Neodymium (Nd)-based homogeneous rare earth catalyst as well as preparation method and application thereof
A rare earth catalyst and catalyst technology are applied in the field of neodymium-based homogeneous rare earth catalyst and its preparation, which can solve the problems of environmental pollution and equipment corrosion, and achieve the effects of excellent physical and mechanical properties and stable and easy polymerization process.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0041] Starting from neodymium trioxide, using cyclohexane as solvent, adopting direct extraction method to obtain neodymium naphthenate / cyclohexane solution, wherein the concentration of neodymium [Nd 3+ ] is 0.21 mol / l. Triisobutylaluminum and diethylaluminum chloride were respectively prepared into cyclohexane solutions with a concentration of 2 mol / l for future use. The water value of the solvent is lower than 20ppm, and the oxygen is exhausted with nitrogen before use; the aging tank is dried and oxygenated.
[0042] Under the protection of nitrogen, add 630ml of cyclohexane solution to the 2L catalyst aging kettle, then add 30ml of isoprene and 62ml of neodymium naphthenate solution into the aging kettle, and then add 16ml of a Add the diethylaluminum chloride solution into the aging kettle, make isoprene, neodymium naphthenate and diethylaluminum chloride contact and react at 50°C for 7 minutes, then add 130ml of triisobutylaluminum solution, Aging at ℃ for 40 minutes...
Embodiment 2
[0045] Triisobutylaluminum and diethylaluminum chloride were respectively prepared into hexane solutions with a concentration of 0.5 mol / l for future use. Neodymium naphthenate is prepared into a hexane solution with a concentration of 0.21mol / l for later use. The treatment mode of the solvent and the aging tank is the same as in Example 1.
[0046] Under the protection of nitrogen, add 218ml of isoprene, 130ml of neodymium naphthenate solution and 8.0L of hexane solution into the 20L catalyst aging kettle, then add 190ml of diethylaluminum chloride solution at 0°C under stirring conditions, After contact reaction at 0° C. for 60 minutes, 546 ml of triisobutylaluminum solution was added, and aging continued for 10 hours. The catalyst concentration is 0.3×10 -5 mol / ml.
[0047] Under the protection of nitrogen, 350 g of isoprene, 1800 g of hexane and 340 ml of catalyst were successively added into a 5 L polymerization kettle, and the monomer concentration was 15%. After rea...
Embodiment 3
[0049] Diisobutylaluminum hydride and diethylaluminum chloride were respectively prepared into hexane solutions with a concentration of 0.5 mol / l for future use. Neodymium naphthenate is prepared into a hexane solution with a concentration of 0.21mol / l for later use. The treatment mode of the solvent and the aging tank is the same as in Example 1.
[0050] Under nitrogen protection, add 15ml of isoprene, 1.1L of hexane solution, 31ml of neodymium naphthenate solution into the 2L catalyst aging kettle, and then add 39ml of diethylaluminum chloride solution at 10°C under stirring conditions, After 20 minutes of contact reaction, 130 ml of triisobutylaluminum solution was added, and aging continued for 2 hours. The catalyst concentration is 0.5×10 -5 mol / ml.
[0051] Under the protection of nitrogen, 350 g of isoprene, 1800 g of hexane and 180 ml of catalyst were successively added into a 5 L polymerization kettle, and the monomer concentration was 15.4%. After reacting at 25...
PUM
Property | Measurement | Unit |
---|---|---|
molecular weight distribution | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com