Preparation method of forging mold by using composite build-up welding and spray welding method

A composite welding and forging die technology, applied in welding equipment, arc welding equipment, manufacturing tools, etc., can solve the problems of low service life, poor forging die performance, low service life, etc., to improve equipment utilization, improve mold The effect of improving performance and life

Active Publication Date: 2010-07-07
CHONGQING JIEPIN TECH
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, my country's forging industry mainly uses 5CrNiMo, 5CrMnMo, H13, etc. as die steels. These steel types have certain hardenability, high temperature strength and impact toughness, but generally have a low service life.
At the same time, the preparation methods of forging dies in my country are basically made by heat treatment after forging. The forging dies made by this method have poor performance and relatively low service life, which is only equivalent to 1 / 3 to 1 / 5 of foreign countries.
Most of the failed molds are scrapped only because the thin layer of the working layer on the surface is worn or partially thermally corroded and peeled off, resulting in a huge waste of resources
According to statistics, the steel consumption and energy waste caused by the low life of the mold, as well as the loss caused by the impact on product quality, amount to tens of billions of yuan every year.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of forging mold by using composite build-up welding and spray welding method
  • Preparation method of forging mold by using composite build-up welding and spray welding method
  • Preparation method of forging mold by using composite build-up welding and spray welding method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The present invention will be described in further detail below in conjunction with the accompanying drawings and specific embodiments.

[0032] The forging die that needs to be prepared in this specific embodiment is the lower die of a common forging die, and the cross-sectional structure to be welded is as follows: figure 1 As shown, its preparation method comprises the following steps carried out in sequence:

[0033] a. Use the newly made 5CrNiMo mold as the matrix, and reserve a margin on the surface of the matrix cavity and form a wave shape. Such as figure 1 shown.

[0034] b. Using the automatic gas shielded surfacing welding process, the transition layer is surfacing on the surface of the mold base cavity, and the transition layer is evenly distributed.

[0035] c. Use one-step spray welding to spray and weld self-fluxing alloy powder on the surfacing transition layer to form a surface strengthening layer. The hardness and toughness of this layer are higher...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention initially provides a preparation method of a forging mold by using a composite build-up welding and spray welding method, combined with the characteristics of the build-up welding and the spray welding, and aiming at the status quo of the traditional forging mold manufacturing technology in China at present. The method comprises the following steps of: a. forging a forging mold substrate and carrying out thermal refining, wherein an allowance is reserved at a substrate cavity; b. build-up welding uniformly distributed build-up welding transition layers on a specific cavity surface by using an automatic gas shield build-up welding technique; c. forming a surface reinforcement layer on the surface of the transition layer by using a one-step spray welding method; d. finishing the spray welding and carrying out the remelting and warming at once by using a tempering and slow cooling technique; and e. fine finishing, and putting the size of each part of the cavity in place. Compared with the traditional preparation method of the forging molds, the production cost is reduced, the condemnation factor of a product is decreased, meanwhile, the joint strength of the mold substrate and a welding layer is enhanced, the strength and the impact toughness of the mold are improved, the wear-resisting and the thermal fatigue resistance properties of a surface layer are optimized, and the property of the mold surpasses that of the new-made integral molds of 5CrNiMo and 5CrMnMo.

Description

technical field [0001] The invention relates to the field of molds, in particular to a method for preparing a forging mold. Background technique [0002] In the manufacturing industry, molds are the basic process equipment for industrial production. The level of mold production technology largely determines product quality, efficiency and new product development capabilities, and has become an important symbol to measure the level of a country's product manufacturing. [0003] At present, my country's forging industry mainly uses 5CrNiMo, 5CrMnMo, H13, etc. as die steels. These steel types have certain hardenability, high temperature strength and impact toughness, but generally have a low service life. At the same time, the preparation methods of forging dies in my country are basically made by heat treatment after forging. The forging dies made by this method have poor performance and relatively low service life, which is only equivalent to 1 / 3 to 1 / 5 of foreign countries....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/24B23K9/04C23C4/06
Inventor 周杰卢顺
Owner CHONGQING JIEPIN TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products