Heat-resistance energy-saving environment-protection epoxy solvent-free paint and production method thereof

An energy-saving, environmentally friendly, solvent-free paint technology, applied in the direction of epoxy resin coatings, coatings, etc., can solve environmental pollution, affect the health of users and other problems, achieve the effect of reducing volume, reducing weight, and saving materials

Inactive Publication Date: 2010-08-18
陕西宏业电工电子新材料有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional lacquer contains a large amount of solvents. During the production and use process, there is a large amount of volatilization of harmful organic aromatic solvents, which causes environmental pollution and affects the health of users.
With the rapid development of domestic economic construction, in order to reduce the volatilization of organic aromatic solvents and reduce environmental pollution, according to different domestic needs, epoxy solvent-free paints have been produced by many domestic companies, but according to national standards, its resistance Most of the thermal grades are B and F grades, which cannot meet the needs of some special environments. Therefore, the research on environmental protection epoxy solvent-free paint has become a research topic for various enterprises.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation Embodiment 1

[0021] Take 900kg of raw material E-44 epoxy resin and 100kg of bismaleimide, heat the raw material E-44 epoxy resin to 135±5℃, slowly add bismaleimide, keep it warm for 2.5h, and the material to be sampled Clear, remove from heat, and cool.

[0022] Take 661.8kg of tung oil, 147.2kg of maleic anhydride, and 190kg of bismaleimide. First, heat the tung oil to 100±5°C to remove water, keep it at this temperature for 1 hour, and then lower the temperature to 80°C after removing water. Add maleic anhydride, then raise the temperature to 140°C, keep it warm for 0.5h, slowly add bismaleimide at this temperature, after adding bismaleimide, increase the temperature at 5°C / min to 200±2 ℃, keep warm for 1h, and after 2-3min by the conventional knife method, cool down and discharge the material, the material is transparent after cooling.

[0023] Take 400kg of heat-resistant polyester as raw material, 100kg of modified epoxy resin, 100kg of tungalin anhydride, 300kg of vinyltoluene, 15k...

preparation Embodiment 2

[0025] The difference between this embodiment and Example 1 is that the raw material E-44 epoxy resin is changed into CYD-128 epoxy resin, and the weight ratio of CYD-128 epoxy resin and bismaleimide is according to 10:1 Preparation, namely CYD-128 epoxy resin 1000kg, bismaleimide 100kg, all the other are with embodiment 1.

preparation Embodiment 3

[0027] The difference between this embodiment and Example 1 is that the add-on of heat-resistant polyester is 500kg, the add-on of modified epoxy resin is 80kg, and all the other are the same as Example 1.

[0028] 4) Finished product inspection

[0029] Appearance: Orange-yellow transparent liquid

[0030] Particle size: large 4 viscosity cups, 20±2°C, 20-40 seconds

[0031] Curing time: 140°C±2°C <60min

[0032] Electric strength: normal >22kv / mm

[0033] 180℃±2℃ >16kv / mm

[0034] Soak in water for 24h >20kv / mm

[0035] Volume resistivity: normal >1×10 12 (Ω·m)

[0036] Soak in water for 24h >1×10 10 (Ω·m)

[0037] 180℃±2℃>1×10 8 (Ω·m)

[0038] Adhesive force: normal > 100N,

[0039] Temperature index > 180.

[0040] The heat-resistant, energy-saving and environment-friendly epoxy solvent-free paint prepared by the present invention is H-grade heat-resistant grade, that is, the working temperature is increased from 130°C to 155°C to 180°C, and the curing temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses heat-resistance energy-saving environment-protection epoxy solvent-free paint. The prepared heat-resistance energy-saving environment-protection epoxy solvent-free paint consists of the following ingredients in percentage by weight: 40 to 50 percent of heat-resistance polyester, 8 to 10 percent of modified epoxy, 10 to 12 percent of tongma estolide, 30 to 40 percent of vinyltoluene, 1 to 1.5 percent of cumyl peroxide, 0.02 percent of hydroquinone and 0.02 percent of epoxide resin curing agents, wherein the percentage sum of the ingredients is 100 percent. The grade H heat-resistance grade can be reached, i.e. the work temperature is improved from 130 DEG C to 155 DG C to 180 DEG C, the energy is saved, materials are saved, the invention is favorable for size reduction, weight reduction and material saving of mechanical and electrical products, the volatile substances are reduced by 20 to 30 percent, and the invention has the advantages of heat resistance, energy saving, environment protection and the like.

Description

technical field [0001] The invention relates to a solvent-free paint and its preparation, in particular to a heat-resistant, energy-saving and environment-friendly epoxy solvent-free paint and a production method thereof. Background technique [0002] Traditional lacquer contains a large amount of solvents. During the production and use process, there is a large amount of volatilization of harmful organic aromatic solvents, which causes environmental pollution and affects the health of users. With the rapid development of domestic economic construction, in order to reduce the volatilization of organic aromatic solvents and reduce environmental pollution, according to different domestic needs, epoxy solvent-free paints have been produced by many domestic companies, but according to national standards, its resistance Most of the thermal grades are B and F grades, which cannot meet the needs of some special environments. Therefore, research on environmentally friendly epoxy sol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D163/10
Inventor 俞翔霄
Owner 陕西宏业电工电子新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products