Anticorrosive sealing liquid and method for sealing anodic oxide film containing copper-aluminium alloy by utilizing same

An anodized film, copper-aluminum alloy technology, applied in electrolytic coatings, surface reaction electrolytic coatings, coatings, etc., can solve the problems of short life of the sealing solution, difficult to control hot water, generation of dirt, etc., and achieve stable sealing effect. , easy to control, cost-saving effect

Inactive Publication Date: 2011-12-21
BEIHANG UNIV
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Hot water often creates fouling on sealing surfaces, while hot water is difficult to control in large-scale production due to pH changes and contamination (e.g. phosphates, silicates, and chlorides), resulting in short sealing solution life
Hot water sealing takes a long time (2min / μm) and high energy consumption is the obvious disadvantage of hot water sealing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anticorrosive sealing liquid and method for sealing anodic oxide film containing copper-aluminium alloy by utilizing same
  • Anticorrosive sealing liquid and method for sealing anodic oxide film containing copper-aluminium alloy by utilizing same
  • Anticorrosive sealing liquid and method for sealing anodic oxide film containing copper-aluminium alloy by utilizing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The first step: sample selection

[0040]The sample is the LY11 alloy treated according to the People's Republic of China Aviation Industry Standard "Sulfuric Acid Anodizing Process for Aluminum and Aluminum Alloys" (HB / Z233-93), with a size of 100mm×50mm×2.5mm;

[0041] The thickness of the anodized film on the surface of the LY11 alloy measured by a vortex thickness gauge is 3 μm. The morphology of the anodized film was observed with a scanning electron microscope (Hitachi S-4800 SEM). figure 2 As shown in the figure, there are holes in the anodized film.

[0042] Step 2: Prepare corrosion inhibiting sealing solution

[0043] The corrosion inhibition blocking solution is to dissolve 10g of ammonium adipate and 10μg of 2-mercaptobenzothiazole in 100ml of deionized water at a temperature of 25°C, and measure the pH value with the FE20 model FiveEasy pH meter produced in Switzerland. 7.0;

[0044] The third step: closed processing

[0045] (A) Add the corrosion-inh...

Embodiment 2

[0055] The first step: sample selection

[0056] The sample is LC5 alloy treated by boric acid-sulfuric acid anodizing process (U.S. Pat. No. 4,894, 127, Jan. 16, 1990), with a size of 100mm×50mm×2.5mm;

[0057] Step 2: Prepare corrosion inhibiting sealing solution

[0058] The corrosion-inhibiting blocking solution is to dissolve 5 g of ammonium adipate and 50 μg of benzotriazole in 100 ml of deionized water at a temperature of 40° C., and measure the pH value to 6.8 with a pH meter;

[0059] The third step: closed processing

[0060] (A) Add the environment-friendly corrosion-inhibiting sealing solution prepared in the second step into the stainless steel electrolytic cell, and the consumption of the corrosion-inhibiting sealing solution is 2 / 3 of the volume of the electrolytic cell;

[0061] (B) heating the corrosion inhibiting sealing solution to 100°C;

[0062] (C) The sample selected in the first step is completely immersed in the corrosion-inhibiting sealing solution...

Embodiment 3

[0066] The first step: sample selection

[0067] The sample is LY17 alloy treated according to the People's Republic of China Aviation Industry Standard "Sulfuric Acid Anodizing Process for Aluminum and Aluminum Alloys" (HB / Z233-93), with a size of 100mm×50mm×2.5mm;

[0068] Step 2: Prepare corrosion inhibiting sealing solution

[0069] The corrosion inhibition sealing solution is to dissolve 15g of ammonium adipate and 45 μg of quinaldicic acid in 100ml of deionized water at a temperature of 30°C, and measure the pH value to 7.2 with a pH meter;

[0070] The third step: closed processing

[0071] (A) Add the corrosion-inhibiting sealing solution prepared in the second step into the stainless steel electrolytic cell, and the consumption of the corrosion-inhibiting sealing solution is 2 / 3 of the volume of the electrolytic cell;

[0072] (B) heating the corrosion inhibiting sealing solution to 90°C;

[0073] (C) The sample selected in the first step is completely immersed in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses anticorrosive sealing liquid and a method for sealing an anodic oxide film containing a copper-aluminium alloy by utilizing the same. The anticorrosive sealing liquid is prepared by dissolving 5-15g of adipate and 10-100mu g of anticorrosive in 100ml of deionized water. The anticorrosive is 2-mercaptobenzothiazole, benzotriazole, salicylaldoxime, 8-hydroxyquinoline or quinaldic acid. The sealing method is characterized by sealing the anodized copper-aluminium alloy in the electric field. By the sealing method, not only the micropores of the anodic oxide film are sealed, but also the anticorrosive is adsorbed in the anodic oxide film in the applied electric field, when the anodic oxide film is corroded, the anticorrosive is released from the micropores of the anodicoxide film through capillarity to play a role of corrosion inhibition to the copper-bearing phases in the base materials containing the copper-aluminium alloys to prevent further corrosion.

Description

technical field [0001] The invention relates to a sealing technology suitable for copper-containing aluminum alloy anodic oxidation film, in particular to a corrosion-inhibiting sealing liquid and a method for sealing the copper-containing aluminum alloy anodic oxidation film. Background technique [0002] Anodic oxidation is the most commonly used surface treatment method for aluminum and aluminum alloys. Porous anodized films will be formed on the surface of aluminum and aluminum alloys after anodization. Composed of two parts. Although this porous characteristic endows the anodized film with the ability to color and other functions, it is impossible to meet the requirements for corrosion resistance, weather resistance, and pollution resistance. Therefore, considering practical application, the anodized film of aluminum and aluminum alloy must be sealed. [0003] The aviation industry standard of the People's Republic of China "Sulfuric Acid Anodizing Process of Aluminum...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25D11/18
Inventor 刘建华李永星于美李松梅李英东李明
Owner BEIHANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com