Aluminum alloy wire surface reaction film treatment liquid and treatment process thereof

A surface reaction, aluminum alloy technology, applied in metal material coating process, cable/conductor manufacturing, electrical components, etc., can solve problems such as affecting product use effect, easy oxidation of insulating film, high cost copper layer surface, etc.

Pending Publication Date: 2022-05-13
WENZHOU ANNENG TECH CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Aluminum alloy wire core conductor is a necessary material for cables and control cables. Existing aluminum alloy wire electroplated copper products often have the following disadvantages: the price and weight of copper are higher than that of aluminum, the cost is high, and the surface of the copper layer is easily oxidized to form an insulating film ;Due to the great difference in the electrode potential of the metal contact interface of copper-plated products, when the copper-plated surface is damaged, it is easy to corrode or even rot, which greatly affects the use effect of the product
[0003] At this stage, aluminum is gradually used to replace copper, but the biggest disadvantage of aluminum is that the surface is easily oxidized to form film resistance. Therefore, it is particularly important to carry out anti-corrosion treatment on the surface of aluminum alloy materials in cable structures.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy wire surface reaction film treatment liquid and treatment process thereof
  • Aluminum alloy wire surface reaction film treatment liquid and treatment process thereof
  • Aluminum alloy wire surface reaction film treatment liquid and treatment process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] This embodiment provides a surface reaction film treatment solution for aluminum alloy wire rods, which is mainly prepared from the following raw materials in parts by weight: 6 grams of octadecyltrimethylammonium bromide, 10 grams of polyalphaolefin, polyacetylene 18 grams, 8 grams of two (4-hydroxyphenyl) sulfones, 15 grams of 4-hydroxydodecanoic acid anilide, and 1000 grams of trichloroethane solution, the trichloroethane solution is 95 by mass ratio: 5 trichloroethane and absolute ethanol prepared by mixing.

[0038] The preparation method of above-mentioned treatment liquid is as follows:

[0039] Get 950 grams of trichloroethane, then add 50 grams of absolute ethanol into the trichloroethane, stir evenly, then octadecyltrimethylammonium bromide, polyalphaolefin, polyacetylene, bis(4- Add hydroxyphenyl) sulfone and 4-hydroxydodecanoic acid anilide according to the above ratio, and mix well.

[0040] This embodiment also provides a surface reaction film treatment ...

Embodiment 2

[0047]This embodiment provides a treatment solution for the surface reaction film of an aluminum alloy wire rod, which is mainly prepared from the following raw materials in parts by weight: 8 grams of octadecyltrimethylammonium bromide, 6 grams of industrial animal fat, polyaniline 16 grams, two (4-hydroxyphenyl) sulfones 6 grams, 15 grams of 4-hydroxy dodecanoic acid anilides, and 1000 grams of trichloroethane solution, the trichloroethane solution is 95 by mass ratio: 5 trichloroethane and absolute ethanol prepared by mixing.

[0048] The preparation method of above-mentioned treatment liquid is as follows:

[0049] Get 950 grams of trichloroethane, then add 50 grams of absolute ethanol to chloroform, stir evenly, then add octadecyltrimethylammonium bromide, industrial animal oil, polyaniline, bis(4-hydroxy Phenyl) sulfone and 4-hydroxydodecanoic acid anilide are added according to the above ratio, and mixed evenly.

[0050] This embodiment also provides a surface reactio...

Embodiment 3

[0057] This embodiment provides a treatment solution for the surface reaction film of aluminum alloy wire rods. The treatment solution is mainly prepared from the following raw materials in parts by weight: 6 grams of octadecyltrimethylammonium bromide, 10 grams of polyalphaolefin, industrial animals Fat 5 grams, polypyrrole 18 grams, bis(4-hydroxyphenyl) sulfone 8 grams, 4-hydroxydodecanoic acid anilide 10 grams, 4-hydroxyoctadecanoic acid anilide 8 grams, and trichloro 1000 grams of ethane solution, the chloroform solution is prepared by mixing trichloroethane and absolute ethanol with a mass ratio of 95:5.

[0058] The preparation method of above-mentioned treatment liquid is as follows:

[0059] Get 950 grams of chloroform, then add 50 grams of absolute ethanol to the chloroform, stir well, then add octadecyltrimethylammonium bromide, polyalphaolefin, industrial animal fat, polypyrrole, bis( 4-hydroxyphenyl) sulfone, 4-hydroxydodecanoic acid anilide, 4-hydroxyoctadecanoic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of aluminum alloy wire surface treatment, in particular to aluminum alloy wire surface reaction film treatment liquid and a treatment process thereof. According to the invention, the surface of the aluminum alloy wire is treated by adopting the treating fluid prepared from specific raw materials according to a specific ratio and a specific treatment process, so that micropores in the surface of a plating layer and the post-treated surface of metal can be effectively sealed and plugged, and harmful gas and corrosive media are prevented from invading; therefore, the phenomena of generation of trapping points on the surface of the coating and corrosion and yellowing of the coating are reduced.

Description

technical field [0001] The invention relates to the field of surface treatment of aluminum alloy wires, in particular to a treatment solution for surface reaction film of aluminum alloy wires and a treatment process thereof. Background technique [0002] Aluminum alloy wire core conductor is a necessary material for cables and control cables. Existing aluminum alloy wire electroplated copper products often have the following disadvantages: the price and weight of copper are higher than that of aluminum, the cost is high, and the surface of the copper layer is easily oxidized to form an insulating film ; Due to the great difference in the electrode potential of the metal contact interface of copper-plated products, when the copper-plated surface is damaged, it is easy to corrode or even rot, which greatly affects the use effect of the product. [0003] At this stage, aluminum is gradually used to replace copper, but the biggest disadvantage of aluminum is that the surface is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/02C23C22/78C25D5/48C25D7/06H01B13/22
CPCC23C22/02C23C22/78C25D5/48C25D7/0607H01B13/221
Inventor 种鹏蛟孔祥湾王鑫慧
Owner WENZHOU ANNENG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap