A metal surface, shot peening technology, applied in the field of metal surface strengthening, can solve the problems of thin strengthening layer thickness, low strengthening efficiency, and no related reports on shot peening of metal materials, etc. , Improve the effect of shot peening

Inactive Publication Date: 2003-08-27
INST OF METAL RESEARCH - CHINESE ACAD OF SCI
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the shot peening speed of shot peening strengthening at home and abroad is generally 70-100m / s, and the most recently developed shot peening technology in Japan is the 200 m / s strengthening shot peening technology (Tadaji Kagaya, Surface Technology (Day), 2001 , 52(2): 169; (Recent Trends in Shot Peening Technology)) and (Kagaya Tadashi, Kubota Pukan, Special Steel (Japan), 2000, 49(5): 33; ultrafine powder impact processing), Its maximum speed: 150-200 m / s, micro-powder particle size: 40-60 μm, its disadvantages are low strengthening efficiency and thin strengthening layer
[0004] In addition, the supersonic spraying process uses compressed air to obtain supersonic speed through the Lava nozzle, and sprays other metal materials or alloys with different properties from the base metal on the surface of the base to form a coating. However, there are no related reports on the use of supersonic jets to strengthen metal materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal-surface supersonic stress peening method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The base material is 316L stainless steel pipe, and the projectile is Al 2 o 3 (The particle size of the projectile is about 150 microns) Use compressed air to carry the projectile, inject gas through the Lava nozzle to accelerate the projectile to 300-1100m / s, and continuously bombard the surface of the metal material to produce a residual compressive stress layer on the metal surface. The process parameters are as follows:

[0016] The spray distance is 70mm, the gas pressure is 3.0MPa, the gas temperature is room temperature, the gas flow rate is 30g / s, the power consumption is 12kW, the shot feeding voltage is 30V, the shot peening time is 6 minutes, and the average thickness of the surface strengthening layer is 75 microns according to X-ray diffraction analysis. about.

[0017] This embodiment adopts as figure 1 The supersonic spraying device shown is a Russian patent, and the patent numbers are respectively 1674585 (1991), 1603581 (1993), 1618778 (1993), 177307...

Embodiment 2

[0019] The difference from Example 1 is:

[0020] The matrix material is a carbon steel test piece, and the projectile adopts steel shot (about 100 microns), and the process parameters are as follows:

[0021] The spraying distance is 55mm, the gas pressure is 2.5MPa, the gas temperature is room temperature, the gas flow rate is 28g / s, the power consumption is 10kW, the shot feeding voltage is 25V, and the shot peening time is 10 minutes. According to X-ray diffraction analysis, the average thickness of the surface strengthening layer reaches 75 Microns or so.

Embodiment 3

[0023] The difference from Example 1 is:

[0024] The base material is a mold steel test piece, and the projectile uses nylon particles (about 200 microns). The process parameters are as follows:

[0025] The spray distance is 100mm, the gas pressure is 2.2MPa, the gas temperature is room temperature, the gas flow rate is 26g / s, the power consumption is 8kW, the shot feeding voltage is 20V, the shot peening time is 15 minutes, and the average thickness of the surface strengthening layer is 70 microns according to X-ray diffraction analysis. about.

[0026] In addition, the device used in the present invention can also adopt the cold air power spraying device in the Chinese patent application (application number is 01128130.8).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention refers to the intensifying technology of metal surface, especially is metal surface supersonic velocity blasting shot intensifying method, the character is that it uses compressed air to carry metal or nonmetal pills, accelerates the pills to speed of 300-1100 m / s, and the pills strikes the metal surface continuously, forms a remnants tress layer on the surface of the metal, the craft parameters is: the ejecting distance 55-100mm, the pressure of air 2.2-3.0 MPa, the air temperature is room temperature, the flux of air 26-30 g / s, the pills sending voltage 20-30 V, the diameter of pill 50-200 micron.

Description

technical field [0001] The invention relates to metal surface strengthening technology, in particular to a metal surface supersonic shot peening strengthening method. Background technique [0002] It is generally believed that fatigue cracks occur in the tensile stress area of ​​the metal surface, and the existence of residual tensile stress accelerates the initiation and propagation of cracks, which eventually leads to the fracture of the material. On the contrary, the existence of residual compressive stress helps to improve the fatigue life. The wear resistance of the components is enhanced, and at the same time, it can effectively prevent stress corrosion and improve the corrosion fatigue life of the components. [0003] Shot peening can improve the fatigue resistance of metal parts and improve the mechanical properties of metal parts. Metal surface shot peening is very important to improve the fatigue life of metal parts. The formation of a residual compressive stress l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D7/06
Inventor 熊天英李铁藩吴杰金花子吴敏杰
Owner INST OF METAL RESEARCH - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com