Composite temperature-sensitive aquagel and preparation method thereof
A temperature-sensitive hydrogel and water-soluble technology, applied in chemical instruments and methods, carrier binding/immobilizing peptides, non-active components of polymer compounds, etc., can solve the problem of limiting drug inclusion effects and clinical applications, and the limitations of chemical cross-linking agents. application, poor solubility of β-cyclodextrin, etc., to achieve good research and development application prospects, wide applicability, biocompatibility and good slow-release performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] The composite temperature-sensitive hydrogel of this embodiment is made through the following steps:
[0029] (1) Copolymerize 6-deoxy-6-amino-α-cyclodextrin and carboxymethyl chitosan to obtain water-soluble 6-deoxy-6-amino-α-cyclodextrin-carboxymethyl chitosan copolymerization Add 0.20g of water-soluble 6-deoxy-6-amino-α-cyclodextrin-carboxymethyl chitosan copolymer to 20ml of distilled water, stir evenly, and prepare solution A, add 0.20g active The substance doxorubicin was stirred and dissolved, and the stirring speed was 3000rpm to obtain solution B;
[0030] (2) Dissolve 1.0 g of sodium glycerophosphate in 2 ml of distilled water, stir to dissolve, and prepare solution C;
[0031] (3) Place solution B and solution C in an ice bath and cool to 4°C, then add solution C to solution B under stirring, and stir evenly to prepare a composite temperature-sensitive hydrogel.
Embodiment 2
[0033] The composite temperature-sensitive hydrogel of this embodiment is made through the following steps:
[0034] (1) Copolymerize 6-deoxy-6-amino-β-cyclodextrin and carboxymethyl chitosan to obtain water-soluble 6-deoxy-6-amino-β-cyclodextrin-carboxymethyl chitosan copolymerization Add 2g of water-soluble 6-deoxy-6-amino-β-cyclodextrin-carboxymethyl chitosan copolymer to 20ml of distilled water, stir evenly, and prepare solution A, add 0.02g active substance to solution A Doxorubicin was stirred and dissolved, and the stirring speed was 3000rpm to prepare solution B;
[0035] (2) Dissolve 0.8g sodium glycerophosphate in 2ml distilled water, stir to dissolve, and prepare solution C;
[0036] (3) Place solution B and solution C in an ice bath and cool to 0°C, then add solution C to solution B under stirring, and stir evenly to prepare a composite temperature-sensitive hydrogel.
Embodiment 3
[0038] The composite temperature-sensitive hydrogel of this embodiment is made through the following steps:
[0039] (1) Copolymerize 6-deoxy-6-amino-β-cyclodextrin and carboxypropyl chitosan to obtain water-soluble 6-deoxy-6-amino-β-cyclodextrin-carboxypropyl chitosan copolymerization Add 1.0g of water-soluble 6-deoxy-6-amino-β-cyclodextrin-carboxypropyl chitosan copolymer to 20ml of distilled water, stir evenly, and prepare solution A, add 0.10g active The substance mercaptopurine was stirred and dissolved, and the stirring speed was 3000rpm to obtain solution B;
[0040] (2) Dissolve 3.0 g of sodium glycerophosphate in 5 ml of distilled water, stir to dissolve, and prepare solution C;
[0041] (3) Place solution B and solution C in an ice bath and cool to 0°C, then add solution C to solution B under stirring, and stir evenly to prepare a composite temperature-sensitive hydrogel.
PUM
Property | Measurement | Unit |
---|---|---|
concentration | aaaaa | aaaaa |
molecular weight | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com