Tech. for spraying corrosion resistant coating on dry screw compressor rotor

A dry screw compressor, spraying anti-corrosion coating technology, applied in mechanical equipment, machines/engines, rotary piston pumps, etc., can solve the problems of uneven thickness, weak adhesion, poor coating quality, etc., to achieve meshing Reasonable gap, excellent adhesion, uniform thickness

Inactive Publication Date: 2006-06-14
WUXI COMPRESSOR CO LTD
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After using this kind of coating, the quality of the coating is poor, the adhesion is not strong, the thickness is uneven, and the color and luster and water corrosion resistance are sometimes not stable enough, which is easy to affect the service life of the coating.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tech. for spraying corrosion resistant coating on dry screw compressor rotor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] 1. The material of the rotor body is forged steel 35#, and the pretreatment is carried out first:

[0035] The first condition for the coating not to be damaged is to pre-treat the base material to be sprayed.

[0036] (1) Cut the rotor matrix material into the required rotor blank when calculating the profile of the rotor tool. The spiral surface of the rotor blank should be given a coating value, and the coating value is: 0.02mm;

[0037] (2) After the rotor blank is processed, the test run is carried out, and the feasible meshing clearance of the rotor profile is tested; 0.28mm;

[0038] (3) The rotor blank is forged from the blank, and after rough machining, it must be treated with stress relief annealing, so as to avoid peeling off of the coating due to stress release due to temperature rise during sintering.

[0039] 2. Stress relief annealing heat treatment of rotor blank:

[0040] (1) Put the rotor blank into the furnace below 220°C;

[0041] (2) Afterwards, ...

Embodiment 2

[0059] 1. Pretreatment of the rotor matrix material:

[0060] The coating value is: 0.03mm; the meshing gap of the rotor profile is; 0.3mm;

[0061] 2. Stress relief annealing heat treatment of rotor blank:

[0062] (1) Put the rotor blank into the furnace below 220°C;

[0063] (2) Afterwards, heat up to 600°C at a rate below 80°C / hour;

[0064] (3), when the temperature is: 580 ℃, heat preservation for 3 hours;

[0065] (4) Cool in the furnace to below 300°C;

[0066] (5) When the temperature in the furnace reaches below 300°C, take out the rotor blank from the furnace;

[0067] (6), then placed in the atmosphere to cool.

[0068] 3. Pre-treatment of spraying anti-corrosion layer:

[0069] (1) The surface of the rotor blank to be sprayed is cleaned with acetone or trichlorethylene;

[0070] (2) Sinter in an electric furnace after cleaning, and sinter at a temperature of 300°C for 3 hours;

[0071] (3) After sintering and cooling, the rotor blank is subjected to sandblas...

Embodiment 3

[0081] Using the process steps and process conditions in Embodiment 1 and Embodiment 2, the rotor coated with an anti-corrosion layer can also obtain the above effects. The thickness of the rotor spiral surface coating is 0.03mm, and it only needs to be sprayed once to reach the desired thickness, and then dried; the thickness of the rotor spiral end surface coating is 0.06mm, and the thickness of the outer circle coating of the rotor shaft seal is: 0.06mm (thickness above 0.03mm); therefore, when using a spray gun to spray on the rotor helical end face and the outer circle of the rotor shaft seal, it must be sprayed more than two times, and a pre-drying treatment should be carried out every time it is sprayed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

An anticorrosive coating spraying process for a dry-screw compressor rotor belongs to a technical field of mechanical spraying process, which includes the following steps: first, pretreating the rotor parent material and stress relief annealing heat treating the rotor blank; then pretreating the spray anticorrosive coating and spraying polytetrafluoroethylene coating and at last sintering treating and detecting to be the rotor finished products. The inventive coating thickness is uniform and its colour is black. When the dry-screw compressor is in a normal state, the service life of the coating can reach more than 24000 hours.

Description

technical field [0001] The invention relates to a technique for spraying an anticorrosion layer on a rotor of a dry screw compressor, in particular to spraying a polytetrafluoroethylene anticorrosion layer on the outer surface of the rotor of a dry screw compressor, and belongs to the technical field of mechanical spraying techniques. Background technique [0002] The corrosion resistance of the air passage of the dry screw compressor and the purity of the gas are the key issues to obtain oil-free and clean compressed air in the dry screw compressor. Since the rotor is a moving part, its rotating speed is high, the spiral profile is complex, and the tolerance range is small. It is not easy to choose a suitable formula and a coating with qualified adhesion. If there is no correct rotor profile and practicable Engage the gap and the coating peels off easily. [0003] Before the present invention was made, in the prior art, the outer surface of the dry screw compressor rotor h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F04C18/16
Inventor 周嵩荃
Owner WUXI COMPRESSOR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com