Micro-alloying compound cored wire for high-strength steel

A technology of micro-alloying and high-strength steel, which is applied in the field of cored wire, can solve the problems of center segregation and low isotropic performance, improve the grain size, solve the problem of central segregation center looseness and uneven distribution of impurities, The effect of improving mechanical properties

Inactive Publication Date: 2010-05-12
HUBEI KMK WELDING MATERIALS
View PDF3 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a high-strength micro-alloyed composite cored wire, which is mainly aimed at technical problems such as central segregation, low transverse impact performance, and low isotropic performance in the current high-strength steel smelting slab.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Micro-alloying compound cored wire for high-strength steel
  • Micro-alloying compound cored wire for high-strength steel
  • Micro-alloying compound cored wire for high-strength steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Example 1: The particle size of the powdered particles in the cored wire powdered inner core is 1 to 1.2 mm, and the powdered inner core is wrapped by a carbon steel outer skin to make a cored wire with a diameter of 13 mm. The carbon steel outer skin is made of 08Al steel strip with a thickness of 0.3-0.4 mm, and the element composition and mass in the powdered inner core are: Ca 22%, Si 51%, Mg 0.65%, Ba 2.5%, Re 0.6 %, B 1.2%, Zr 1.6%, Ti.2.8%, Nb 0.6%, the balance is iron and unavoidable impurities.

Embodiment 2

[0021] Example 2: The particle size of the powdery particles in the powdered core of the cored wire is 1.2-1.5 mm, and the powdered core is wrapped by a carbon steel outer skin to make a cored wire with a diameter of 13 mm. The carbon steel outer skin adopts a low-carbon steel strip with a thickness of 0.3-0.4 mm. The element composition and mass% in the powdery inner core are: Ca 28%, Si 55%, Mg 1.5%, Ba 1.3%, Re 1.0%, B 0.6%, Zr 3.5%, Ti 1.3%, Nb 1.2%, the balance is iron and inevitable impurities.

Embodiment 3

[0022] Example 3: The particle size of the powdery particles in the cored wire powdered inner core is 1 to 1.5 mm, and the powdered inner core is wrapped by a carbon steel outer skin to make a cored wire with a diameter of 13 mm. The carbon steel outer skin is made of 08Al steel strip with a thickness of 0.3-0.4 mm. The element composition and mass% in the powdered inner core are: Ca 25%, Si 53%, Mg 1.0%, Ba 2.0%, Re 0.8 %, B 0.8%, Zr 2.0%, Ti 2.0%, Nb 0.8%, the balance is iron and unavoidable impurities.

[0023] In order to further verify the effects of the present invention, the inventors conducted the following performance tests, and the results are as follows.

[0024] 1. Using the cored wire obtained in Example 3, add 2 kg of powdered core per ton of molten steel (KD type high-strength steel, Rm≥800MPa, impact toughness CV=250-300J, -20℃) Cored wire. Then analyze the slag samples before and after the cored wire is added, and the results are shown in Table 1.

[0025] Table 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a micro-alloying compound cored wire for high-strength steel, comprising a carbon steel sheath and a powdery core, wherein the core is prepared from the following chemical components by weight percent: 23 to 28 wt% of Ca, 51 to 55 wt% of Si, 0.65 to 1.5 wt% of Mg, 1.3 to 2.5 wt% of Ba, 0.6 to 1.0 wt% of Re, 0.6 to 1.2 wt% of B, 1.6 to 3.5 wt% of Zr, 1.3 to 2.8 wt% of Ti, 0.6 to 1.2 wt% of Nb, and balance of ferrum and inevitable impurities. The invention reduces the content of C in high-strength steel through reasonably designing the chemical components and simultaneously and greatly enhances the grain sizes in continuous casting billets so that the grains are refined. The mechanical properties of the steel can be obviously improved, and the transverse impact properties of the steel are obviously enhanced to approximate to longitudinal impact value. Besides, the invention well solves the problems of center segregation and center porosity of the continuous casting billets, nonuniform impurity distribution, and the like.

Description

Technical field [0001] The invention relates to a cored wire, in particular to a microalloyed composite cored wire for high-strength steel. Background technique [0002] With the rapid development of my country's national economy, the development of the domestic steel industry has also grown rapidly. In recent years, my country's steel production has been ranked first in the world. China is a veritable steel power, but it is not a steel power. High-strength, high-toughness, and high-value-added steel products still need to be imported in large quantities from abroad. Therefore, the development of high-performance, high-value-added steel products to make China a strong steel country as soon as possible has always been the direction of our people, especially the metallurgical industry. [0003] In addition to scientific rolling and heat treatment processes for high-strength steel plates with excellent performance, reasonable composition design is also the key to production. Althou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21C7/00C22C1/10
Inventor 樊兴龙李志远
Owner HUBEI KMK WELDING MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com