Carbon dioxide-based ionic antibacterial polyurethane as well as preparation method and application thereof

A carbon dioxide and ionic technology, applied in the field of carbon dioxide-based ionic antibacterial polyurethane and its preparation, polyurethane, to achieve good biological antibacterial properties, simple preparation method, and good structural adjustability

Inactive Publication Date: 2022-05-10
SUZHOU UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, currently CO 2 Base ionic polyurethane has not been reported yet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon dioxide-based ionic antibacterial polyurethane as well as preparation method and application thereof
  • Carbon dioxide-based ionic antibacterial polyurethane as well as preparation method and application thereof
  • Carbon dioxide-based ionic antibacterial polyurethane as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] This embodiment provides a carbon dioxide-based ionic antibacterial polyurethane, which is prepared through the following steps:

[0032] Dissolve 1 mmol CO in 10 mL DMSO 2 Derivatized ionic cyclic carbonate with imidazolium as cation and bromide as anion with addition of 1 mmol hexamethylenediamine and CO 2 Derivatized ionic cyclic carbonate 20 mol% DBU. The above precursor solution was poured into a round bottom flask, purged with nitrogen for 5 minutes to remove oxygen, then the temperature was raised to 80°C, stirred and reacted for 24 hours, washed with ethyl acetate for many times, precipitated and dried to obtain CO 2 Based on ionic polyurethane, the antibacterial rate against Staphylococcus aureus and Escherichia coli is over 99%.

[0033] CO in this example 2 The antibacterial effect of base ionic polyurethane on Escherichia coli is as follows: figure 1 shown. The comparison sample is a blank sample.

Embodiment 2

[0035] This embodiment provides a carbon dioxide-based ionic antibacterial polyurethane, which is prepared through the following steps:

[0036] Dissolve 0.5 mmol CO in 10 mL DMSO 2 Derivatized ionic cyclic carbonate with imidazole as the cation and iodide as the anion with addition of 0.5 mmol hexamethylenediamine and CO 2 Derivatized ionic cyclic carbonate 20 mol% DBU. The above precursor solution was poured into a round bottom flask, purged with nitrogen for 5 minutes to remove oxygen, then the temperature was raised to 80°C, stirred and reacted for 24 hours, washed with ethyl acetate for many times, precipitated and dried to obtain CO 2 Based on ionic polyurethane, the antibacterial rate against Staphylococcus aureus and Escherichia coli is over 99%.

Embodiment 3

[0038] This embodiment provides a carbon dioxide-based ionic antibacterial polyurethane, which is prepared through the following steps:

[0039] Dissolve 1 mmol CO in 10 mL DMSO 2 Derivatized ionic cyclic carbonate with imidazolium as the cation and tetrafluoroborate ion as the anion with the addition of 1 mmol hexamethylenediamine and CO 2 Derivatized ionic cyclic carbonate 20 mol% DBU. The above precursor solution was poured into a round bottom flask, purged with nitrogen for 5 minutes to remove oxygen, then the temperature was raised to 100°C, stirred and reacted for 24 hours, washed with ethyl acetate for many times, precipitated and dried to obtain CO 2 Based on ionic polyurethane, the antibacterial rate against Staphylococcus aureus and Escherichia coli is over 99%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides carbon dioxide-based ionic antibacterial polyurethane as well as a preparation method and application thereof. The preparation method comprises the following steps: taking ionic cyclic carbonate derived from carbon dioxide and a diamine compound as monomers, and carrying out polymerization reaction under the action of a catalyst to obtain the carbon dioxide-based ionic antibacterial polyurethane. The invention also provides the antibacterial polyurethane prepared by the preparation method. The preparation method of the carbon-dioxide-based ionic antibacterial polyurethane is simple and environmentally friendly, resource utilization of carbon dioxide is achieved, and the carbon-dioxide-based ionic antibacterial polyurethane has potential application prospects in the field of antibacterial high polymer materials.

Description

technical field [0001] The invention relates to a polyurethane, in particular to a carbon dioxide-based ionic antibacterial polyurethane and a preparation method thereof, belonging to the technical field of functional polymer materials. Background technique [0002] Although carbon dioxide (CO 2 ) have seriously affected the ecological environment and social development. But from the perspective of green chemistry, CO 2 It is a C1 raw material with abundant reserves, low price, non-toxic and renewable, green and environmental protection. After decades of development, CO 2 It has been transformed into a variety of high value-added chemical products, such as methanol, urea, carbamic acid, cyclic carbonate, polycarbonate, polyurethane and polyurea, etc. [0003] Currently, the CO 2 Converted into a polymer material with excellent performance is CO 2 One of the important ways of solidification and utilization. Among them, polyurethane exhibits excellent wear resistance, o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G71/04
CPCC08G71/04
Inventor 严锋周莹杰郭江娜
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap