Niobium niobium antimony sodiate potassium leadless piezoelectric ceramic composition

A ceramic composition, lead-free piezoelectric technology, applied in piezoelectric/electrostrictive/magnetostrictive devices, circuits, electrical components, etc., to achieve low sintering temperature, excellent piezoelectric performance, and stable preparation process

Inactive Publication Date: 2009-03-04
THE HONG KONG POLYTECHNIC UNIV
View PDF0 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional ceramic technology cannot produce dense and high-performance Na 1-x K x NbO 3

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Niobium niobium antimony sodiate potassium leadless piezoelectric ceramic composition
  • Niobium niobium antimony sodiate potassium leadless piezoelectric ceramic composition
  • Niobium niobium antimony sodiate potassium leadless piezoelectric ceramic composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Recipe: (Na 0.5 K 0.5 )(Nb 0.99 Sb 0.01 )O 3 (99.5mol%)+MnO 2 (0.5mol%)

[0028] performance:

[0029] d 33 (pC / N)ε 33 / ε 0 k p (%)k t (%)T c (℃)

[0030] 114 325 46.2 48.8 406

Embodiment 2

[0032] Recipe: (Na 0.5 K 0.5 )(Nb 0.97 Sb 0.03 )O 3 (99.5mol%)+MnO 2 (0.5mol%)

[0033] performance:

[0034] d 33 (pC / N)ε 33 / ε 0 k p (%)k t (%)T c (℃)

[0035] 128 409 46.3 48.7 385

Embodiment 3

[0037] Recipe: (Na 0.5 K 0.5 )(Nb 0.94 Sb 0.06 )O 3 (99.5mol%)+MnO 2 (0.5mol%)

[0038] performance:

[0039] d 33 (pC / N)ε 33 / ε 0 k p (%)k t (%)T c (℃)

[0040] 176 665 50.8 51.5 316

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides lead-free sodium potassium niobate antimonate piezoelectric ceramic composition. The composition is lead-free piezoelectric ceramic solid solution formed by introducing high electronegativity Sb part into the B position of alkali metal niobate ferroelectrics (Na1-xKx) NbO3 with ABO3 type perofskite structure to replace Nb. The lead-free piezoelectric ceramic composition has the advantages that the piezoelectric performance is excellent, the Curie temperature is high, the thermostability of the piezoelectric performance is good, the preparation technique is stable, the composition is obtained by adopting tradition piezoelectric ceramics, the sintering temperature is low, and the compactness is good.

Description

technical field [0001] The invention relates to a piezoelectric ceramic composition, in particular to a novel multi-element niobate lead-free piezoelectric ceramic composition. Background technique [0002] Since the mid-1940s, the piezoelectricity of barium titanate ceramics was discovered, especially lead zirconate titanate Pb(Ti, Zr)O with excellent piezoelectric properties and high Curie temperature 3 After the successful development of ceramics, the structural feature is ABO 3 The research and development of lead-based perovskite piezoelectric ceramics is very active. Piezoelectric ceramics and piezoelectric ceramic devices have been widely used in industry, especially in the field of information industry. With Pb(Ti, Zr)O 3 Lead-based binary systems represented by lead zirconate titanate (Pb(Ti, Zr)O 3 ) as the base, add the third component [such as lead magnesium niobate (Pb (Mg 1 / 3 Nb 2 / 3 )O 3 ) as the representative] lead-based ternary piezoelectric ceramic ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/495H01L41/187
Inventor 郭建荣赁敦敏陈王丽华
Owner THE HONG KONG POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com