Solvent-free asphalt waterproofing material for cold applications modified silicon polymer and method for the same

A technology of waterproof material and asphalt coating film, which is applied in asphalt coatings, building insulation materials, chemical instruments and methods, etc., can solve the problem of difficulty in actively responding to changes in the surrounding environment, chemical resistance, ozone resistance, UV resistance, and waterproof performance. Weakening and other problems to achieve the effect of preventing rapid oxidation and aging, inhibiting the generation of harmful gases, and minimizing harmful gas emissions

Inactive Publication Date: 2015-03-25
RV LTD +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] As mentioned above, the rubber asphalt-based coating film waterproof material has the advantages of elongation, crack resistance, frost resistance and bonding, but also has poor reducing power, chemical resistance, ozone resistance and ultraviolet resistance. The problem
[0008] As far as the coating film waterproof material mainly composed of styrene-butadiene rubber (Styrene Butadiene Rubber; SBR) is concerned, due to its very poor reducing power, there is a problem that once it is repeatedly elongated, it will degenerate and lose its original physical properties. This will inevitably result in a loss of quality
[0009] In addition, for coating waterproof materials with SBR as the main component, due to their poor chemical resistance, ozone resistance and ultraviolet resistance, there is a problem that they are exposed to various chemicals and ozone for a long time, or exposed to ultraviolet rays. Quality also drops dramatically
[0010] On the contrary, as far as the coating film waterproof material mainly composed of chloroprene rubber (Chloroprene Rubber Latex; CR) is concerned, due to the poor freezing resistance (Freezing Resistance), there is a problem that it is difficult to actively respond to changes in the surrounding environment.
[0021] At this time, due to the improvement of the low temperature and poor flexibility of waterproof asphalt, the waterproof performance has been relatively improved, but its viscosity is higher than that of waterproof asphalt. In order to maintain a workable temperature, the on-site heating temperature is required to reach about 220 ° C. As mentioned above, there are still problems such as environmental pollution, damage to the physical properties of asphalt, weakening of waterproof performance, and there are safety hazards such as burns.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solvent-free asphalt waterproofing material for cold applications modified silicon polymer and method for the same
  • Solvent-free asphalt waterproofing material for cold applications modified silicon polymer and method for the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0082] After heating 20 parts by weight of straight-run asphalt to 180° C., 5 parts by weight of thermoplastic rubber were mixed in the heated straight-run asphalt, and mixed in a high-shear mixer at a stirring speed of 4000 rpm for 60 minutes. Next, after heat-treating the mixture to 150°C, 5 parts by weight of a C9-based aromatic petroleum resin was mixed, and stirred in a low-shear mixer at a stirring rate of 150 rpm for 30 minutes at a temperature of 150°C. Then, 8 parts by weight of paraffin-based white oil was mixed, and naturally cooled while stirring until it reached 80°C.

[0083] Then, 18 parts by weight of the modified silicone-based polymer and 15 parts by weight of petroleum-based hydrocarbon oil were mixed while stirring until the temperature reached 60°C. Then, 50 parts by weight of heavy calcium carbonate and precipitated calcium carbonate were added, and after stirring at a low speed for 30 minutes, vinyl silane and amino silane were added to produce a coating...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
penetrationaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

A solvent-free asphalt waterproofing material is provided to suppress the generation of toxic gas and to prevent fire and oxidation and aging according to hot melt. A solvent-free asphalt waterproofing material containing a modified silicon polymer comprises 15-20 parts by weight straight asphalt, 1-5 parts by weight thermoplastic rubber -5 parts by weight C9 aromatic petroleum resin, 3-8 parts by weight paraffinic white oil, 10-15 parts by weight petroleum hydrocarbon oil, 12-18 parts by weight modified silicon polymer, 30-50 parts by weight filler, 0.5-1.5 parts by weight dehydrating agent and 0.5-1.5 parts by weight adhesion accelerator

Description

technical field [0001] The invention relates to a cold-applied solvent-free asphalt coating waterproof material, in particular to an environmentally friendly cold-applied solvent-free asphalt coating waterproof material containing a modified organosilicon polymer and a manufacturing method thereof. The polymer component can prevent rapid oxidation and aging caused by high-temperature melting, suppress the generation of harmful gases during operation, and minimize environmental pollution while ensuring the safety of operators. Background technique [0002] Generally speaking, the so-called waterproofing compound (Waterproofing Compound) refers to the application of water-based or oil-based liquid waterproofing materials on the surfaces of various buildings and structural walls, and the waterproofing effect is obtained by using the film left after the water or solvent evaporates. of composite materials. [0003] This kind of film waterproof material is usually used for roof w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D195/00C09D153/02C09D157/02C09D183/04C09D7/12C09D5/00
CPCC09D5/00C09D7/65C09D195/00C09K3/18E04B1/64E04D11/02
Inventor 金圭振林镇先
Owner RV LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products