Water-based PU brush surface conditioning agent for synthetic leather

A technology of synthetic leather and surface treatment agent, applied in fiber processing, textiles and papermaking, etc., can solve the problems of poor stability, poor hand feel, dissolution of the bottom layer of synthetic leather, poor hand feel of synthetic leather, etc., and achieve comprehensive effects. Excellent, solvent-resistant coating, excellent cross-linking hardness

Inactive Publication Date: 2010-05-12
JIANGSU BAOZE POLYMER MATERIAL
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1. The organic solvent contained in the solvent-based powder surface treatment agent will cause the bottom layer of synthetic leather or artificial leather to dissolve, and the treated synthetic leather will not feel good;
[0005] 2. The organic solvent contained in the solvent-based powder surface treatment agent not only has high cost, strong smell, and is easy to pollute the environment, but also has safety hazards such as flammability and explosion;
[0006] 3. The synthetic leather products prepared by solvent-based powder rubbing agent have poor comprehensive effects such as stability and hand feeling

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 1. The water-based PU powder surface treatment agent for synthetic leather is composed of the following raw materials: 100 kg of water-based baking varnish resin, 20 kg of water-based polyurethane (30% solid content), 400 kg of tap water, 54 kg of silica matting powder, and water-based modified polyester. 25 kg of ethylene wax emulsion, 12 kg of silicone defoamer, and 6 kg of silicone leveling agent.

[0026] 2. The preparation method of the water-based PU powder rubbing surface treatment agent for synthetic leather of the present invention is as follows:

[0027] ① Select 100 kg of water-based baking varnish resin according to the above ratio, 20 kg of water-based polyurethane (30% solid content), 400 kg of tap water, 12 kg of silicone defoamer, 6 kg of silicone leveling agent, and 25 kg of water-based modified polyethylene wax emulsion kg, mix, stir;

[0028] ② Take 54 kg of silica matting powder and add the mixture obtained in step ① while stirring and stir for 90 m...

Embodiment 2

[0034] 1. The water-based PU water-based powder surface treatment agent for synthetic leather is composed of the following raw materials: 60 kg of water-based baking varnish resin, 10 kg of water-based polyurethane (30% solid content), 200 kg of tap water, 30 kg of silica matting powder, water-based modified Polyethylene wax emulsion 15 kg, silicone defoamer 8 kg, silicone leveling agent 3 kg.

[0035] 2. The preparation method of the water-based PU powder rubbing surface treatment agent for synthetic leather of the present invention is as follows:

[0036] ① Select 60 kg of water-based baking varnish resin according to the above ratio, 10 kg of water-based polyurethane (30% solid content), 200 kg of tap water, 3 kg of silicone leveling agent, 8 kg of silicone defoamer, and 15 kg of water-based modified polyethylene wax emulsion. kg, mix, stir;

[0037] ② Take 30 kg of silica matting powder and add the mixture obtained in step ① while stirring and stir for 90 minutes;

[003...

Embodiment 3

[0043] 1. The water-based PU water-based powder surface treatment agent for synthetic leather is composed of the following raw materials: 40 kg of water-based baking varnish resin, 6 kg of water-based polyurethane (30% solid content), 150 kg of tap water, 25 kg of silica matting powder, water-based modified 9 kg of polyethylene wax emulsion, 5 kg of silicone defoamer, 1.5 kg of silicone leveling agent.

[0044] 2. The preparation method of the water-based PU powder rubbing surface treatment agent for synthetic leather of the present invention is as follows:

[0045] ① Select 40 kg of water-based baking varnish resin according to the above ratio, 6 kg of water-based polyurethane (30% solid content), 150 kg of tap water, 1.5 kg of silicone leveling agent, 5 kg of silicone defoamer, and 9 kg of water-based modified polyethylene wax emulsion kg, mix, stir;

[0046] ② Take 25 kg of silica matting powder and add the mixture obtained in step ① while stirring and stir for 90 minutes;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based PU brush surface conditioning agent for synthetic leather, which comprises the following materials by weight percent: 10 to 20 percent of water-based stoving varnish resin, 1 to 6 percent of water-based polyurethane, 60 to 70 percent of water, 5 to 13 percent of silicon dioxide matting agent, 0.5 to 2 percent of organic silicon flatting agent, 1 to 5 percent of organic silicon foam killer and 2 to 6 percent of water-based modified polyethylene wax emulsion. In the water-based PU brush surface conditioning agent for synthetic leather, water is taken as solvent to replace noxious solvents, such as dimethyl formamide and butanone, so that the water-based PU brush surface conditioning agent has the performances of non-inflammation, safety, environmental protection and cost saving, and resin has the advantages of good film reforming property, firm bonding, solvent resistance, cold resistance, hydrolysis resistance and thermosenescence resistance of coating, and the finished product made of the surface conditioning agent has unique brush effect, strong dermis effect, water resistance and good air permeability.

Description

technical field [0001] The invention relates to a water-based PU resin for synthetic leather, in particular to a water-based PU powder surface treatment agent for synthetic leather used in the post-process of synthetic leather. Background technique [0002] With the improvement of people's living standards, people are gradually pursuing high-quality daily products, and the demand for leather products is increasing. With the enhancement of animal protection awareness, animal leather can no longer meet people's needs. At present, synthetic leather products have gradually become a popular trend in the future. Synthetic leather has been widely used in the production of luggage, clothing, footwear and other products. The base fabric of PU leather is canvas PU material with good tensile strength. In addition to being coated on the base fabric In addition to the upper surface, the base fabric can also be included in the middle, so that the existence of the base fabric cannot be see...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/564D06M15/227D06M11/79D06M13/50D06N3/14
Inventor 时云刚
Owner JIANGSU BAOZE POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com