Producing method for a high strength ultra-thin anode supporting type solid oxide fuel cell

An anode-supported, solid oxide technology, used in solid electrolyte fuel cells, fuel cell parts, battery electrodes, etc., can solve problems such as high cost, and achieve improved mechanical strength, good catalytic performance, and easily controllable conditions. Effect

Active Publication Date: 2011-01-19
NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high cost of this type of fuel cell system at that time, it was only used in special occasions such as aerospace and military

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Producing method for a high strength ultra-thin anode supporting type solid oxide fuel cell
  • Producing method for a high strength ultra-thin anode supporting type solid oxide fuel cell
  • Producing method for a high strength ultra-thin anode supporting type solid oxide fuel cell

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] The green body of the anode support is prepared by tape casting. The experimental materials are NiO powder and 3% (mol) YSZ powder, weighing 268.8 grams of NiO and 211.2 grams of 3% (mol) YSZ powder (60% of the total mass of the slurry, wherein YSZ: NiO is 0.44: 0.56) and mixed uniformly, Then add ethanol and 2-butanone mass ratio and be 30% and 70% mixed solvent 280 grams (35% of slurry total mass) and 40 grams of polyvinyl butyral (5% of slurry total mass), will Put the above mixture into a 1000ml ball mill tank, then put in a zirconia ball milling medium with three times the mass of the powder, and then ball mill at a speed of 250rpm for 24 hours, and degas the slurry on a small defoamer for 80 minutes to obtain a cast slurry (The distance between the casting knife edge and the support plate is controlled at 1 mm), and the green body of the anode support body with a thickness of 600 μm can be prepared by the casting machine.

[0049] The active anode was prepared by...

Embodiment 2

[0056] The green body of the anode support is prepared by tape casting. The experimental materials are NiO powder, alumina powder and 3% (mol) YSZ powder, weighing 162.4 grams of NiO and 127.6 grams of 3% (mol) YSZ powder (29% of the total mass of the slurry, wherein YSZ: NiO is 0.44: 0.56 ) and 10 grams of aluminum oxide (1% of the total mass of the slurry) are mixed uniformly, and then adding ethanol and 2-butanone mass ratio is 550 grams of mixed solvents (55% of the total mass of the slurry) and 150% of the mixed solvent of 30% and 70%. gram of polyvinyl butyral (15% of the total mass of the slurry), the above mixture is put into a 1000ml ball mill jar, then put into a zirconia ball mill medium with three times the quality of the powder, and then ball mill for 24 hours at 280rpm , the slurry was defoamed on a small defoaming machine for 120 minutes to obtain casting slurry (the distance between the casting blade and the support plate was controlled at 1 mm), and the green ...

Embodiment 3

[0063]The anode support green body is prepared by the casting method. The experimental materials are NiO powder, alumina powder and 3% (mol) YSZ powder, weighing 211.68 grams of NiO, 166.32 grams of 3% (mol) YSZ powder (42% of the total mass of the slurry, where YSZ:NiO is 0.44:0.56 ) mixed with 27 grams of alumina (3% of the total mass of the slurry), and then added 405 grams of mixed solvent (45% of the total mass of the slurry) and a mixture of ethanol and 2-butanone with a mass ratio of 30% and 70%. 90 grams of vinyl butyral (10% of the total mass of the slurry), put the above mixture into a 1000ml ball mill, and then put three times the mass of the powder into a zirconia ball milling medium, and then ball mill for 24 hours at a rotating speed of 360 rpm , defoaming the slurry on a small defoaming machine for 160 minutes to obtain a casting slurry (the distance between the casting knife edge and the support plate is controlled at 1 mm), and a green anode support body with ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a high-strength ultra-thin anode supported solid oxide fuel cell, the method comprises: the slurry of an anode support is firstly used for preparing an anode support green compact with a certain thickness by a tape casting method, then an active anode slurry and an electrolyte slurry are sprayed onto the anode support green compact by using an air direct spraying method, the green compact of the composite material is further increased to a certain temperature by a certain heating rate for the calcination, then a half cell is obtained, then the cathode slurry is finally sprayed on the half cell by the air spraying method, and a single cell is obtained by drying, calcinating and other steps. The obtained flat-plate single cell has the advantages of high mechanical strength of the anode support, even thin active anode, conditional method, easy control, simple process, easy industrial enlargement, etc.

Description

technical field [0001] The invention relates to a preparation method of a solid oxide fuel cell. Background technique [0002] A fuel cell is an electrochemical energy conversion device that directly converts chemical energy into electrical energy. In principle, fuel cells are not limited by the Carnot cycle, and compared with traditional heat engines, they have high energy conversion efficiency (up to 50% to 60%) and environmental friendliness (that is, very low NO x , SO 2 and noise emission) and other advantages. Long before the advent of the internal combustion engine (1842), William Grove in England demonstrated the world's first dilute sulfuric acid electrolyte, H 2 , O 2 An electrochemical power conversion device for fuel. However, until the 1950s, due to the backwardness of the kinetic theory of the electrode process and the advent and rapid development of the internal combustion engine, a relatively simple energy conversion device, in the late 19th century, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M8/10H01M8/02H01M4/88
CPCY02E60/522Y02E60/50Y02P70/50
Inventor 王蔚国薛业建李华民
Owner NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com