Low smoke zero halogen thermoplastic elastomer flame-retardant cable material and production method thereof

Abstract

The invention discloses a low smoke zero halogen thermoplastic elastomer flame-retardant cable material which comprises the following components in weight ratio: 100 parts of ethylene-propylene diene monomer rubber, 50-200 parts of SEBS503 and / or maleic anhydride grafted SEBS, 55-100 parts of reinforcing agent, 100-300 parts of plasticizing and softening agent, 0-5 parts of pigment, 8-12 parts of auxiliary agent, 1-4 parts of cross-linking agent, 150-550 parts of flame retardant agent and 40-150 parts of liquid reinforcing and softening rubber. The preparation method of the material comprises the following steps of: firstly, mixing, plasticating, cooling and granulating the SEBS 503 and / or maleic anhydride grafted SEBS, the plasticizing and softening agent, the reinforcing agent, the pigment and the ethylene-propylene diene monomer rubber particles to prepare thermoplastic elastomer master batch; then, mixing the thermoplastic elastomer master batch with the auxiliary agent, the flame retardant agent and the liquid reinforcing and softening rubber, adding into a mixer, and stirring uniformly; and finally, mixing, plasticating, cooling and granulating to obtain a finished product. The product does not contain halogen, has excellent flame retarding efficacy and is not embrittled and hardened under the low temperature condition of subzero 40 DEG C. The preparation method has simple equipment and technology and does not have any three wastes discharge or environmental pollution.

Description

technical field [0001] The invention relates to a cable material for manufacturing cable insulation sheaths, in particular to a low-smoke, halogen-free, flame-retardant and fire-resistant cable material with low temperature resistance; the invention also relates to a production method of the cable material. Background technique [0002] At present, the existing low-smoke halogen-free cable material is made of low-density polyethylene (LDPE) and ethylene-vinyl acetate copolymer (EVA) as the benchmark raw materials, adding flame retardants and additives and plasticizing. The hardness of the product is between 90 and 93 degrees A, and it is inconvenient to move and bend during use. The flame retardant rubber sheathed cable is made of neoprene (CR) and chlorinated polyethylene (CPE). Bromine-phosphorus flame retardant system. Due to a large amount of halogen and a large amount of chloride ions in the rubber itself, a large amount of hydrogen halide gas will inevitably be gener...

AI Technical Summary

Problems solved by technology

Moreover, in the production process of the current domestic production process, it is necessary to add a vulcanization aid with certain toxic and side effects to vulcanize under high temperature and high pressure conditions (steam pipeline), the equipment is complicated, the investment is expensive, and there are a large number of toxic and harmful substances in the raw and auxiliary materials and reaction by-products. Substances, high temperature and high pressure in the production process have serious unsafe hidden dangers; at the same time, the production consumption is large, the scrap rate is high, resulting in increased production costs; and there are a large number of "three wastes" discharged, forming harsh environmental pollution

It can be said that the current technology is a "high energy consumption, high emission, high pollution" technology product, which is completely inconsistent with the current national product, industrial policy and long-term interests of development

Images