Color master batches used by polyvinylidene fluoride OK cable product and preparation method of color master batches

A polyvinylidene fluoride and color masterbatch technology is applied in the field of color masterbatch and color masterbatch preparation, which can solve the problems of static electricity, easy migration of pigments, and unstable performance, so as to prevent the generation of electrostatic charges, resist the High electrostatic performance and the effect of preventing dust adsorption

Inactive Publication Date: 2012-05-02
江苏昊华光伏科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary coloring masterbatch processed by traditional technology, the performance of the product is not stable enough
Especially affected by its content, the pigments often fail to meet the requirements of use, and the pigments are easy to migrate, bleed, and generate static electricity.
Therefore, the amount of addition is large, and the cost of product production is high, which affects the wide use of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Color master batches used by polyvinylidene fluoride OK cable product and preparation method of color master batches
  • Color master batches used by polyvinylidene fluoride OK cable product and preparation method of color master batches
  • Color master batches used by polyvinylidene fluoride OK cable product and preparation method of color master batches

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Color masterbatch used to prepare red polyvinylidene fluoride OK line products:

[0018] First weigh the materials according to the following proportions for pre-mixing:

[0019]

[0020] The above units are g.

[0021] Then put the above-mentioned mixture in a kneading pot with a current control of 35A and mix it at high speed until it is coated, and then put the uniformly stirred mixture into a twin-screw extruder whose main machine temperature is controlled at about 200°C to extrude. After cooling, Dried and granulated to make the required masterbatch.

Embodiment 2

[0023] Color masterbatch used to prepare red polyvinylidene fluoride OK line products:

[0024] First weigh the materials according to the following proportions for pre-mixing:

[0025]

[0026] The above units are g.

[0027] Then put the above-mentioned mixture in a kneading pot with a current control of 35A and mix it at a high speed until it is coated, and then put the uniformly stirred mixture into a twin-screw extruder whose main machine temperature is controlled at about 210°C to extrude. After cooling, Dried and granulated to make the required masterbatch.

Embodiment 3

[0029] Color masterbatch used to prepare blue polyvinylidene fluoride OK line products:

[0030] First weigh the materials according to the following proportions for pre-mixing:

[0031]

[0032]

[0033] The above units are g.

[0034] Then put the above-mentioned mixture in a kneading pot with a current control of 35A and mix it at high speed until it is coated, and then put the uniformly stirred mixture into a twin-screw extruder whose main machine temperature is controlled at about 200°C to extrude. After cooling, Dried and granulated to make the required masterbatch.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides color master batches for a polyvinylidene fluoride OK cable. The color master batches consist of a pigment, a plastic auxiliary agent and carrier resin, wherein the plastic auxiliary agent contains N-N' aethylenum di-octadecanamide, polyethylene wax, zinc stearate, an antistatic agent and a high-grade composite lubricant. The preparation method comprises the following steps of: mixing the materials according to the formula; kneading the materials in a kneading pot at a high speed; and putting the uniformly stirred mixture into a double-screw extruder of which the host temperature is controlled to be between 180 and 210 DEG C, and extruding the mixture; cooling, drying and cutting the mixture into particles to obtain the needed color master batches. The color master batches disclosed by the invention have the advantages of good dispersity and strong covering power, are easy to stir, are bleeding-free and static-free, and cannot cause environmental pollution.

Description

technical field [0001] The invention relates to the technical field of plastic coloring, in particular to a color masterbatch used for polyvinylidene fluoride OK line products. The invention also relates to a preparation method of the color masterbatch used in the polyvinylidene fluoride OK line product. Background technique [0002] Using polyvinylidene fluoride resin to make OK cables requires different colors. Since there are few color masterbatches used in polyvinylidene fluoride resin products in the market, the existing ones mainly rely on imports, let alone OK cables in The requirements for resistance to voltage breakdown are relatively high. Ordinary coloring masterbatch processed by traditional technology, the performance of the product is not stable enough. Especially affected by its content, the pigments often fail to meet the use requirements, and the pigments are easy to migrate, bleed, and generate static electricity. Thereby the addition amount is large, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/16C08K13/02C08K5/20C08K5/098B29B9/06B29C47/92B29C48/92
CPCB29C48/40B29C48/92B29C2948/92704B29C2948/92895
Inventor 王海林王卫国
Owner 江苏昊华光伏科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com