Silicate base zincoxide ion nano hole composite material and board spectrum bacteria inhibitor and sterilizer

A technology of nanoporous materials and composite materials, applied in the field of silicate-based zinc oxide ion nanoporous composite materials, can solve the problems of high cost of silver-based antibacterial agents, easy oxidation and discoloration, and strong reaction sensitivity of silver ions.

Inactive Publication Date: 2005-01-12
JILIN UNIV
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the antibacterial effect of inorganic silver-based antibacterial agents is outstanding, but due to the strong sensitivity of silver ions to light, it is easy to oxidize and change color, which has become an important problem that limits its application. In addition, the cost of silver-based antibacterial agents is also very high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0106] Method 1: Take 1000g of A-type silicate nanoporous material and 1000g of zinc nitrate, put them into a reaction vessel, stir evenly under dark conditions, then transfer to a muffle furnace and heat at 500°C for 5 hours. After cooling, a white or light gray powder solid type A silicate-based zinc oxide ion nanoporous composite material is obtained.

[0107] Method 2: get A-type silicate nanoporous material 1000g, add in the reaction vessel that fills distilled water, add zinc nitrate under stirring, dark condition, reaction mixture mass ratio is nanoporous material: water: zinc nitrate=1: 20:0.8. Then it was stirred at room temperature for 10 hours. After the reaction was completed, the product was filtered, and the final product was dried in the range of 80°C, and then transferred to a muffle furnace for heating and reacting in the range of 500°C for 5 hours. A type A silicate-based zinc oxide ion nanoporous composite material is also obtained.

[0108] In the above ...

Embodiment 2

[0109] Example 2. Except changing the A-type zeolite molecular sieve to X-type zeolite molecular sieve, the reaction step conditions were the same as in Example 1, and a series of white or light gray powder solid X-type silicate-based zinc oxide ion nanoporous composite materials were obtained. The unit cell is: Zn 43-X / 2 Na X [Al 86 Si 106 o 384 ]0-264ZnO (X=0.1-86).

Embodiment 3

[0110]Example 3. Except changing the A-type zeolite molecular sieve to Y-type zeolite molecular sieve, the reaction step conditions were the same as in Example 1, and a series of white or light gray powder solid Y-type silicate-based zinc oxide ion nanoporous composite materials were obtained. The unit cell is: Zn 28-X / 2 Na X [Al 56 Si 136 o 384 ]0-264ZnO (X=0.1-55).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A broad-spectrum bactericide is prepared from the nano-porous material chosen from the molecular sieves of A, X and Y-type zeolite, mordenite, Si-Al zeolite, etc. and the silicate-base zinc oxide ions as active component. It is suitable for skin tinea fungus, multiple pathogenic funguses, and other 10 bacteria including candida, blue mold, aspergillus, etc.

Description

technical field [0001] The invention belongs to a new application field of silicate-based zinc oxide ion nanoporous composite materials, and specifically relates to a silicate-based zinc oxide prepared from silicate-based nanoporous materials, nano-zinc oxide particles and zinc ions Ionic nanoporous composite material and its application in antibacterial and bactericidal aspects. Background technique [0002] Bacteria and viruses have always accompanied the development of human society, but once they mutate and infect humans, they will greatly affect the normal economic life order and health of humans, such as: Neisseria gonorrhoeae (Neisseria gonorrhoeae), Vibrio cholerae (Vibrio cholerae) ), Mycobacterium tuberculosis, hepatitis B virus (HBV), human immunodeficiency virus (HIV), SARS virus, etc. It has been confirmed that Helicobacter pylori is closely related to the pathogenicity of peptic ulcer and gastric cancer. HIV causes acquired immunodeficiency syndrome (AIDS), wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A01N59/16
Inventor 朱广山裘式纶
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap