Cutting tool with coating and preparation method thereof

A cutting tool and coating technology, which is applied in the field of coated cutting tools and its preparation, can solve the problems of large residual stress, poor bonding force between the coating and the gradient coating on the substrate, and reduce the hardness of the coating, so as to suppress excessive The effect of growth, uniform hardness distribution, and stable coating hardness

Active Publication Date: 2022-07-12
GANZHOU ACHTECK TOOL TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, the current coated tools have the following problems: First, during the growth process of the TiAlN coating, as the thickness increases, the coating grains will also grow, thereby reducing the hardness of the coating itself; Due to the large residual stress caused by the different material properties between the material and the substrate, the bonding force between the coating and the substrate and the gradient coating is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cutting tool with coating and preparation method thereof
  • Cutting tool with coating and preparation method thereof
  • Cutting tool with coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0040] The embodiments of the present invention are described below through specific specific examples, and those skilled in the art can easily understand other advantages and effects of the present invention from the contents disclosed in this specification. The present invention can also be implemented or applied through other different specific embodiments, and various details in this specification can also be modified or changed based on different viewpoints and applications without departing from the spirit of the present invention.

[0041] see Figure 1-3 , an embodiment of the present application is a coated cutting tool, which includes a tool substrate 1 and a coating layer 2 .

[0042] The tool base body 1 is made of cemented carbide, titanium-based carbonitride or ceramic material.

[0043] The coating layer 2 is coated on the surface of the tool base 1, and has a multi-layer structure, including TiAlN gradient coating 22, TiAlOCN layer 23 and α-Al sequentially fro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Microhardnessaaaaaaaaaa
Thicknessaaaaaaaaaa
Microhardnessaaaaaaaaaa
Login to View More

Abstract

The cutting tool with the coating comprises a tool base body and coating layers formed on the tool base body in a sequentially deposited mode through a CVD method, each coating layer is of a multi-layer structure and sequentially comprises a TiAlN gradient coating and a TiAlN gradient coating from inside to outside, the TiAlN gradient coating is represented by the general formula Ti1-xAlxN, x is larger than or equal to 0.5 and smaller than or equal to 0.9, and x is larger than or equal to 0.5 and smaller than or equal to 0.9. The Al content in the TiAlN gradient coating is increased in a gradient manner from low to high from the side close to the cutter base body to the side far away from the cutter base body; the composite material comprises an AlOCN layer, a TiAlOCN layer and an alpha-Al2O3 coating, and the alpha-Al2O3 coating is provided with an integral fiber texture. According to the cutting tool and the preparation method thereof, the coating hardness is high, distribution is uniform, and the binding force between the coating and the base body is high.

Description

technical field [0001] The invention belongs to the field of cutting tool production and manufacture, and in particular relates to a coated cutting tool and a preparation method thereof. Background technique [0002] The modern manufacturing industry is developing in the direction of high efficiency and environmental protection. The proportion of high-speed and dry machining is getting higher and higher, and higher requirements for the performance of tools are constantly being put forward. Ordinary carbide cutting tools can no longer meet the development trend of modern manufacturing. As a result, a variety of coated carbide tools have been developed and successfully used in modern manufacturing. [0003] At present, the use of chemical vapor deposition (CVD) method to prepare coated cemented carbide tools is still an important way for enterprise production, and the CVD method has the following advantages: thicker coatings can be prepared, the surface quality of the coating...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C16/34C23C16/30C23C16/32C23C16/36C23C16/40C23C16/44C23C16/06C22C29/08
CPCC23C16/34C23C16/30C23C16/403C22C29/08C22C29/067C23C16/44C23C16/32C23C16/36C23C16/06
Inventor 成伟邱联昌朱骥飞史海东谭卓鹏殷磊廖星文
Owner GANZHOU ACHTECK TOOL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products