Encapsulated sustained-release acid for oil-water well reconstruction and preparation method thereof
A slow-release acid, oil-water well technology, applied in the direction of chemical instruments and methods, drilling compositions, etc., can solve the problems of short acid treatment radius and poor effect, and achieve high true sphericity, good water solubility, particle size small effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0034] Take the following raw materials by weight: (g)
[0035] Solid hydrochloric acid powder 450g, hydroxypropyl guar gum 5g, stearic acid 30g, acrylic resin 15g;
[0036] Preparation:
[0037] Applicable formation temperature of the product: 65-75°C
[0038] (1) Prepare 1000ml binder solution (5g hydroxypropyl guar gum + 1000ml water), let stand for 10min;
[0039] (2) Put 450g of solid hydrochloric acid powder into the side spray fluidized bed; open the side spray fluidized bed, adjust the temperature to 40°C, the fluidized bed speed to 50rpm, the spray flow rate to 20ml / min, and the spray pressure to 0.20MPa , The blast flow rate is 200L / min, and the binder solution is sprayed onto the solid hydrochloric acid powder to form solid hydrochloric acid particles;
[0040] (3) Prepare the wall material solution for the slow-release support layer: dissolve 30 g of stearic acid and 15 g of acrylic resin in 1000 ml of 6 wt % ethanol solution, and let stand for 15 min;
[0041]...
Embodiment 2
[0045] Take the following raw materials by weight: (g)
[0046] Citric acid sieved fine powder 450g, carboxymethyl hydroxypropyl guar gum 5g, pentaerythritol stearate 25g, acrylic resin 20g;
[0047] Applicable formation temperature of the product: 50~60℃
[0048] Preparation:
[0049] (1) Prepare 1000ml binder solution (4g carboxymethyl hydroxypropyl guar gum+1000ml water), let stand for 10min;
[0050](2) citric acid is pulverized, and after crossing a 0.15mm-0.125mm standard sieve, get 450g of sieved fine powder and put it into a side spray fluidized bed;
[0051] (3) Turn on the side spray fluidized bed, adjust the temperature to 40°C, the fluidized bed speed to 50rpm, the spray flow rate to 20ml / min, the jet pressure to 0.20MPa, and the blast flow rate to 200L / min, and the binder solution Spray on citric acid particles to form solid acid particles;
[0052] (4) Preparation of slow release support layer wall material solution: dissolve 20g pentaerythritol stearate, 25g...
Embodiment 3
[0057] Take the following raw materials by weight: (g)
[0058] Solid hydrochloric acid powder 395g, guar gum 8g, polyethylene glycol distearate 25g, polyethylene glycol 23g;
[0059] Applicable formation temperature of the product: 65~75℃
[0060] The preparation method is as in Example 1.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com