Tungsten disulfide based high-temperature dry-film lubricant

A dry film lubricant, tungsten disulfide-based technology, applied in lubricating compositions, base materials, additives, etc., can solve the problems of unsatisfactory wear resistance and poor wear resistance, and achieve a wide processing temperature range, Good wear resistance

Inactive Publication Date: 2009-10-21
上海鑫氟化工材料有限公司
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the existing dry film lubricant products are based on molybdenum disulfide, and often contain heavy metal lead, and these lubricants have poor wear resistance under high load-carrying capacity and high-speed operation. The wear resistance of the product applied to the swash plate parts of the automotive air-conditioning compressor is not satisfactory

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A tungsten disulfide-based high temperature resistant dry film lubricant, the lubricant comprises the following components and content: tungsten disulfide 30wt%, polyamide-imide 30wt%, the glass transition temperature of the polyamide-imide is greater than 270 degrees, polytetrafluoroethylene (PTFE) 5wt%, anti-friction filler antimony trioxide and copper oxide 20wt%, mixed solvent of butanone and dimethylformamide 14wt%, auxiliary wetting agent, leveling agent and enhancer Thickener 1%.

[0017] Disperse the solid substance in the above formula in the mixed solvent, and then grind it into viscous liquid.

Embodiment 2

[0019] A tungsten disulfide-based high temperature resistant dry film lubricant, the lubricant comprises the following components and content: polyamide-imide 60wt%, tungsten disulfide 5wt%, polytetrafluoroethylene (PTFE) 20wt%, anti-friction filler Zirconia 0.2wt%, mixed solvent N-methylpyrrolidone, xylene 13.8wt%, auxiliary agent thickener 1%.

[0020] Manufacturing method is the same as Example 1

Embodiment 3

[0022] A tungsten disulfide-based high temperature resistant dry film lubricant, the lubricant includes the following components and content: polyamide-imide and bisphenol A epoxy resin 20wt%, tungsten disulfide 5wt%, polytetrafluoroethylene (PTFE) 30wt%, antifriction filler aluminum oxide, silicon carbide, calcium fluoride, lanthanum fluoride 4wt%, the mixed solvent 40wt% of butanone, dimethylformamide, N-methylpyrrolidone and xylene, auxiliary agent wetting agent 1%.

[0023] Manufacturing method is the same as Example 1

[0024] Spray the viscous liquid on a clean metal aluminum plate, and after curing for half an hour at 220--280°C, conduct characteristic tests such as hardness, adhesion, and wear resistance.

[0025] The following table shows the 3 groups of parameter test experiments of the obtained lubricant

[0026] The performance test is as follows:

[0027] example 1

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a tungsten disulfide based high-temperature dry-film lubricant which comprises the following components according to the weight percent: 20-70 of caking agent, 5-30 of tungsten disulfide, 5-30 of polyfluortetraethylene, 0.2-20 of wear resistant filling material, 10-40 of component solvent and the balance of addition agent. Compared with the prior art, the invention has the characteristics of high loading capacity, better wear resistance under the condition of high rotating speed, wide processing temperature range and the like.

Description

technical field [0001] The invention relates to a lubricant, in particular to a tungsten disulfide-based high temperature resistant dry film lubricant. Background technique [0002] In order to reduce the wear and power consumption caused by the mechanical movement of equipment and components, people usually reduce friction and reduce wear by coating or adding lubricating grease. Most of the existing dry film lubricant products are based on molybdenum disulfide, and often contain heavy metal lead, and these lubricants have poor wear resistance under high load-carrying capacity and high-speed operation. The wear resistance of this product applied to the swash plate parts of the automobile air-conditioning compressor is not satisfactory. Contents of the invention [0003] The purpose of the present invention is to provide a tungsten disulfide-based high-temperature-resistant dry film lubricant with high load-bearing capacity, better wear resistance under high-speed conditio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10M103/06C10M147/02C10M149/18C10M145/18C10M145/20C10N50/02
Inventor 申勇谢华
Owner 上海鑫氟化工材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com