Composite material special for automobile engine oil pan and preparation method thereof

A composite material and engine oil technology, applied in engine components, engine lubrication, machine/engine, etc., can solve the problems of low durability work adaptability, durability can not reach the service life, etc., to achieve excellent mechanical strength and dimensional stability properties, excellent long-term and short-term thermal properties, excellent chemical resistance

Active Publication Date: 2012-06-20
辰东意普万新材料(广东)有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0015] However, the oil pan manufactured according to the above-mentioned patent has low durability and adaptability to work at low temperature
Durability does not meet the requirements of 10 years of service life (or a cumulative driving of 1 million km), and the use in a low-temperature cold environment of -30°C also fails the test

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite material special for automobile engine oil pan and preparation method thereof
  • Composite material special for automobile engine oil pan and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] A special composite material for an automobile engine oil pan, the composite material contains nylon, alkali-free short glass fibers, mineral fillers, modifiers and auxiliary agents; wherein, the nylon is high-temperature nylon PA46; the alkali-free short glass The fiber is treated with a silane coupling agent; the mineral filler is kaolin; the modifier is acrylonitrile-butadiene-styrene copolymer (ABS); the auxiliary agent contains a temperature-resistant anti-aging agent, a lubricant, Nucleating agent and dyeing agent; The temperature-resistant anti-aging agent is a mixture of alkali metal halide cuprous chloride and potassium bromide, and the lubricant is a mixture of ethylene bis stearamide and silicone powder. The nucleating agent is talcum powder, and the dyeing agent is black masterbatch. The mass percentages of the above-mentioned components are shown in Table 1.

[0056] The preparation method of the special composite material for the oil pan of the automobile...

Embodiment 2

[0062] A special composite material for the oil pan of an automobile engine, the composite material contains nylon, alkali-free short glass fibers, modifiers and auxiliary agents; wherein, the nylon is high-temperature nylon PA9T; the alkali-free short glass fibers are treated with silane Coupling agent treatment; the modifier is a mixture of polyethylene (PE) and polyphenylene ether (PPO); the auxiliary agent contains a temperature-resistant anti-aging agent, lubricant, nucleating agent and dyeing agent; The temperature anti-aging agent is a mixture of alkali metal halide potassium bromide and cuprous iodide, the lubricant is a mixture of ethylene bis stearamide and silicone powder, and the nucleating agent is talcum powder; The dyeing agent is black masterbatch. See Table 1 for the weight percentages of the above-mentioned components.

[0063] The preparation method of the special composite material for the oil pan of the automobile engine includes the following steps:

[...

Embodiment 3

[0069] A special composite material for an automobile engine oil pan, the composite material contains nylon, alkali-free short glass fiber, a modifier and an auxiliary agent; wherein, the nylon is high-temperature nylon and is PPA and PA6T; the alkali-free short glass The fiber is treated with a silane coupling agent; the modifier is a mixture of polycarbonate (PC) and polyethylene terephthalate (PET); the auxiliary agent contains a temperature-resistant anti-aging agent, a lubricant, Nucleating agent and dyeing agent; the temperature-resistant anti-aging agent is alkali metal halide cuprous chloride, the lubricant is a mixture of ethylene bis-stearamide and silicone powder, and the nucleating agent is talcum powder ; The dyeing agent is black masterbatch. See Table 1 for the weight percentages of the above-mentioned components. Wherein, the mass percentage of PPA in the composite material is 30%; the mass percentage of PA6T in the composite material is 35%.

[0070] The pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a composite material special for an automobile engine oil pan and a preparation method thereof. The composite material contains nylon, alkali-free short glass fiber, a mineral filler, a modifier and an aid. The nylon is nylon 66, high-temperature nylon or a mixture thereof; the mineral filler is one or a mixture of more of mica, wollastonite, talcpowder, calcium carbonate, barium sulfate and kaolin; the modifier is selected from ABS, PE, PC, PPS, PPO, PBT and PET; and the aid contains a temperature resistant ageing agent, a lubricating agent, a nucleating agent and a coloring agent. The composite material special for the automobile engine oil pan has the advantages of light weight, high design freedom degree, low cost, low rejection rate, and shock and noise resistance. The durability of the material meets the requirement on the service life of ten years (or of accumulatively running 1000,000 km), and the material passes the using test under a cold environment at the low temperature of 30 DEG C below zero, and reaches an international leading level.

Description

technical field [0001] The invention relates to the field of automobile engine oil pans, in particular to a special composite material for automobile engine oil pans and a preparation method thereof. Background technique [0002] The oil pan of the vehicle engine is installed at the bottom of the engine, which is used to store oil and seal the crankcase to prevent impurities from entering, collect and store lubricating oil flowing back from the friction surfaces of the engine, dissipate part of the heat, and prevent lubricating oil from oxidizing, etc. [0003] The development process of automobile engine oil pan materials and corresponding processes is: cast iron or cast aluminum parts - single-layer thin steel stamping parts - die-cast aluminum alloy parts - (metal / plastic / metal) sandwich composite parts - SMC thermosetting Plastic Molded Parts - (Nylon) Thermoplastic Injection Molded Parts. [0004] The oil pan made of aluminum alloy die-casting has good quality indicato...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/00C08L77/06C08L55/02C08L23/06C08L69/00C08L81/02C08L71/12C08L67/02C08K13/06C08K9/06C08K7/14C08K3/34C08K3/26C08K3/30B29C47/92F01M11/00B29C48/92
CPCB29C48/0022B29C48/04B29C48/92B29C2948/9259B29C2948/92704B29C2948/92885B29C2948/92895
Inventor 高原梁效礼杨冬黄俊辉
Owner 辰东意普万新材料(广东)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap