Diatom ooze coating special for underground space and preparation and application thereof

A technology of diatom mud coating and underground space, applied in the direction of coating, etc., can solve the problems of poor waterproof effect, poor aging resistance and high bonding strength of waterproof coating, and achieve good waterproof and impermeability effect and bonding strength. Large, good extension performance

Inactive Publication Date: 2009-11-04
SHANGHAI XINWANG ANTICORROSION VACUUM FLASK
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a special diatom mud coating for underground space and its preparation and application. Water-based, the water droplets on its surface are like the water droplets on the lotus leaf; it has unique waterproof performance, resistance to ultraviolet radiation, and anti-aging; it avoids the poor waterproof effect and aging resistance of a simple polymer emulsion waterproof coating Poor performance and other shortcomings; it can be made into various colors according to needs; it can make the wall have a "free breathing function", and can automatically adjust the humidity with the change of the indoor ambient air humidity; Oxygen ions, negative oxygen ions can restore oxygen free radicals in the air, and have high bonding strength, good waterproof and shock resistance, and moderate price

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Diatom ooze coating special for underground space and preparation and application thereof
  • Diatom ooze coating special for underground space and preparation and application thereof
  • Diatom ooze coating special for underground space and preparation and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A special diatom mud coating formula for underground space:

[0030] Raw material name Mass percentage (%)

[0031] Pure Acrylic Emulsion 18

[0032] Silicone Emulsion 5

[0033] Diatom mud 20

[0034] Sericite powder 12

[0035] Wollastonite powder 15

[0036] Titanium dioxide (rutile type) 8

[0037] Sodium hexametaphosphate 1

[0038] Ethylene glycol butyl ether 1

[0039] Dibutyl phthalate 1

[0040] Sodium pentachlorophenate 0.5

[0041] Silicone defoamer 0.1

[0042] water 18.4

[0043] crafting process:

[0044] Take water and add sodium hexametaphosphate, stir evenly, add diatom mud, wollastonite powder, titanium dioxide, stir evenly, grind on a three-roller grinder, take samples for testing, stop grinding when the sample particles reach 5-10μm, and add pure acrylic acid Emulsion, silicone emulsion, ethylene glycol butyl ether, dibutyl phthalate, sodium pentachlorophenate, stir evenly, add silicone defoamer, stir evenly, test, filter, pack, and get r...

Embodiment 2

[0046] A special diatom mud coating formula for underground space:

[0047] Raw material name Mass percentage (%)

[0048] Pure Acrylic Emulsion 16

[0049] Silicone Emulsion 10

[0050] Diatom mud 10

[0051] Sericite powder 15

[0052] Wollastonite powder 10

[0053] Titanium dioxide (rutile type) 10

[0054] Sodium hexametaphosphate 1

[0055] Ethylene glycol butyl ether 1

[0056] Dibutyl phthalate 1

[0057] Sodium pentachlorophenate 0.1

[0058] Silicone defoamer 0.1

[0059] water 15.8

[0060] crafting process:

[0061] Take water and add sodium hexametaphosphate, stir evenly, add diatom mud, wollastonite powder, titanium dioxide, stir evenly, grind on a three-roller grinder, take samples for testing, stop grinding when the sample particles reach 5-10μm, and add pure acrylic acid Emulsion, silicone emulsion, butyl glycol ether, dibutyl phthalate, sodium pentachlorophenate, stir evenly, add silicone defoamer, stir evenly, test, filter, pack, and get ready.

Embodiment 3

[0063] A special diatom mud coating formula for underground space:

[0064] Raw material name Mass percentage (%)

[0065] Pure Acrylic Emulsion 10

[0066] Silicone Emulsion 15

[0067] Diatom mud 15

[0068] Sericite powder 12

[0069] Wollastonite powder 15

[0070] Titanium dioxide (rutile type) 12

[0071] Sodium hexametaphosphate 1

[0072] Ethylene glycol butyl ether 2

[0073] Dibutyl phthalate 2

[0074] Sodium pentachlorophenate 0.4

[0075] Silicone defoamer 0.2

[0076] water 15.4

[0077] crafting process:

[0078] Take water and add sodium hexametaphosphate, stir evenly, add diatom mud, wollastonite powder, titanium dioxide, stir evenly, grind on a three-roller grinder, take samples for testing, stop grinding when the sample particles reach 5-10μm, and add pure acrylic acid Emulsion, silicone emulsion, butyl glycol ether, dibutyl phthalate, sodium pentachlorophenate, stir evenly, add silicone defoamer, stir evenly, test, filter, pack, and get ready. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a diatom ooze coating special for underground space and preparation and application thereof. The coating is prepared by taking a polymer as a main film forming substance, water as a solvent, diatom ooze and the like as fillings and adding other addition agents. The coating takes the water as the solvent, so the coating has no toxicity and resistance to ultraviolet radiation, can generate negative oxygen ions, has high adhesive strength, good waterproof and quake-proof effects and moderate cost, and is widely used for decorating the inner walls of buildings such as office buildings, residential buildings, hospitals, schools, factory buildings, markets, and entertainment places; the coating has high adhesive strength, good effects of water resistance and permeability resistance, thermal resistance, frost resistance and good extensibility; the coating is performed cold construction, is directly painted, and is operated conveniently; and the coating is applicable to the water resistance, permeability resistance and moisture resistance of various buildings such as new and old roofs, basements, toilets, grain warehouse, dams, oil warehouses, pipelines, swimming pools, tunnels, construction gaps, expansion joints, roads and bridges and the like.

Description

technical field [0001] The invention belongs to the field of waterproof paint and its preparation and application, in particular to a special diatom mud paint for underground space and its preparation and application. Background technique [0002] Most waterproof projects in my country use traditional waterproof materials, which have disadvantages such as poor aging resistance, low tensile strength, and sensitivity to temperature. Used for roof waterproofing, it is easy to cause aging, cracking, deformation, breaking, delamination and other phenomena. It is used for indoor waterproofing. For places with complex shapes, it is difficult to construct, and it is even more difficult to guarantee the quality of leakage. People spend a lot of money and labor on rework every few years. It not only disrupts people's normal life, work and production order, but also directly affects the service life of the entire building. [0003] At present, there are many kinds of waterproof coat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D7/12C09D5/00
Inventor 张心旺
Owner SHANGHAI XINWANG ANTICORROSION VACUUM FLASK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com