Permanent anti-static PP (polypropylene) composite material and preparation method thereof

A composite material and antistatic masterbatch technology, which is applied in chemical instruments and methods, other chemical processes, etc., can solve the problem that the conductivity is lower than that of metal materials, achieve good antistatic effect, improve compatibility, and increase surface activity. Effect

Active Publication Date: 2012-04-04
上海日之升科技有限公司
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is suitable for making general mechanical parts, corrosion-resistant parts and automobile and electrical parts. However, PP has good electrical insulation like most polymer materials, and its surface resistivity is generally 10 13 -10 15 Ω.m, the conductivity is much smaller than that of metal materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Permanent anti-static PP (polypropylene) composite material and preparation method thereof
  • Permanent anti-static PP (polypropylene) composite material and preparation method thereof
  • Permanent anti-static PP (polypropylene) composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-5

[0023] The raw material formulations of the antistatic masterbatch of Examples 1-5 are as follows:

[0024]

[0025] In the above embodiment, the alkali metal salt is M + X - , Where M + Li + , Na + , K + ; X - For Cl - , Br - , I - , CLO 4 - , Preferably LiCLO 4 .

[0026] In the foregoing embodiment, the antioxidant is a 1:1 compound of phenothiazine and phosphite (s9228);

[0027] In the foregoing embodiment, the heat stabilizer is a 2:1:1 compound of organotin heat stabilizer, calcium stearate, and zinc stearate;

[0028] In the foregoing embodiment, the antistatic agent is silica;

[0029] In the above embodiment, the polymer material containing polyether block is a 5:1 compound of polyethylene oxide and polyethylene glycol methacrylic acid copolymer; the molecular weight of the two polymers is preferably 6 Between 160,000.

[0030] Put the above-mentioned components into a high-mixer in proportion to mix for 2-5 minutes, discharge the material, and then extrude and pelletize with ...

Embodiment 5

[0036] Example 5 has the lowest surface resistivity and the highest cost performance.

Embodiment 6

[0051] Weigh the raw materials according to the weight ratio: 1% of the above-mentioned antistatic masterbatch, 98% PP, and 1% of the compatibilizer. Weigh the raw materials according to the weight ratio, put them in a high-mixer and mix for 2-5 minutes, then discharge, Then use a twin-screw extruder to extrude and pelletize, the processing temperature is 190-220℃, and the screw rotation speed is 40 Hz. The surface resistivity of the prepared material is 10 13 Ω.m.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Notched impact strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a permanent anti-static PP (polypropylene) composite material and a preparation method thereof. The material comprises the following components in percentage by weight: 3 to 8 percent of anti-static master batch, 80 to 95 percent of PP and 1 to 5 percent of compatilizer. The preparation method comprises the following steps of: weighing the raw materials according to weight proportion; placing the raw materials into a high mixing machine to mix the raw materials for 2 to 5 minutes; discharging; and then carrying out extrusion pelletizing by a double-screw extruder, wherein a processing temperature is in the range of 190 to 220 DEG C and screws have revolution of 35 to 40Hz. Compared with the prior art, the permanent anti-static PP composite material has the advantages of sustained anti-static effect, permanent anti-static effect, good anti-static effect, high comprehensive mechanical property, performance close to pure PP, light color, capability of being prepared into various colors, low cost, good heat resistance and the like. The surface resistivity of the permanent anti-static PP composite material can reach 106 to 108 ohm.m.

Description

Technical field [0001] The invention relates to a permanent antistatic masterbatch and a preparation method. The invention also relates to a method for preparing permanent antistatic PP composite material. Background technique [0002] PP is non-toxic, tasteless, low density, low price, and has good electrical properties. Common acid and alkali organic solvents have almost no effect on it. It is suitable for making general mechanical parts, corrosion-resistant parts and automobile and electrical parts. But PP has good electrical insulation like most polymer materials, and its surface resistivity is generally 10 13 -10 15 Ω.m, the conductivity is much smaller than that of metal materials. It is easy to accumulate static charge when it comes into contact with other substances or rubs. The negative effects of static electricity accumulation have seriously affected production, life, and work, and sometimes even cause fires and explosions. In some specific working environments in t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/12C08L51/08C08L51/06C08K13/02C08K5/524C08K5/46C08K5/098C08K3/36C08K3/24C08J3/22C09K3/16
Inventor 郭建鹏朱晓龙杨涛陈晓东
Owner 上海日之升科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com