Organic and inorganic mixed fingerprint-resistance coating and preparation method thereof

An anti-fingerprint, inorganic technology, applied in epoxy resin coatings, polyurea/polyurethane coatings, coatings, etc., can solve environmental pollution and other problems, and achieve high gloss, fingerprint resistance, adhesion, and high hardness.

Inactive Publication Date: 2011-05-25
SOUTHEAST UNIV
View PDF10 Cites 44 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On July 8, 2010, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences applied (application number: CN201010226044.8) for a high-hardness anti-fingerprint coating and its preparation method, using fluorocarbon resin as the main film-forming substance, and then adding amino Combination of resin, nanoparticles, polytetrafluoroethylene, polyethylene wax, additives and organic solvents, but the coating is solvent-based, which has certain pollution to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic and inorganic mixed fingerprint-resistance coating and preparation method thereof
  • Organic and inorganic mixed fingerprint-resistance coating and preparation method thereof
  • Organic and inorganic mixed fingerprint-resistance coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A preferred organic / inorganic hybrid anti-fingerprint coating specific proportion is as follows:

[0034] Table 1

[0035]

[0036] Put 600g of water-based epoxy resin into the reaction kettle, add 80g of modified silica sol, 30g of ammonium zirconium carbonate, 12g of water-based polyethylene wax slurry while stirring, then add 71732g of amino resin, 48g of blocked polyisocyanate and 45g of adhesion promoter , and finally put 2 g of leveling agent and 260 g of remaining deionized water into the reaction kettle, and continue to stir for 15 to 45 minutes to obtain organic / inorganic hybrid anti-fingerprint coating No. 1.

Embodiment 2

[0038] A preferred organic / inorganic hybrid anti-fingerprint coating specific proportion is as follows:

[0039] Table 2

[0040]

[0041] Put 750g of water-based epoxy resin into the reaction kettle, add 110g of modified silica sol, 38g of ammonium fluorotitanate, 15g of water-based polyethylene wax slurry while stirring, then add 71743g of amino resin, 55g of blocked polyisocyanate and titanate bismuth 20g of joint agent, and finally put 2.5g of leveling agent and the remaining 294g of deionized water into the reaction kettle, and continue stirring for 15 to 45 minutes to obtain organic / inorganic hybrid anti-fingerprint coating No. 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to an organic and inorganic mixed fingerprint-resistance coating and a preparation method thereof. The coating is prepared from the following chemical components in percentage by weight: 40 to 70 percent of aqueous resin, 3 to 10 percent of modified silica solution, 2 to 15 percent of amino resin, 2 to 10 percent of polyisocyanates, 1 to 5 percent of mineral salt, 1 to 6 percent of aqueous polyethylene wax pulp, 1 to 9 percent of adhesion promoter, 0.1 to 0.5 percent of flatting agent, and 10 to 40 percent of deionized water. And the total weight percentage of the raw materials is 100 percent. The organic and inorganic mixed fingerprint-resistance coating prepared by the method does not contain metal ions which cause pollution to the environment. The coating can be coated on an electrogalvanized steel sheet, hot-dip galvannealed sheet, tin-plated steel sheet or cold-rolled steel sheet, and after being coated, the coating can be baked for only 8 to 15 seconds to be solidified into a transparent coating with high fingerprint resistance, corrosion resistance, high hardness, scraping resistance, conductivity, self-lubricating performance, coating performance and the like.

Description

technical field [0001] The invention relates to a metal surface protective coating composition, in particular to an organic / inorganic hybrid anti-fingerprint coating and a preparation method thereof. Background technique [0002] In recent years, galvanized steel sheets have been widely used in industries such as home appliances, automobiles, office supplies, and toys. With the continuous improvement of people's quality of life, the products used are not only required to be aesthetically pleasing, but also environmentally friendly. Fingerprint-resistant steel plate is a high value-added surface treatment product. Compared with the general bare galvanized steel plate, it not only has fingerprint resistance, but also has corrosion resistance, electrical conductivity and repaintability. Today, the market demand for anti-fingerprint steel products is increasing day by day, which also promotes the research on anti-fingerprint processing technology and the development of new appli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D163/00C09D175/04C09D161/32C09D7/12
Inventor 陈志明陈坤林邵利焦真
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com