Permanent antistatic PA6 (Polyamide 6) composite material and preparation method thereof

A composite material and antistatic technology, which is applied in the field of permanent antistatic PA6 composite material and its preparation, can solve the problems of low conductivity and achieve low cost, light color and good antistatic effect

Inactive Publication Date: 2012-04-18
SHANGHAI SUNNY
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, PA6 has good electrical insulation like most polymer materials, and its surface resistivity is generally 10 13 -10 15 Ω·m, the conductivity is much lower than that of metal materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Permanent antistatic PA6 (Polyamide 6) composite material and preparation method thereof
  • Permanent antistatic PA6 (Polyamide 6) composite material and preparation method thereof
  • Permanent antistatic PA6 (Polyamide 6) composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5

[0029] The raw material formula of embodiment 1-5 is as follows:

[0030]

[0031] Put the above components into a high mixer according to the proportion and mix them for 2-5 minutes, discharge the material, and then use a screw extruder to extrude and granulate. The processing temperature is 150-200°C, and the screw speed is 25-35HZ.

[0032]

[0033] According to the samples prepared in Examples 1-5, the surface resistivity test was carried out for comparison.

[0034] The test performance comparison is shown in the table below:

[0035] project

[0036] The surface resistivity of the permanent antistatic masterbatch prepared according to the above formula and method reaches 10 2 -10 3 Ω·m, can be widely used in modified PA6; compared with the existing technology, it has long-lasting antistatic effect, small amount of addition but good antistatic effect, little impact on PA6 performance, light color, low cost, and heat resistance good points.

Embodiment 5

[0037] Example 5 has the lowest surface resistivity and the highest cost performance.

[0038] The permanent antistatic masterbatch prepared by using the formula and method of Example 5 is used for the preparation of the permanent antistatic PA6 composite material of the present invention.

[0039] Preparation of permanent antistatic PA6 composite material

[0040] Example 1-5

[0041] The raw material formula of embodiment 1-5 is as follows:

[0042]

[0043] Put the above components into a high-speed mixer according to the proportion and mix them for 2-5 minutes, discharge the material, and then use a screw extruder to extrude and pelletize.

[0044]

[0045] The samples prepared according to Examples 1-5 were compared in performance tests, using ASTM standards. The test performance comparison is shown in the table below:

[0046] project

[0047] Compared with the existing technology, the permanent antistatic PA6 composite material prepared according ...

Embodiment 6-7

[0048] Embodiment 6-7 is permanent antistatic PA6 composite material and preparation method thereof

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Surface resistivityaaaaaaaaaa
Notched impact strengthaaaaaaaaaa
Surface resistivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a permanent antistatic master batch and a preparation method thereof. The master batch comprises the following components in percentage by weight: 1-15 percent of alkali metal salt, 0.5-2 percent of antioxidant, 0.5-2 percent of heat stabilizer, 0-10 percent of assisting antistatic agent and 71-95 percent of polyether block-containing high polymer material. The preparation method comprises the following steps of: weighing raw materials according to the proportions, and putting into a high mixer for mixing for 2-5 minutes; discharging; and extruding and pelletizing with a double screw extruder to obtain the master batch, wherein the processing temperature is 150-200 DEG C, and the number of revolutions of a screw is 25-35 HZ. The invention further relates to a permanent antistatic composite material comprising the antistatic master batch and a preparation method thereof. The permanent antistatic master batch and the permanent antistatic composite material have the advantages of durable antistatic effect, permanent antistatic effect, various colors, low cost and high heat resistance.

Description

technical field [0001] The invention relates to a permanent antistatic masterbatch and a preparation method thereof, and also relates to a permanent antistatic PA6 composite material and a preparation method thereof. Background technique [0002] Nylon 6 (PA6) has good comprehensive mechanical properties, high heat resistance, good wear resistance, self-lubrication, good flame retardancy, excellent chemical corrosion resistance, excellent barrier properties and other properties Become the most widely used engineering plastics. However, PA6 has good electrical insulation like most polymer materials, and its surface resistivity is generally 10 13 -10 15 Ω·m, the conductivity is much smaller than that of metal materials. It is easy to accumulate static charge when it contacts or rubs with other substances. The negative effects brought by the accumulation of static electricity have seriously affected production, life, and work, and sometimes even cause fires and explosions. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L71/02C08K13/02C08K3/24C08K3/16C08K5/524C08K5/46C08K5/098C08K3/36C08J3/22C08L77/02B29B9/06B29C47/92B29C48/92
CPCB29C48/04B29C48/40B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 郭建鹏孟成铭杨涛范潇潇
Owner SHANGHAI SUNNY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com