Method of welding dissimilar steel 10Cr9Mo1VNb and 1Cr18Ni9

A 1cr18ni9, welding method technology, applied in the field of special steel pipe welding, can solve the problems of difficult welding, brittle cold cracks of welded joints, and decreased impact toughness of welds, etc.

Inactive Publication Date: 2007-08-08
WORKER WELDING & CUTTING TECHN ASSOC OF HEBEI
View PDF0 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The welding of T91 steel is relatively difficult, which is mainly manifested in the problems of oxidation on the back of the weld, embrittlement of welded joints, cold cracks, and low impact toughness. The main reason is that during the welding process, the welding line energy is large and the interlayer temperature is high. As a result, the interlayer structure is overheated, resulting in Widmanstatten structure, large grains and network grain boundaries. These structures are prone to crack sources, forming cracks and expanding, resulting in a decrease in the impact toughness of the weld

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method of welding dissimilar steel 10Cr9Mo1VNb and 1Cr18Ni9

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0014] 1. Welding method

[0015] The welding method adopts the combination of manual argon tungsten arc welding and the welding method of workpiece rotation with the installation of a welding positioner. The displacement pulse argon tungsten arc welding process has a beautiful appearance and is used for mass production; Dissimilar steel with flexible handling for narrow construction sites.

[0016] 2. Selection of welding process parameters

[0017] 2.1 preheating,

[0018] According to the data, the characteristics of the two steels are analyzed as follows:

[0019] ① 10Cr9Mo1VNb steel (T91) belongs to the air-cooled martensitic structure and is sensitive to cold cracks;

[0020] ②Due to reasons such as steel materials, welding materials, and manual welding processes, hydrogen may remain in the weld in a supersaturated state during martensitic transformation, making the area embrittled;

[0021] ③The phase transformation after welding, coupled with the structural restrai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for the welding of steels like 10Cr9Mo1VNb and 1Cr18Ni9, which controls the temperature between 150-200deg.C before welding at the layer. With the back welding current being 115A / 85A(peak / base), welding speed 2-3cm / min, thickness no less than 3mm, filling welding current 150A / 20A (peak / base), welding speed 2-3cm / min, width of the welding channel being 2-3 times of the solder wire. It has smaller welding depth, reasonable control of the fuse ratio and chemical effusion.

Description

technical field [0001] The invention relates to a welding method of dissimilar steel 10Cr9Mo1VNb and 1Cr18Ni9, belonging to the technical field of special steel pipe welding. Background technique [0002] Dissimilar steel 10Cr9Mo1VNb (T91 steel) is a new type of high-alloy heat-resistant steel, which is widely used for its high-temperature durable strength and excellent creep fracture resistance. Compared with austenitic steel, it has a small expansion coefficient and improves heat conduction The price is also relatively cheap; whether it is in terms of performance or economy, it has shown its superiority. It is the first choice and alternative steel grade for high-temperature and high-pressure pipelines such as high-temperature superheater headers and main steam pipelines. The welding of T91 steel is relatively difficult, which is mainly manifested in the problems of oxidation on the back of the weld, embrittlement of welded joints, cold cracks, and low impact toughness. Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K9/16B23K9/095B23K35/02B23K35/24B23K9/235B23K33/00B23K103/18
Inventor 王宝才王志伟王迎军焦荣格孙芳何生贵杨全义
Owner WORKER WELDING & CUTTING TECHN ASSOC OF HEBEI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com