Odorless ultraviolet-curing wood lacquer and preparation method thereof

A technology of wood coatings and ultraviolet light, applied in the direction of epoxy resin coatings, coatings, etc., can solve the problems of not being able to achieve clean odor, benzene health, environmental impact, and environmental pollution, and achieve short construction period and excellent leveling effect, the effect of flat surface

Active Publication Date: 2013-01-30
QINGDAO ZHANCHEN NEW MATERIAL
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The defect of this patent is that there is no residual irritating smell after curing, and the function of "clean taste" cannot be achieved. Moreover, the manufacturing process before curing still pollutes the environment
At the same time, some compounds mentioned in the technical background of the patent formula contain benzene before being exposed to light, and it does not increase after being exposed to light; it shows that benzene remains in the manufacturing process or has already caused a great impact on human health and the surrounding environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Odorless ultraviolet-curing wood lacquer and preparation method thereof
  • Odorless ultraviolet-curing wood lacquer and preparation method thereof
  • Odorless ultraviolet-curing wood lacquer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Embodiment 1: net odor UV photocuring coating

[0044] Raw material weight percentages are as follows:

[0045] composition

Weight percentage (%)

621-100 UV curable resin

32

188 UV curable resin

19

EM2382

9

ACMO

9

CX-2

6

Talc powder TP1250

11.5

Transparent powder TM2500

9

fumed silica

0.5

6022 Photoinitiator

3.0

Defoamer BYK-390

0.4

Leveling agent TEGO-410

0.3

Wetting and dispersing agent BYK333

0.3

total

100

[0046] 2. Preparation method:

[0047] 1) First add 621-100, 188, EO-TMPTA, ACMO, and CX-2 into the tank, then add TP1250, TM2500, and A200 under stirring, and disperse at high speed for 10 minutes after stirring evenly;

[0048] 2) Add BYK-333, BYK-390, TEGO410 and disperse at medium speed for 10 minutes;

[0049] 3) Add 6022 photoinitiator, stir evenly, and adjust the viscosi...

Embodiment 2

[0053] Embodiment 2: net odor UV photocuring coating

[0054] 1. The weight percentage of raw materials is as follows:

[0055] composition

Weight percentage (%)

621-100 UV curable resin

26.8

188 UV curable resin

28

EM2382

8

ACMO

6

CX-2

7

Talc powder TP1250

8

Transparent powder TM2500

12

[0056] fumed silica

0.5

PBZ photoinitiator

3.0

Defoamer BYK-390

0.2

Leveling agent TEGO-410

0.2

Wetting and dispersing agent BYK333

0.3

total

100

[0057] 2. Preparation method:

[0058] 1) First add 621-100, 188, EO-TMPTA, ACMO, and CX-2 into the tank, then add TP1250, TM2500, and A200 under stirring, and disperse at high speed for 10 minutes after stirring evenly;

[0059] 2) Add BYK-333, TEGO410, BYK-390 and disperse at medium speed for 10 minutes;

[0060] 3) Add PBZ photoinitiator, stir ev...

Embodiment 3

[0064] Embodiment 3: net odor UV photocuring coating

[0065] Raw material weight percentages are as follows:

[0066] composition

Weight percentage (%)

621-100 UV curable resin

38

EM-2382

23

ACMO

5

CX-2

9

Talc powder TP1250

11.5

Transparent powder TM2500

9.0

fumed silica

0.5

BP photoinitiator

3.0

leveling agent

0.3

Defoamer

0.2

Wetting and dispersing agent

0.5

total

100

[0067] 2. Preparation method:

[0068] 1) First add 621-100, EM-2382, ACMO, and CX-2 into the tank, then add TP1250, TM2500, and A200 under stirring, and disperse at high speed for 10 minutes after stirring evenly;

[0069] 2) Add BYK-333 and BYK-390 to disperse at medium speed for 10 minutes;

[0070] 3) Add BP photoinitiator, stir evenly, and adjust the viscosity to 40-60KU / 25°C to obtain the product.

[0071] 3. The detection met...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
refractionaaaaaaaaaa
Login to View More

Abstract

The invention relates to an odorless ultraviolet-curing wood lacquer and a preparation method thereof. The wood lacquer is prepared from the following components in percentage by weight: 45-65% of ultraviolet-curing resin, 10-25% of reactive monomer, 5.0-15% of talcum powder, 5.0-15% of transparent powder, 0.5-1.0% of gas-phase silicon dioxide, 1.0-5.0% of photoinitiator, 0.2-0.5% of defoaming agent, 0.2-1.0% of leveling agent and 0.2-1.2% of wetting agent. The odorless ultraviolet-curing wood lacquer does not have irritating odor before and after construction, does not contain benzene, and can be used immediately after construction; and meanwhile, the surface effect and fullness are not inferior to those of nitrocellulose dope, unsaturated paint or polyester paint.

Description

technical field [0001] The invention relates to an ultraviolet light-curable coating for wood products, in particular to an odor-cleaning ultraviolet light-curable wood transparent varnish for wood products. Background technique [0002] UV-curable coatings have developed rapidly due to the advantages of short recoating time, high production efficiency, and environmental protection. However, nitro coatings, unsaturated resin coatings, and polyurethane coatings are all inferior to UV light-curing coatings due to their environmental protection, efficiency, and production costs. Especially in terms of environmental protection, it is also inferior to UV photocurable coatings, and the formulations commonly used in the existing UV photocurable coating technology have been systematically analyzed and tested. Combined with the experimental data of the market, the regularity Recognition, a formula composed of a variety of acrylic compounds, the mechanism of benzene produced during t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/10C09D7/12
Inventor 陈寿生彭钧浪孙倩
Owner QINGDAO ZHANCHEN NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More