Preparation method of colloid of mono-dispersed silver nano particles and nano silver powder and conductive ink thereof

A technology of silver nanoparticles and nano-silver powder, which is applied in the field of preparation of silver nanoparticles, can solve problems such as reducing the performance of printed products, and achieve the effects of reducing preparation costs, simple process, and uniform dispersion

Inactive Publication Date: 2011-07-13
INST OF CHEM CHINESE ACAD OF SCI
View PDF8 Cites 60 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Poor organic solvents will make the printed circuit patterns prone to "coffee rings", seriously reducing the performance of printed products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of colloid of mono-dispersed silver nano particles and nano silver powder and conductive ink thereof
  • Preparation method of colloid of mono-dispersed silver nano particles and nano silver powder and conductive ink thereof
  • Preparation method of colloid of mono-dispersed silver nano particles and nano silver powder and conductive ink thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] Dissolve 2g of silver nitrate in 15ml of water until fully dissolved; dissolve 4g of gum arabic in 30ml of water, stir until completely dissolved and add it to the above silver nitrate aqueous solution; The aforementioned structure, in which R1, R2, R3, R4, and R5 are all H) was added into 15ml of water, and fully stirred until completely dissolved. At room temperature and under stirring, add the prepared reducing agent acetylphenylhydrazine aqueous solution into the above-prepared mixed solution of silver nitrate and gum arabic in a constant flow and dropwise, and at the same time make up the amount of water to 70ml. Reaction stops after 30 minutes, obtains the colloid of the silver nanoparticle of monodisperse, and the transformation efficiency of silver nitrate is 79%; Obtain the ultraviolet-visible absorption spectrum of the colloid of the silver nanoparticle of monodisperse see figure 1 shown.

[0063] The scanning electron microscope model adopted is Hitachi S-55...

Embodiment 2

[0066] Dissolve 1g of silver acetate in 15ml of solvent toluene until fully dissolved; dissolve 6g of dispersant dodecylamine in 30ml of toluene, stir until completely dissolved and add it to the above silver salt solution; Acid dihydrazide (structural formula is: ) was added to 15ml of toluene, stirred thoroughly until completely dissolved. At room temperature and under stirring, the prepared reducing agent solution was added dropwise at a constant flow to the above-prepared mixed solution of silver acetate and dodecylamine, and the final solvent volume was controlled at 60 ml. At normal temperature, the reaction was stopped after 60 minutes to obtain a colloid of monodisperse silver nanoparticles, and the conversion rate of silver acetate was 71%.

[0067]The transmission electron microscope model that adopts is Japan's JEM-2011, and the colloidal sample of the monodispersed silver nanoparticle that obtains is dropped on the copper grid that is attached with ultra-thin car...

Embodiment 3

[0070] Dissolve 1g of silver nitrate in 15ml of water until fully dissolved; dissolve 3g of dispersant polyvinylamine in 20ml of water, stir until completely dissolved and add it to the above silver nitrate solution; then, add 1.5g of reducing agent oxalic acid di Hydrazide (the structural formula is: ) was added to 15ml of water and stirred thoroughly until completely dissolved. At the set temperature (30°C) while stirring, the prepared reducing agent oxalic acid dihydrazide aqueous solution was added dropwise at a constant flow to the above-mentioned mixed solution of silver nitrate and polyvinylamine, and the final amount of water was controlled at 50ml. At a temperature of 30° C., the reaction was stopped after 40 minutes to obtain a colloid of monodisperse silver nanoparticles, and the conversion rate of silver nitrate was 73%.

[0071] The model of the laser particle size analyzer used is (UK) Malvern Zetasizer Nano ZEN3600. The particle size distribution curve of th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of colloid of mono-dispersed silver nano particles and nano silver powder, and conductive ink prepared on the basis of the nano silver powder. The method comprises the following steps of: dropwise adding a reducing agent solution in a constant-flow manner to the mixed solution of silver salt precursor and a dispersant to obtain a reaction system; after reaction is finished, obtaining the colloid of the mono-dispersed silver nano particles; performing centrifugation on the colloid of the mono-dispersed silver nano particles; cleaning the precipitate with a cleaning agent and drying to obtain the nano silver powder; and mixing the nano silver powder, a terpene alcohol compound solvent and auxiliaries to prepare the conductive ink. The method forpreparing the colloid of mono-dispersed silver nano particles provided by the invention has simple and quick process, high product output, mild preparation conditions, and no need of protection of inert gas. The terpene alcohol compound solvent used for preparing the conductive ink can uniformly disperse the nano silver powder and can maintain long-time stability. The terpene alcohol compound solvent can keep the conductive ink and a substrate in a good spread state.

Description

technical field [0001] The invention belongs to the field of preparation of silver nanoparticles, in particular to a method for preparing colloid of silver nanoparticles with controllable particle size and monodisperse and nano-silver powder, and conductive ink prepared based on nano-silver powder. Background technique [0002] Silver nanoparticles have many unique properties, such as large specific surface area, high surface energy, good catalytic performance, superior electrical and thermal conductivity, low sintering temperature, and good stability. Catalysts, nano antibacterial materials, ultra-low temperature refrigerants, antistatic materials, and as materials for preparing Raman-enhanced biosensors have a wide range of applications. In recent years, a series of methods for preparing silver nanoparticles have been reported. [0003] At present, the methods for preparing nano-silver particles at home and abroad include: laser-induced meteorological pyrolysis method (CN...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F9/24C09D11/02B22F1/00C09D11/52
Inventor 张兴业安粒宋延林
Owner INST OF CHEM CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com