Polymer cement based self-levelling materials and preparation method thereof

A self-leveling, cement-based technology, applied in the field of building materials, can solve the problems of high cost, inconvenient use and transportation, etc., and achieve the effect of convenient transportation, high bonding strength and good deformation ability

Inactive Publication Date: 2007-11-14
SHANGHAI JIANWEI CULTURAL HERITAGE CONSERVATION TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Aiming at the shortcomings of cement-based self-leveling materials, people have introduced a two-component polymer emulsion cement-based self-leveling material, which has the advantages of good fluidity, fast setting speed, and good elasticity, but the cost is high, and it is difficult to use and transport. not very convenient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Portland cement 100

[0035] Polymer latex powder 10

[0036] High alumina cement 15

[0037] Shuangfei powder mineral admixture 5

[0038] Superplasticizer 2.5

[0039] Defoamer 0.3

[0040] 0.1mm-1.25mm quartz sand 100

[0041] The ground self-flowing material composed of this formula has high fluidity, moderate setting time, and high strength. It is suitable for leveling new ground, leveling the base of secondary ground, and repairing old ground, sandy ground and unqualified ground.

Embodiment 2

[0043] Portland cement 100

[0044] Polymer latex powder 10

[0045] High alumina cement 15

[0046] Fly Ash Mineral Admixture 5

[0047] Superplasticizer 2.0

[0048] Defoamer 0.3

[0049] 0.1mm-1.25mm quartz sand 100

[0050] The ground self-leveling material composed of this formula has high fluidity, moderate setting time and high strength. It is suitable for leveling new ground, self-levelling of the final layer of the ground, and repairing old ground, sandy ground and unqualified ground.

Embodiment 3

[0052] Portland cement 100

[0053] Polymer latex powder 15

[0054] High alumina cement 8

[0055] Shuangfei powder mineral admixture 5

[0056] Superplasticizer 2.5

[0057] Defoamer 0.5

[0058] 0.1mm-1.25mm quartz sand 100

[0059] The ground self-flowing material composed of this formula has high fluidity, moderate setting time, high bonding strength, high elasticity and good wear resistance, and is suitable for ground leveling with special requirements.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a polymeric cement gravity flow leveling material prepared from silicate cement, polymer emulsion powder, high-alumina cement, mineral blending materials, high efficiency water reducing agent, defoaming agent, and quartz sand and with right weight ratio through finite process, material possesses good mobility, stability, high early stage folding and compression resistant strength, thus can be widely applied in ground surface leveling and mending of old ground surface, sand streak ground surface and ground surface with less qualified construction.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a ground self-leveling material. Background technique [0002] With the development of modern industrial technology and production, the requirements for cleaner production are getting higher and higher, requiring the workshop floor to be corrosion-resistant, clean, wear-resistant and smooth. In addition, during the construction of the building ground, problems such as uneven ground, sand, pockmarked surface, and damage often occur due to various reasons. In response to the development and requirements of ground engineering, a ground self-leveling material has been widely used. The self-leveling material is mixed with water to form a highly fluid and stable slurry, which can be self-leveled when poured on the ground. After hardening, a smooth and flat ground can be obtained. . It can effectively replace the traditional ground method, and can be used to rep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/06C04B28/04C04B18/08C04B24/16C04B103/30
CPCC04B2111/62C04B2111/72C04B28/06C04B7/02C04B14/06C04B24/24C04B2103/302C04B2103/50
Inventor 蒋正武孙振平
Owner SHANGHAI JIANWEI CULTURAL HERITAGE CONSERVATION TECH CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com