Leadless ohmic electrode silver coating for PTC ceramic and its preparation method

A technology of silver paste and ceramics, which is applied in the manufacture of resistors, conductive materials dispersed in non-conductive inorganic materials, circuits, etc., can solve environmental pollution and other problems, and achieve strong process adaptability, wide firing temperature range, and aging resistance The effect of superior performance

Inactive Publication Date: 2006-11-29
HEFEI SHENGDA ELECTRONIC TECH IND CO LTD
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, this slurry will cause greater pollution to the environment during its manufacture and use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0038] One, the organic carrier in the lead-free ohmic electrode silver paste for PTC ceramics, it is made up of ethyl cellulose, rosin, castor oil, terpineol, and its weight percentage is

[0039] Ethylcellulose 7%

[0040] Rosin 2%

[0041] Castor Oil 2%

[0042] Terpineol 89%

[0043] Mix the components well, and heat at 100°C to fully dissolve the ethyl cellulose and rosin.

[0044] 2. Lead-free ohmic electrode silver paste for PTC ceramics, which is composed of silver micropowder, nickel powder or zinc powder or aluminum powder or any mixture thereof, organic carrier, and its weight percentage is

[0045] Silver micropowder 42%

[0046] Nickel powder (or zinc powder or aluminum powder or any mixture of zinc powder, nickel powder, aluminum powder) 28%

[0047] Organic Vehicle 30%

[0048] Spherical silver powder with a particle size of less than 1 μm is selected for the silver micropowder; spherical powder with a particle size of 500-1200 mesh and a lead and calcium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A method for preparing silver size pole of lead free ohm electrode used on PTC ceramic includes mixing and grinding silver micro powder, zinc powder and organic carrier together to obtain silver size pole material then firing obtained material at temperature of 480-580deg.c to let electrode layer attached on surface of ceramic body tightly for forming excellent ohm contact property.

Description

technical field [0001] The invention relates to lead-free ohmic electrode silver paste for PTC ceramics. Background technique [0002] Since PTC (Positive Temperature Coefficient Thermistor) ceramics is a semiconductor ceramic material, an ohmic electrode layer must be formed on its surface during the manufacturing process to eliminate the surface barrier of PTC ceramics so that the electrode layer and the ceramic body Form a good ohmic contact, and its various electrical properties can be reflected. A layer of silver electrode layer is made on the ohmic electrode layer so that it can be brazed with leads or pins. [0003] PTC ohmic electrode silver paste is usually formulated and processed from silver powder, zinc powder, glass powder, organic carrier and other raw materials. Silver micropowder and zinc powder are the main components of the slurry, which play the role of conducting electricity and eliminating surface barriers in the electrode. The glass powder is melted d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01B1/20H01B1/22C08L1/02H01C7/02H01C17/00
Inventor 雷跃文
Owner HEFEI SHENGDA ELECTRONIC TECH IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com