Heat treatment method of high-chromium martensitic stainless steel

A heat treatment method and high chromium martensite technology, applied in the field of stainless steel heat treatment, can solve the problems of oil pollution, easy ignition, low safety factor, etc. Effect

Active Publication Date: 2012-10-10
HENAN ZHONGYUAN SPECIAL STEEL EQUIP MFG CO LTD
View PDF3 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After the 4Cr16Mo stainless steel products are heat treated according to the conventional process, although the mechanical properties can be guaranteed, but because oil is used as the cooling medium during quenching, the oil fumes during production are relatively large, resulting in serious oil pollution in the heat treatment furnace, crane and production site, and due to the size of the workpiece Larger (the maximum diameter is about 450mm, the length is about 10m, and the weight of the forging is about 10t), the quenching temperature is high, and it is easy to catch fire when it is cooled in a horizontal oil tank, and the safety factor is low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat treatment method of high-chromium martensitic stainless steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A heat treatment method for high chromium martensitic stainless steel, the method is as follows:

[0020] 1) Annealing

[0021] Put the forged stainless steel workpiece into the furnace at a surface temperature of 650°C, put it into a furnace at 700°C, and raise the temperature to 830°C at a heating rate of 100°C / h, and the holding time is 2.3 to 2.7 hours / 100mm Calculation, that is, calculate the holding time according to the length of the workpiece. After the holding is over, cool down with the furnace at a cooling rate of 30°C / h to 80-200°C and leave the furnace for air cooling;

[0022] 2) Preheat

[0023] After the annealing process, the stainless steel forgings are preheated twice at the furnace temperature of 300°C. The first preheating temperature is 560°C, and the holding time is 4h. The second preheating temperature is 820°C, and the holding time is 4h;

[0024] 3) Quenching

[0025] After twice preheating, the quenching temperature of the forging is 1060°C...

Embodiment 2

[0029] A heat treatment method for high chromium martensitic stainless steel, the method is as follows:

[0030] 1) Annealing

[0031] Put the forged stainless steel workpiece into the furnace at 700°C at a furnace temperature of 700°C, and raise the temperature to 830°C at a heating rate of 60°C / h. The holding time is calculated at 2.3 to 2.7 hours / 100mm. After the heat preservation is over, cool down with the furnace at a cooling rate of 10°C / h to 80°C and leave the furnace for air cooling;

[0032] 2) Preheat

[0033] The stainless steel forgings that have undergone the annealing process are preheated twice at a furnace temperature of 400°C. The first preheating temperature is 480°C, and the holding time is 1h. The second preheating temperature is 760°C, and the holding time is 1h;

[0034] 3) Quenching

[0035] After twice preheating, the forging is quenched at a quenching temperature of 950°C and the holding time is 0.8 to 1.3 hours / 100mm, so that the center of the wor...

Embodiment 3

[0039] A heat treatment method for high chromium martensitic stainless steel, the method is as follows:

[0040] 1) Annealing

[0041] Put the forged stainless steel workpiece into the furnace at 660°C at the furnace temperature of 660°C, and heat it up to 850°C at a heating rate of 80°C / h. The holding time is calculated at 2.3 to 2.7 hours / 100mm. After the heat preservation is over, cool down with the furnace to 140°C at a cooling rate of 20°C / h and leave the furnace for air cooling;

[0042] 2) Preheat

[0043] After the annealing process, the stainless steel forgings are preheated twice at a furnace temperature of 100°C. The first preheating temperature is 520°C, and the holding time is 2.5h. The second preheating temperature is 790°C, and the holding time is 2.5h;

[0044] 3) Quenching

[0045] After twice preheating, the forgings are quenched at a quenching temperature of 1000°C and the holding time is 0.8 to 1.3 hours / 100mm, so that the central part of the workpiece r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a stainless-steel heat treatment technology, in particular to a heat treatment method of high-chromium martensitic stainless steel. The heat treatment method comprises the following steps of: 1) annealing; 2) preheating; 3) quenching; and 4) tempering. The heat treatment method has the following advantages that 4Cr16Mo stainless steel heat treatment process comprises the following procedures of: (1) complete annealing, controlling the furnace entering temperature after forging, the heating speed, the heating temperature, the insulating time and the furnace cooling speed; (2) quenching heating, controlling the preheating temperature, the heating speed, the heating temperature and the insulating time; (3) quenching cooling, adopting a gap-cooling mode of air-liquid-air-liquid-air-liquid, the quenching stress is furthest reduced while ensuring that a workpiece obtains enough quenching cooling severity and obtains a martensitic structure, and the cracking of the workpiece caused by excessive stress is avoided; and (4) tempering, strictly controlling the tempering furnace-entering time, tempering heating temperature and the insulating time, the structure transformation is complete, the quenching stress is eliminated, and fine and uniform tempering sorbite is obtained.

Description

technical field [0001] The invention relates to a heat treatment technology for stainless steel, in particular to a heat treatment method for high-chromium martensitic stainless steel. Background technique [0002] For the high-strength corrosion-resistant stainless steel used in the production of polyester fiber catalyst spindles in the petrochemical industry, it needs to install multiple blades on the shaft during work, and install them in polyester tanks as a rotating agitator. The working environment is very harsh, so it must have High corrosion resistance and good comprehensive mechanical properties. After heat treatment of 4Cr16Mo stainless steel products according to the conventional process, although the mechanical properties can be guaranteed, but because oil is used as the cooling medium during quenching, the oil fume is relatively large during production, resulting in serious oil pollution in the heat treatment furnace, crane and production site, and due to the si...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D1/18C22C38/44
Inventor 赵颖仲维王国宣王学玺马军平
Owner HENAN ZHONGYUAN SPECIAL STEEL EQUIP MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com