Method for preparing water-soluble hot-melt adhesive glue

A water-soluble hot-melt adhesive and glue technology, which is applied in the direction of adhesives, adhesive additives, polymer adhesive additives, etc., can solve the problems of not being a production worker, and achieve the effect of low cost and simple process

Inactive Publication Date: 2008-09-17
上海爱世博有机硅材料有限公司
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of glue that can be produced and formulated in China is made of toluene as a solvent, heated to dissolve EVA hot-melt resin, and then compounded with petroleum resin, microcrystalline wax, terpene resin, rosin, etc., because there is a large amount of toluene, so Non-green and environmentally friendly glue is not welcomed by production workers, nor is it accepted by foreign merchants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0011] Example 1: In a batching tank with a capacity of 300 liters, add 48 kilograms of silicon micropowder, 100 kilograms of distilled water, and add 10 grams of antifungal agent, 100 grams of defoamer, 750 grams of sulfuric acid sulfonated butyl oleate ammonium salt, 600 grams of cetyl alcohol ethylene oxide condensate, 500 grams of hydroxyethyl cellulose, start the stirring motor, after stirring for half an hour to 1 hour, add 80 kilograms of EVA emulsion with a solid content of 50% and high ethylene content, Then add 20 kg of EVA emulsion with 50% solid content and low ethylene content, stir evenly, then add 10 kg of acrylic acid copolymer emulsion with 30% content, continue stirring, add terpene phenolic emulsion with 50% solid content 16 kg, plus 20 kg of rosin emulsion with a solid content of 50%, after stirring evenly, adjust the pH to neutral or slightly alkaline with ammonia. Discharge after stirring evenly.

example 2

[0012] Example 2. In a batching tank with a capacity of 300 liters, add 100 kilograms of distilled water, 500 grams of sodium lauryl sulfate, 750 grams of nonylphenol ethylene oxide condensate, and then add 50 grams of antifungal agent and defoamer 500 grams, start the stirring motor, add 24 kg of silicon micropowder, then add 24 kg of calcium carbonate powder, stir for half an hour to 1 hour, add 60 kg of EVA emulsion with a solid content of 50% and high ethylene content, and then add Measure 40 kilograms of EVA emulsions with low ethylene content of 50%, after stirring evenly, then add 10 kilograms of solid content 30% acrylic acid copolymer emulsions, continue under stirring, add solid content and be 16 kilograms of terpene phenolic emulsions of 50%, Add 20 kilograms of rosin emulsion with a solid content of 50%, after stirring evenly, adjust the pH to neutral or slightly alkaline with ammonia water, and then discharge.

example 3

[0013] Example 3. In the batching tank of 300 liters, add 100 kilograms of distilled water, ethylhexyl succinate sodium sulfate 250 grams, trimer, potassium phosphate 600 grams, alkali-soluble acrylic acid copolymer emulsion (40%) 250 grams, Then add 20 grams of antifungal agent and 200 grams of defoamer, start the stirring motor, add 12 kg of silicon micropowder, 12 kg of calcium carbonate powder, 12 kg of quartz powder, and 12 kg of talc powder, then stir for half an hour to 1 hour, then add Containing 70 kilograms of high ethylene content EVA emulsion with solid content of 50%, add 30 kilograms of EVA emulsion with low ethylene content containing 50% solid content again, after stirring evenly, then add 15 kilograms of acrylic acid copolymerization emulsion with solid content 30%, add Solid content is 31 kilograms of the rosin emulsion of 50%, after stirring, adjust pH to neutrality or slightly alkaline with ammoniacal liquor.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of the high milecular polymerization emulsion type glue water, in particular to a method for preparing water-soluble hot melt adhesive glue water, The method for preparing the water-soluble hot melt adhesive glue water is characterized in that filling materials and water with calculated amount are added into a blending pan; a stirring motor is started to perform rapid stirring; auxiliary agents are added into the blending pan, such as an anti-foaming agent, an anti-mildew agent, an emulsifying agent, a dispersing agent, etc.; after being stirred for a period of time, the stirring speed is slowed down, EVA emulsion is added; then an anchoring agent is added; and the water-soluble hot melt adhesive glue water is prepared through even stirring. Compared with the prior art, the method has the advantages of simple process and low cost, and the study keeps the development direction of the domestic international high milecular polymerization on track, is market oriented, fills the gap in our country, meets the urgent requirements of the market, can conform to the requirement of the production process in the industrialization, can produce novel hot melt adhesive glue water which is free of environmental pollution, three-waste pollution and aquosity, does not contain organic solvent, is nontoxic and non-explosive and has no danger for combustion, therefore, the study is worthy of popularization and application.

Description

[technical field] [0001] The invention relates to the field of technical macromolecular polymerization emulsion type glue, and specifically provides a preparation method of water-soluble hot-melt glue. [Background technique] [0002] With the rapid development of my country's medical equipment and food industry, there is a great need for an emulsion-type heat-sealing glue that takes ethylene-vinyl acetate copolymer resin as the base material for further processing. Disposable medical supplies such as syringes, infusion sets, medical gauze, sterile cotton, etc. must be strictly sterilized and packaged before reaching the hands of medical workers. One side of this packaging material is a transparent plastic film or composite film, and the other side is paper printed with explanatory text such as product name, specification and brand. This kind of paper is easy to tear by hand. [0003] The plastic film is usually a PVC or PE composite film. To bond the paper to the PE composi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/08C09J11/08C09J9/00
Inventor 陈俊钦章基凯
Owner 上海爱世博有机硅材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com