80 kilogram grade low welding crack sensibility high-strength steel plate special-purpose welding wire

A technology of low welding crack, high strength steel plate, applied in welding medium, welding equipment, welding/cutting medium/material, etc., can solve the problem of increasing the production cost of welding wire, high Pcm value, high low carbon equivalent, inability to achieve welding, and poor performance of steel plate. Excellent performance and other problems, to achieve the effect of preventing cold cracking, grain refinement, and improving strength and toughness

Inactive Publication Date: 2008-04-09
金秋生
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The high-strength steel plate with low welding crack sensitivity welded by this substitute welding wire, because the content of alloy elements in the weld is too high, resulting in too high Pcm value and low carbon equivalent, it cannot be welded without preheating or low preheating. The steel plate does not reflect its unique excellent performance, and thus greatly increases the production cost of the welding wire
At present, there is no special welding wire specially used for welding high-strength steel with low welding crack sensitivity in the environment between minus 20°C and minus 50°C, which is economical and has good welding performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The steel with both S and P less than 0.10% by weight is selected for smelting the welding wire steel, and there is no special requirement for the smelting process. In the process of smelting, the following elements by weight are added: C: 0.10, Si: 0.8, Mn: 1.80, Ti: 0.10, B: 0.001, Ni: 0.40, Cr: 1.0, V: 0.09, and the balance is iron and other elements. Avoid impurities whose content is not more than 0.01% of the iron content.

Embodiment 2

[0018] The steel with both S and P less than 0.025% by weight is selected for smelting welding wire steel, and there is no special requirement for the smelting process. In the process of smelting, the following elements by weight are added: C: 0.06, Si: 1.0, Mn: 1.40, Ti: 0.02, B: 0.008, Ni: 0.60, Cr: 0.05, V: 0.05, and the balance is iron and other elements. Avoid impurities whose content is not more than 0.40% of the iron content. After being drawn into welding wire, the welding wire is copper-plated, and the amount of copper plating is 0.5% of the iron content in the welding wire.

Embodiment 3

[0020] The steel with both S and P less than 0.015% by weight is selected for smelting welding wire steel, and there is no special requirement for the smelting process. During the smelting process, the following elements by weight percentage are added: C: 0.12, Si: 0.4, Mn: 2.10, Ti: 0.15, B: 0.010, Ni: 0.20, Cr: 0.50, V: 0.01, and the balance is iron and other elements. Avoid impurities whose content is not more than 0.10% of the iron content. After being drawn into welding wire, the welding wire is copper-plated, and the amount of copper plating is 0.3 percent of the iron content in the welding wire.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the welding wire technical field, and discloses a special welding wire for 80 Kg level steel plate with low welding crack sensibility and high strength. The invention has the technical proposal that the welding wire includes the elements in the following weight percentage: 0.06 to 0.12 percent of carbon, 0.40 to 1.00 percent of silicon, 1.40 to 2.10 percent of manganese, 0.02 to 0.20 percent of titanium, 0.001 to 0.01 percent of boron, 0.05 to 1.50 percent of nickel, 0.05 to 1.20 percent of chromium, niobium b lower than or equal to 0.10 percent, vanadium lower than or equal to 0.10 percent, sulfur lower than or equal to 0.10 percent, phosphorus lower than or equal to 0.10 percent, the rest comprises iron and other unavoidable foreign matters. Through the experiment, the ambient temperature of the welding joint for welding crack sensibility and high strength steel plate is subzero 20 DEG C to 50 DEG C by utilizing the welding wire without preheat, and the occurrence of cold cracks can be prevented.

Description

technical field [0001] The invention belongs to the technical field of welding wires, and in particular relates to a special welding wire for high-strength steel plates with low welding crack sensitivity of 80 kilograms. Background technique [0002] High-strength steel plate with low welding crack sensitivity is a steel plate that can weld without cracks without preheating or low preheating. The main characteristics of this type of steel plate are low Pcm value, low carbon equivalent, excellent welding It has the characteristics of low C content, high purity, high strength and high toughness. Because this kind of steel is a new type of steel, there is no special welding wire specially used for this steel welding so far, and there is no special welding wire used for welding at lower temperatures. When welding this type of steel, ordinary high-strength welding wire is often used as a substitute. In order to improve the weld strength, high-strength welding wire (such as ER76...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23K35/30
Inventor 金秋生
Owner 金秋生
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products