Preparation process of rubber and plastic heat insulation material

A thermal insulation and preparation technology, which is applied in the field of rubber and plastic thermal insulation material preparation technology, can solve the problems that thermal insulation materials cannot meet thermal insulation, water resistance, fire prevention, poor comprehensive performance, and small stamping resistance at the same time. Conducive to environmental protection, long service life, good stamping resistance effect

Pending Publication Date: 2022-02-18
合肥汇东橡塑有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem that the heat insulation materials in the prior art cannot meet the performance requirements of heat insulation, water resistance, and fire prevention at the same time, and have low strength, no compression resistance, small stamping resistance, easy aging, and no durability. Insufficient and other problems, and proposed a rubber-plastic thermal insulation material preparation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The preparation process of a kind of rubber and plastic thermal insulation material proposed by the present invention comprises the following steps:

[0022] S1. After cleaning, crushing and removing impurities from recycled waste foam plastics, recycled plastic granules are added, and the solvent obtained by mixing naphtha, heavy diesel oil and cyclohexanone with a quality of 3:3:1 is added and stirred until completely dissolved. The amount of addition is 15% of the total amount of recycled plastic particles, and then silicone rubber, cyclohexyl methacrylate and diethylene glycol dibenzoate are added to stir and mix evenly to obtain a mixed main ingredient. Control the recycled plastic particles, silicone rubber, formazan The mass ratio of cyclohexyl acrylate and diethylene glycol dibenzoate is 70:30:1:1;

[0023] S2, in parts by weight, weigh 100 parts of mixed main ingredients, 28 parts of thermal insulation fillers, 5 parts of epoxy soybean oil, 3 parts of oleic aci...

Embodiment 2

[0026] S1. After cleaning, crushing and removing impurities from recycled waste foam plastics, recycled plastic granules are added, and the solvent obtained by mixing naphtha, heavy diesel oil and cyclohexanone with a quality of 4:4:1 is added and stirred until completely dissolved. The amount of addition is 45% of the total amount of recycled plastic particles, and then silicone rubber, cyclohexyl methacrylate and diethylene glycol dibenzoate are added to stir and mix evenly to obtain a mixed main ingredient, and the recycled plastic particles, silicone rubber, formazan The mass ratio of cyclohexyl acrylate and diethylene glycol dibenzoate is 40:19:1:1;

[0027] S2, in parts by weight, weigh 110 parts of mixed main ingredients, 34 parts of thermal insulation fillers, 8 parts of epoxy soybean oil, 5 parts of oleic acid amide, 3 parts of stearic acid, 3.5 parts of sulfur, 3 parts of antioxidant, 4 parts of fuel, 6.5 parts of blowing agent, wherein, the thermal insulation filler...

Embodiment 3

[0030] S1. After cleaning, crushing and removing impurities from recycled waste foam plastics, recycled plastic granules are added, and the solvent obtained by mixing naphtha, heavy diesel oil and cyclohexanone with a quality of 5:5:1 is added and stirred until it is completely dissolved. The amount of addition is 75% of the total amount of recycled plastic particles, and then silicone rubber, cyclohexyl methacrylate and diethylene glycol dibenzoate are added to stir and mix evenly to obtain a mixed main ingredient. Control the recycled plastic particles, silicone rubber, formazan The mass ratio of cyclohexyl acrylate and diethylene glycol dibenzoate is 30:15:1:1;

[0031] S2, in parts by weight, weigh 120 parts of mixed main ingredients, 40 parts of thermal insulation fillers, 12 parts of epoxy soybean oil, 7 parts of oleic acid amide, 5 parts of stearic acid, 5 parts of sulfur, 5 parts of antioxidant, 5 parts of fuel, 8 parts of foaming agent, wherein the thermal insulation ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of heat insulation materials, particularly relates to a preparation process of a rubber and plastic heat insulation material, and aims to solve the problems that a heat insulation material in the prior art cannot meet the performance requirements of heat insulation, water resistance, fire prevention and the like at the same time, and is low in strength, not resistant to pressure, small in stamping resistance, easy to age, not durable, poor in comprehensive performance and the like. The preparation process of the rubber and plastic heat insulation material comprises the following steps: adding silicone rubber, cyclohexyl methacrylate and diethylene glycol dibenzoate into recycled waste foamed plastic, mixing, adding a heat insulation filler, epoxidized soybean oil, oleamide, stearic acid, sulfur, an antioxidant, a flame retardant and a foaming agent, and mixing to obtain the rubber and plastic heat insulation material. The obtained rubber and plastic heat insulation material has excellent heat insulation and heat preservation, sound absorption and noise reduction, fire prevention, flame retardance, moisture prevention, water prevention and the like, is high in strength, has good stamping resistance and aging resistance, is excellent in comprehensive performance and long in service life, and can be widely applied to the fields of buildings, metallurgy, chemical engineering, electric power and the like.

Description

technical field [0001] The invention relates to the technical field, in particular to a preparation process of rubber and plastic thermal insulation materials. Background technique [0002] Thermal insulation materials refer to materials with a thermal conductivity of less than 0.14W / (m K) when the average temperature is equal to or less than 623K (350°C), and usually have the characteristics of light weight, looseness, porosity, and small thermal conductivity. Thermal insulation materials It is widely used in construction, metallurgy, chemical industry, electric power and other fields. Using good thermal insulation technology and materials in industry and construction can often achieve twice the result with half the effort. Thermal insulation materials have the characteristics of low density, high flexibility, can collect excess heat, good randomness, no cavity, and can avoid tearing and falling off under negative wind pressure. [0003] With the increasing energy consump...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J9/10C08L101/00C08L83/04C08K5/101C08K5/103C08K3/34C08K3/36C08K7/28C08K5/20C08K5/09C08K3/06C08K5/098C08K5/36C08K3/38C08K5/3415C08K13/04
CPCC08J9/105C08J9/10C08J9/0023C08J9/0028C08J9/0033C08J9/0066C08J9/0061C08J9/0095C08J2399/00C08J2483/04C08J2491/00C08J2203/04
Inventor 王明兴
Owner 合肥汇东橡塑有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products