are loaded into the reactor, stirred and pre-emulsified for 1 hour. Then take 200ml of pre-emulsion, add sodium bicarbonate to adjust the pH to about 5, add 15ml of initiator APS (20%) solution, add in the reactor, continue nitrogen protection, control the temperature at 85 ° C, start the stirrer, and control the speed At 400r / min. When the material in the reactor gradually turned into a micro-blue seed emulsion, the remaining mo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a double-sided adhesive tape, and specifically relates to the double-sided adhesive tape used for a solar cell assembly and a preparation method thereof. The double-sided adhesive tape comprises a substrate, an adhesive, a backlining and backlining glue, wherein the adhesive mainly comprises the following components of, by weight, 0.5-1 part of ammonium sulfate, 5-10 parts of methyl methacrylate, 55-65 parts of butyl acrylate, 20-30 parts of hydroxymethyl acrylamide, 1-2 parts of a composite emulsifier, 60-70 parts of a tackifying resin, 0.2-0.8 part of acrylic acid, 1-2 parts of hydroethyl methacrylate, 1-1.5 parts of 2-acrylamide-2-methylpro panesulfonic acid and 1-3 parts of 3-(methacryloxy)propyltrimethoxysilane. The preparation method comprises the steps of firstly pre-preparing a high-strength organosilicone and acrylate co-polymeric emulsion pressure-sensitive adhesive; and then performing operations of double roll reverse coating, drying, compositing, transferring and the like with a B-50 multifunctional coating machine, wherein both the font side and the back side of the backlining of the substrate are already coated by a layer of low-adhesivity backlining glue.

Description

technical field [0001] The invention relates to a double-sided adhesive tape, in particular to a double-sided adhesive tape used for packaging solar cell modules and a manufacturing method thereof. Background technique [0002] Solar photovoltaic power is currently the most economical, cleanest and most environmentally friendly sustainable energy available. Solar cells are the core components of solar photovoltaic systems. Due to physical and chemical defects such as thinness, brittleness and easy oxidation of solar cells, long-term exposure to high humidity, high temperature, low temperature, strong ultraviolet rays, ozone, microorganisms, wind and rain and other natural conditions can easily cause water permanent damage, and it is difficult to application. Therefore, in order to realize the industrialized application of solar power generation, especially to achieve a service life of more than 20 years, protective packaging is required to form a solar cell module with sta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J7/02C09J133/08C08F220/18H01L31/048
CPCY02E10/50
Inventor 任天斌王永涛刘新武传业
Owner SUZHOU DATONG ADVANCED MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com