Cellulose gelatin coating-based rotator cuff patch and preparation method thereof
A technology of cellulose and patch, applied in the field of making patch and rotator cuff patch, can solve problems such as foreign body reaction and local inflammation, and achieve good biocompatibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0040] Example 1 Preparation of mesh
[0041] The preparation method of cellulose electrospinning film comprises the following steps: 1.5g of cellulose acetate is added to a mixed solvent composed of 6mL N, N-dimethylacetamide (DMAc) and 4mL acetone, stirred for about 6h to form a uniform and transparent slurry. Under the condition of spinning rate of 0.4mL / h and spinning voltage of 10kV, the slurry electrospinning is formed into a film. The membrane was then immersed in LiOH aqueous solution (0.05mol / L) for 12 h, washed with deionized water, and dried in a vacuum oven at 70 °C for 12 h.
[0042] At 50 ~60 °C, dissolve astragalus extract in 5wt% gelatin solution and stir well to give Gel-astragalus extract solution, the concentration of astragalus extract is 5mg / ml. The pretreated cellulose electrospinning membrane was immersed in Gel-Astragalus extract solution, sonicated for 5min, and the cellulose electrospinning membrane was slowly lifted with forceps at a speed of 1 mm / s and ...
Embodiment 2
[0045] Example 2 Performance test
[0046] Animal experiment grouping: a. cellulose membrane group; b. cellulose gelatin coating group.
[0047] Weaving of the mesh: The mesh is sewn at both ends so that it is used to stitch the rotator cuff stumps and the humerus end to fix. The size of the patch after weaving is 10 mm long, 4 mm wide and 1 mm thick, which is suitable for the suturing model of the tendon under the rabbit gang. The sutured patch was biomechanically tested to meet the maximum needs of rabbit inferior muscle tears of about 130 N.
[0048] (1) 2.5-3.5kg New Zealand white rabbit, anesthetized shoulder joint skin, about 4cm parallel incision above the inferior tendon, layer by layer blunt separation, exposing the inferior tendon. The inferior muscle is excised close to the humerus stop point and the stump and bone surface are rested.
[0049] (2) Make 2 1mm bone passages at the humerus stop point, cross the stump of the inferior muscle, and stitch the suture back to th...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com