Catalyst for producing vinyl acetate
A catalyst, acetic acid technology, applied in the direction of physical/chemical process catalyst, organic compound/hydride/coordination complex catalyst, metal/metal oxide/metal hydroxide catalyst, etc. Bulk void fraction, high space-time yield, reduced pressure drop loss
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment Construction
[0022] The present invention will be further described below by some embodiments, in the embodiments: [Examples 1-6] carrier preparation:
[0023] Add extrusion aids and binders to the silica gel powder, mix well, and form the carrier precursor by extrusion. Dry the carrier at room temperature for 48 hours, then dry it at 100°C for 24 hours, and place it in a muffle furnace for 730 °C for 2 hours. After cooling, put it into an autoclave, add a solution made of acetic acid and ammonium acetate, take out the carrier at 165°C and 0.6MPa for 14 hours at constant temperature and pressure, wash it with distilled water until it is neutral, and then roast it at 300°C for 3 hours. After cooling, the desired carrier is obtained. The physical characteristics of the carriers prepared in each embodiment are shown in Table 1. Catalyst preparation:
[0024] With Na containing the equivalent of 6.35 g palladium 2 PdCl 4 and HAuCl equivalent to 2.96 g of gold 4 Prepare 450ml of aqueo...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com