Prepn of C5 hydrogenated petroleum resin

A technology of hydrogenated petroleum resin and hydrogenation catalyst, which is applied in the field of preparation of C5 hydrogenated petroleum resin, can solve the problems of high hue and low bromine price, and achieve the effect of high hue and reduced unsaturated bond content

Active Publication Date: 2007-01-03
BC P INC CHINA NAT PETROLEUM CORP +1
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Overcome the long-standing problem of low bromine price and high hue in actual production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0013] The hydrogenation catalyst is firstly prepared by spraying method. The weight of the catalyst carrier alumina is 100 parts, 0.8 part of palladium, 0.2 part of transition metal copper, 0.5 part of rare earth metal cerium, and 1 part of the fourth main group element tin. Carry out the preparation of carrier first, soak and calcinate the alumina ball in cerium chloride to obtain the catalyst carrier treated with rare earth; after spraying active components such as palladium, cerium, tin on the carrier, obtain the hydrogenation catalyst carrier of the present invention through activation catalyst.

[0014] The C5 distillate by-product of ethylene cracking is used as raw material, after raw material pretreatment, polymerization, neutralization and water washing under the action of aluminum trichloride catalyst, the crude C5 petroleum resin is placed in a reactor equipped with a hydrogenation catalyst, After removing impurities such as dechlorination at 280°C, carry out hydr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The preparation process of C5 hydrogenated petroleum resin with the C5 fraction as the side product of cracking ethylene includes the steps of: pre-treating material, neutralizing, water washing, eliminating chlorine ion impurity from crude resin product at 200-300 deg.c under the action of modified alumina as catalyst, and hydrogenation at 150-350 deg.c and 6.0-20.0 MPa in the presence of hydrogenation catalyst. The hydrogenation catalyst is prepared through spraying process and consists of catalyst carrier alumina 100 weight portions, Pd 0.2-1.2 weight portions, transition metal 0.06-0.48 weight portion, RE metal 0.001-0.05 weight portion and IV element 0.06-2.4 weight portions. The present invention is used in producing C5 hydrogenated petroleum resin with the material possessing relatively high cyclopentadiene and arene content.

Description

Technical field [0001] The present invention relates to the preparation method of mixed carbon five hydrogenated petroleum resin, especially relates to the preparation of carbon five by-products of piperylene, isoprene, cyclopentadiene, pentene and other mixed carbon five fractions as raw materials The preparation method of hydrogenated petroleum resin. Background technique [0002] C5 petroleum resin is a low-molecular-weight thermoplastic resin, which is polymerized by the by-product C5 fraction of ethylene plant under the action of aluminum trichloride and other catalysts. The average molecular weight is between 1000 and 3000. Resin has good compatibility, mixed with other substances, has good water resistance, acid resistance, low melting point, and good adhesion. Petroleum resin is mainly used as adhesives, road marking paints, rubber additives, coatings and inks. C5 petroleum resin generally has defects such as dark hue, bad smell, low thermal stability and oxidation ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F240/00C08F8/04
Inventor 曹耀强许翠红王福善潘广勤邓廷昌李亮毛兵
Owner BC P INC CHINA NAT PETROLEUM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com