Casting and smelting additive

An additive, sodium oxide technology, applied in the field of casting and smelting additives, can solve the problems of very large impact, pollution, and energy loss, and achieve the effects of saving power consumption, not polluting the environment, and prolonging the life of the furnace body

Active Publication Date: 2011-04-06
郑州维达铸造材料有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the metallurgical smelting and foundry industry, the melting speed of various types of electric furnaces (such as high-frequency, intermediate-frequency or electric arc furnaces, etc.) serious pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Casting smelting additive of the present invention, it is by raw material sodium oxide 10 parts; Aluminum oxide 3.5 parts; Potassium oxide 3.5 parts; Sodium carbonate 6 parts; Silicon dioxide 3 parts; Calcium oxide 11 parts; 0.5; 3.1 parts of polyolefin thermoplastic elastomer; 1.2 parts of dysprosium oxide and 5 parts of anhydrous borax;

[0026] Use a crusher to crush the above-mentioned raw materials to a particle size of 0.05 microns to 1.6 mm, vibrate and sieve, mix evenly, and pack them into bags according to specifications.

Embodiment 2

[0028] Casting smelting additive of the present invention, it is made of raw material sodium oxide 15 parts; Aluminum oxide 8.5 parts; Potassium oxide 8.5 parts; Sodium carbonate 11 parts; Silicon dioxide 9 parts; Calcium oxide 18 parts; 2 parts; 5.5 parts of polyolefin thermoplastic elastomer; 3.3 parts of dysprosium oxide and 10 parts of anhydrous borax;

[0029] The preparation method is the same as in Example 1.

Embodiment 3

[0031] Casting smelting additive of the present invention, it is made of raw material sodium oxide 13 parts; Aluminum oxide 6 parts; Potassium oxide 6 parts; Sodium carbonate 9 parts; Silicon dioxide 6 parts; Calcium oxide 15 parts; 1 part; 4 parts of polyolefin thermoplastic elastomer; 2.5 parts of dysprosium oxide and 8 parts of anhydrous borax;

[0032] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a casting and smelting additive which is prepared from the raw materials including 10-15 parts of sodium oxide, 3.5-8.5 parts of aluminum oxide, 3.5-8.5 parts of potassium oxide, 6-11 parts of sodium carbonate, 3-9 parts of silicon dioxide, 11-18 parts of calcium oxide, 1.5-8.5 parts of iron oxide, 0.5-2 parts of titanium dioxide, 3.1-5.5 parts of olefinic thermoplastic elastomer, 1.2-3.3 parts of dysprosium oxide and 5-10 parts of anhydrous sodium borate. The additive has the advantages of low cost, no toxin, no harmful ingredient and no environmental pollution; because the liquidity of molten steel can be increased during smelting, the air pores and the slag eyes of finished casts can be reduced, the compression strength and the tensile strength of the casts can be increased, and thus, the finished cast rate is increased from 90% to 98%; the bridging phenomenon of a poured material can be avoided during smelting; residues can not be stuck to the furnace wall during smelting, the service life of the furnace body can be prolonged by 20%, the smelting time can be shortened by 1 / 3, the power consumption can be greatly saved, and the enterprise revenue can be increased.

Description

technical field [0001] The invention relates to auxiliary materials for smelting and casting, in particular to a casting and smelting additive that can rapidly increase the smelting speed. Background technique [0002] In the metallurgical smelting and foundry industry, the melting speed of various types of electric furnaces (such as high-frequency, intermediate-frequency or electric arc furnaces, etc.) serious pollution. Contents of the invention [0003] The object of the present invention is to provide a casting smelting additive which can increase the smelting speed, save energy and reduce waste discharge. [0004] To achieve the above object, the present invention can take the following technical solutions: [0005] Casting smelting additive of the present invention, it is made of raw material sodium oxide (Na 2 O), alumina (Al 2 o 3 ), potassium oxide (K 2 O), sodium carbonate (NaCO 3 ), silicon dioxide (SiO 2 ), calcium oxide (CaO), iron oxide (Fe 2 o 3 ),...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21C5/52
CPCY02P10/20
Inventor 王铭钧王莉
Owner 郑州维达铸造材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products