Gas-phase anti-corrosion paint

A gas-phase anti-rust, gas-phase anti-rust agent technology, used in anti-corrosion coatings, polyester coatings, coatings, etc., can solve the problem of slow drying, low hardness, water resistance, acid and alkali resistance and chemical corrosion resistance of metal anti-rust coatings Poor and other problems, to achieve the effect of superior anti-corrosion performance, high hardness and strong self-healing

Inactive Publication Date: 2008-08-20
DALIAN YATAI SCI & TECH NEW MATERIAL
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] In order to solve the shortcomings of metal anti-rust coatings such as slow drying, low hardness, water resistance, acid and alkali resistance, and poor chemical corrosion performance, the present invention is mainly developed for various steel pipes, castings, especially petroleum steel pipes or petroleum casings. Vapor phase anti-rust coating with fast surface drying speed, long anti-rust time, high hardness, high gloss and good weather resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The vapor phase antirust coating in this experiment has the following composition:

[0039] Acrylic modified alkyd resin 15

[0040] 2402 phenolic resin 10

[0041] Barium petroleum sulfonate 4

[0042] imidazoline dodecenyl succinate 3

[0043] Tributylamine octanoate 4

[0044] Monoethanolamine Benzoate 5

[0045] Drier 0.5

[0046] Dibutyl phthalate 3

[0047] Xylene / 200 # Solvent (1:1) balance

[0048] The acrylic acid modified alkyd resin used in this experiment was purchased from Jiangsu Sanmu Group Company.

[0049] First add 2402 phenolic resin to the mixed solvent, heat to 50°C to dissolve, and then add imidazoline dodecenyl succinate, tributylamine octanoate, monoethanolamine benzoate, and barium petroleum sulfonate in sequence , acrylic modified alkyd resin, dibutyl phthalate, drier, etc. Stir for 2 hours to dissolve evenly. Discharge, put into the storage tank, let stand. barreled. The vapor phase antirust coating shown in this embodiment 1, its...

Embodiment 2

[0051] A kind of vapor phase antirust coating of this experiment, its composition is as follows:

[0052] Acrylic modified alkyd resin 10

[0053] 2402 phenolic resin 15

[0054] Barium petroleum sulfonate 4

[0055] imidazoline dodecenylsuccinate 2

[0056] Dicyclohexylamine octanoate 2.4

[0057] Monoethanolamine Benzoate 4

[0058] Drier 0.4

[0059] Dibutyl phthalate 3

[0060] Thixotropic agent 1.2

[0061] black paste 10

[0062] Xylene / 200 # Solvent (1:1) balance

[0063] The acrylic acid modified alkyd resin used in this experiment was purchased from Jiangsu Sanmu Group Company.

[0064] First add 2402 phenolic resin to the mixed solvent, heat to 50°C to dissolve, and then add imidazoline dodecenyl succinate, tributylamine octanoate, monoethanolamine benzoate, and barium petroleum sulfonate in sequence , acrylic modified alkyd resin, dibutyl phthalate, black pulp, and finally add drier. Stir at high speed for 2 hours to dissolve evenly. Discharge, put into t...

Embodiment 3

[0066] The vapor phase anti-rust coating in this experiment has the following composition:

[0067] Acrylic modified alkyd resin 10

[0068] 2402 phenolic resin 15

[0069] Barium petroleum sulfonate 4

[0070] Oxidized Petroleum Magnesium Soap 12

[0071] Morpholine sebacate 4

[0072] Monoethanolamine Benzoate 4

[0073] Drier 0.5

[0074] Dibutyl phthalate 3

[0075] Thixotropic agent 1.2

[0076] black paste 10

[0077] Xylene / 200 # Solvent (1:1) balance

[0078] First add 2402 phenolic resin and oxidized petroleum grease magnesium soap into the mixed solvent, heat to about 50°C to dissolve completely, and then add barium petroleum sulfonate, morpholine sebacate, monoethanolamine benzoate, Acrylic modified alkyd resin, dibutyl phthalate, black pulp and thixotropic agent, etc., and finally add drier. Use a high-speed stirring disperser, stir for 2 hours to dissolve evenly, discharge the material, put it into a storage tank, and let it stand. barreled. The gas-p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a gas phase antirust coating, the components of the combination account according to parts by weight, and the scope is as follows: 8 to 25 parts of acrylate modified alkyd resin, 5 to 20 parts of 2402 phenolic resin, 0 to 15 parts of petroleum sulfonate barium, 0 to 25 parts of oxidized malthenes magnesium soap, 0 to 5 parts of dodecatylene base succinic acid imidazoline, 0 to 6 parts of sebacic acid morpholine, 0 to 6 parts of octanoic acid two cyclohexylamines, 0 to 6 parts of octanoic acid tributyl amine, 0 to 6 parts of capric acid tributyl amine, 0 to 15 parts of benzoic acid monoethanolamine, 0.1 to 1.0 part of drier, 0 to 5 parts of thixotropic agent, 1 to 5 parts of dibutyl phthalate, 0 to 5 parts of black paste, and the rest of xylene / 200 model solvent (1:1). The gas phase antirust coating of the invention has the advantages of fast table-drying speed, long antirust time, high rigidity, high brightness, good temperature resistance, etc., and can satisfy the requirements of the automatic pipeline production and long time open storage antirust need of oil steel pipes and other large pipes or profiles.

Description

technical field [0001] The invention belongs to the coating field of fine chemical industry, especially a novel anticorrosion coating in metal anticorrosion technology. Background technique [0002] Corrosion of metal is a phenomenon in which metal is destroyed by chemical or electrochemical action of environmental medium. The corrosion of metals spreads all over the national economy and brings huge losses to the national economy. In developed countries, corroded and rusted steel accounts for about 20% of the output every year, and about 30% of the equipment is scrapped due to corrosion. In China, the economic loss caused by metal corrosion is as high as 30 billion yuan per year, accounting for 4% of the gross national product. [0003] For a long time, people have used a variety of techniques to protect metals from corrosion. Among them, coating anti-rust coatings on metal surfaces is one of the most effective and commonly used methods for metal equipment anti-corrosion....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D167/06C09D5/08C23F11/02C09D161/06
Inventor 王美君张历男
Owner DALIAN YATAI SCI & TECH NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products