Cold-resistant self-sticking emulsion product, and its production method and use

A self-adhesive, latex technology, applied in adhesive types, ester copolymer adhesives, etc., can solve problems such as insufficient adhesion, unsafe cost of oil-based adhesives, poor water resistance, etc.

Inactive Publication Date: 2005-05-04
TAIBO ADDHESIVE MATERIALS SHANGHAI
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is: to overcome the defects in the prior art that the ordinary self-adhesive latex has insufficient adhesion, poor water resistance, easy to become cloudy, and cannot solve the problem of cold resistance, and the use of oily glue is unsafe and costly, and provides Three kinds of water-based self-adhesive latex products with different uses and excellent cold resistance that can completely replace oily glue and their applications, and at the same time provide a kind of water-based self-adhesive latex that can dissolve xylene-modified resins, rosin-modified resins, natural rubber or synthetic rubber with cold-resistant properties. Method for producing cold-resistant self-adhesive latex products by changing its oiliness to water-based and emulsifying and dispersing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cold-resistant self-sticking emulsion product, and its production method and use
  • Cold-resistant self-sticking emulsion product, and its production method and use
  • Cold-resistant self-sticking emulsion product, and its production method and use

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0080] Embodiment 1 Prepare 1# cold-resistant self-adhesive latex as follows:

[0081] (1) First put 400Kg octyl acrylate and 0.5Kg benzoyl peroxide into the stainless steel tank of the fast stirring emulsifying machine to dissolve;

[0082] (2) 10Kg solid content is 100% natural rosin denatured phenolic resin R-100 and puts into the stainless steel tank of the fast stirring emulsifying machine and immerses in dissolving;

[0083] (3) Stir and dissolve the natural rosin denatured phenolic resin with a 3600 R.P.M fast stirring emulsifier, take a sample after about 30 minutes, clamp the test solution with 2 transparent glass test pieces, check whether the solution is completely dissolved, until it is completely dissolved and there are no particles;

[0084] (4) Put 10Kg of reactive emulsifier ELEMINOL JS-2 with a solid content of 40%, and then stir it with a 3600 R.P.M fast mixer for 30 minutes, then take a sample and clamp the test solution with a transparent glass test piece t...

Embodiment 2

[0089] Embodiment 2 Prepare 2# cold-resistant self-adhesive latex as follows:

[0090] (1) First put 500Kg octyl acrylate and 0.75Kg benzoyl peroxide into the stainless steel tank of the fast stirring emulsifying machine to dissolve;

[0091] (2) Put 15Kg of reactive emulsifier LATEMUL S-180 with a solid content of 40%, and then stir it with a 3600 R.P.M fast mixer for 30 minutes, then take a sample and clamp the test solution with a transparent glass test piece to check whether it is completely emulsified Uniformly until there are no particles;

[0092] (3) Put 5Kg of methyl methacrylate, 5Kg of methacrylic acid, 25Kg of acrylic acid and 155Kg of pure water into a stainless steel bucket to mix with the emulsion formed in the previous steps, then stir with a 3600 R.P.M fast stirring emulsifier for 30 minutes and then take a sample for inspection Whether it is uniform, store it in the middle tank after being uniform, and prepare for the dropping point;

[0093] (4) Put 2Kg of...

Embodiment 3

[0096] Embodiment 3 Prepare 3# cold-resistant self-adhesive latex as follows:

[0097] (1) Put 300Kg butyl acrylate into the stainless steel barrel of the fast stirring emulsifying machine to dissolve;

[0098] (2) 30Kg of natural rosin modified phenolic resin Tamanole-102 with a solid content of 50% is put into the stainless steel barrel of a fast stirring emulsifying machine and immersed in it for dissolution;

[0099] (3) Stir and dissolve the natural rosin denatured phenolic resin with a 3600 R.P.M fast stirring emulsifier, take a sample after about 30 minutes, clamp the test solution with 2 transparent glass test pieces, check whether the solution is completely dissolved, until it is completely dissolved and there are no particles;

[0100] (4) Put 8Kg of reactive emulsifier LATEMUL S-180A with a solid content of 40%, and then stir it with a 3600 R.P.M fast mixer for 30 minutes, then take a sample and clamp the test solution with a transparent glass test piece to check wh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to three watercrafts self-viscosity latex product with superior cold tolerance, and its usage. Meanwhile, it offers a manufacturing method of cold tolerance self-viscosity latex product, which can be described as follows: dissolve xylene denatured resin, rosin denatured resin, natural rubber, or synthetic rubber, in order to change its oiliness into watercrafts, and then make it have emulsification and dispersion. One feature of the invention lies in the use of a kind of reactivity emulsifier that can take combined polymerization reaction with monomer; another feature lies in that it acquires the cold tolerance by dissolving xylene denatured resin, rosin denatured resin, natural rubber, or synthetic rubber, in order to change its oiliness into watercrafts, and by making it have emulsification and dispersion. The cold tolerance self-viscosity latex has the advantages such as initial adhesion, high adhesion in winter, fine water resistance, low cost, no evocative fire hazard, more safety, better environmental protection, better guarantee of worker's health, so it can substitute oiliness rubber and solvent form Alec Rubber completely.

Description

technical field [0001] The invention belongs to the field of organic chemical polymer polymerization fine chemical adhesives, and relates to three kinds of water-based self-adhesive latex products with excellent cold resistance and their application and a modified method for producing cold-resistant self-adhesive latex. Background technique [0002] The self-adhesive latex currently produced, due to the use of general emulsifiers, the emulsifier molecules cannot be copolymerized with other monomers in the micelles, so the adhesiveness of the produced latex is limited, and there is emulsification between molecules. The gap between the agent molecules reduces the adhesion, so that the water-based adhesive has lower adhesion than oil-based adhesives, poor water resistance, and easily turns white when it meets water. So far, water-based latex cannot achieve the adhesion properties of oil-based rubber or solvent-based acrylic adhesives. It is not much different in summer and can ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F2/22C08F220/10C09J133/08
Inventor 郭孟垤
Owner TAIBO ADDHESIVE MATERIALS SHANGHAI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap