Process method for preparing ultra-fine high-brightness sericite powder by pyrophyllite

A process method, the technology of sericite powder, which is applied in the chemical industry, can solve the problems of limited application fields and low utilization of resources, and achieve the effect of increasing value, improving economic and social benefits, and excellent sheet structure

Active Publication Date: 2010-09-08
厦门博大东方新材料有限公司
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] my country is relatively rich in pyrophyllite resources, but the resource utilization is very low. The previous production process was mainly limited to crushing or wet processing to obtain about 400 mesh of ordinary commodities, which can only be used in building materials, refractory materials, coatings, rubber, Low-end fields such as ordinary ceramics greatly restrict its application fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] (1) Mineral dressing: Raw ore is classified and processed, and 1000kg of qualified ore is selected for washing and drying.

[0009] (2) Crushing and sand making: After drying, the ore is sent to the jaw crusher to crush the fragments below 40×40mm into the sand making machine to make ore below 3×3mm.

[0010] (3) Calcination: Send the ore sand into a high-temperature rotary kiln and calcine for 100 minutes at a temperature of 1030°C for 20 minutes in the high-temperature zone.

[0011] (4) Cooling powder making: the calcined ore enters the rotary cooler and cools to normal temperature, then enters the LHJ-260 ultrafine mechanical pulverizer to be pulverized into 800 mesh fine powder.

[0012] (5) Beating: Send 800-mesh fine powder into the beater according to the ratio of mineral powder and water 1:1, mix and beat at the same time, add 2 kg of sodium dithionite, and stir for 30 minutes at a temperature of 40°C ± 5°C.

[0013] (6) Wet grinding: the prepared slurry is gr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a process method for preparing ultra-fine high-brightness sericite powder by pyrophyllite, which belongs to the chemical field. The process method comprises the following steps: crushing ore with a crusher, adding the crushed ore into a sand making machine to produce sands, feeding the sands into a rotary kiln for calcinations, cooling the calcined ore sands to the room temperature, feeding the cooled ore sands into the crusher, crushing the ore sands into fine powder, feeding the fine powder into a beater, adding sodium hydrosulfite with the weight ratio being 0.1-0.2 percent while beating with the weight ratio of the ore powder and water being 6:4, adding sodium hexametaphosphate while grinding, feeding the ground slurry into a storage tank, adding sulfuric acid according to a weight ratio, feeding the mixture into a high-pressure filter for dehydration, and drying, thereby obtaining the product. The invention has the advantages that: the ultra-fine powder product can be obtained through treatment in the method, and when the particle size is 2mu m, the product can maintain the unique and excellent laminated structure and the excellent radius-thickness ratio, thereby broadening the application scope of the pyrophyllite in high-end products, improving the value of the pyrophyllite, fully developing and utilizing pyrophyllite resources, and increasing the economic and social benefits.

Description

technical field [0001] The invention belongs to the technical field of chemical industry. Background technique [0002] my country is relatively rich in pyrophyllite resources, but the resource utilization is very low. The previous production process was mainly limited to crushing or wet processing to obtain about 400 mesh of ordinary commodities, which can only be used in building materials, refractory materials, coatings, rubber, Low-end fields such as ordinary ceramics have greatly restricted its application fields. The existing sericite powder is mainly produced by purifying mica stone as a raw material, and the process method is simple, mainly including dry crushing and wet grinding processes, and can produce products with a maximum whiteness of 1250 mesh to 2000 mesh and 85. Contents of the invention [0003] The purpose of the invention is to provide a process for preparing superfine high-whiteness sericite powder with pyrophyllite. It can produce ultra-fine powder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B33/42
Inventor 李钦俊李为农
Owner 厦门博大东方新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products