Rutile type flux-cored wire with yield strength exceeding 890 MPa

A rutile type, yield strength technology, applied in welding equipment, welding medium, metal processing equipment, etc., can solve the problems of poor welding processability, poor low temperature toughness of mechanical properties, and strength that cannot meet the welding requirements of 890MPa steel, and achieves welding manufacturability. Excellent, stable welding arc effect

Active Publication Date: 2021-12-17
725TH RES INST OF CHINA SHIPBUILDING INDAL CORP
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to its high content of diffusible hydrogen, it is easy to produce welding cold cracks and poor mechanical properties, especially low-temperature toughness, which affects its large-scale promotion and use in high-strength steel welding, especially the welding of ultra-high-strength steel with a strength exceeding 890MPa.
[0005] CN 101323057A discloses a patent for a metal powder cored flux-cored welding wire with a yield strength exceeding 690MPa. This welding wire cannot meet the requirements of all-position welding, and its strength cannot meet the requirements of 890MPa steel welding
[0006] CN 110076477 A, discloses a metal powder cored wire with a multi-pass welding deposited metal to obtain a multi-phase split microstructure and high strength and toughness. The maximum yield strength of the weld metal can only reach 860MPa, and it cannot meet the requirements of all-position welding
[0007] Patent application number 20150378935.8 and publication number CN 14959748A disclose a low-temperature high-strength steel flux-cored welding wire for marine engineering. The yield strength is about 500MPa and the tensile strength is less than 670MPa, which is difficult to meet the welding requirements of 890MPa steel.
[0008] CN 110936060 A The present invention discloses a basic high-strength steel flux-cored welding wire, the highest yield strength of which is only 797MPa, and the basic flux-cored welding wire has the problem of poor welding processability in all positions
[0009] Through the search of existing patents, there is currently no equal-strength matching rutile flux-cored wire suitable for welding low-alloy steels with a yield strength exceeding 890MPa and excellent all-position welding performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rutile type flux-cored wire with yield strength exceeding 890 MPa
  • Rutile type flux-cored wire with yield strength exceeding 890 MPa
  • Rutile type flux-cored wire with yield strength exceeding 890 MPa

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] Below in conjunction with specific embodiment the present invention is described in further detail:

[0017] A rutile-type flux-cored welding wire suitable for welding low-alloy high-strength steels with a yield strength exceeding 890MPa. It is composed of a steel strip wrapped around the flux core and a flux core filled in it. There is no gap, that is, the form of seamless flux-cored welding wire is adopted, wherein the filled flux core contains slagging agent, arc stabilizing agent, alloying agent, etc., relative to the total weight of the welding wire, the filling rate of the filled flux core is 14.5-15.5%, including Has the following components:

[0018] C:0.03-0.09%, Si:0.3-0.8%, Mn:1.2-2.2%, Ni:0.5-1.5%, Co:1.0-3.5%, Ta:0.020–0.045%, REM (rare earth alloy):0.2- 0.5%, TiO 2 :2.0–4.0%, SiO 2 :0.2-0.5%, ZrO 2 :1.0–3.0%, K 2 O:0.2-0.4%; the remainder is Fe and other unavoidable impurities.

[0019] C can effectively improve the strength of the weld metal, but if...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

A rutile type flux-cored wire with the yield strength exceeding 890 MPa is composed of a steel belt wrapping a flux core and the flux core filling the steel belt. The flux core comprises, by weight, 0.03%-0.09% of C, 0.3%-0.8% of Si, 1.2%-2.2% of Mn, 0.5%-1.5% of Ni, 1.0%-3.5% of Co, 0.020%-0.045% of Ta, 0.2%-0.5% of rare earth alloy, 2.0%-4.0% of TiO2, 0.2%-0.5% of SiO2, 1.0%-3.0% of ZrO2, 0.2%-0.4% of K2O, and the balance Fe and other inevitable impurities. The welding wire adopts 80% Ar + 20% CO2 mixed gas for shielded welding, and has the characteristics that the yield strength of weld metal exceeds 890 MPa, the low-temperature impact toughness is larger than 47 J at the temperature of -40 DEG C, diffusible hydrogen is smaller than 2 ml / 100 g, the welding arc is stable, and the all-position welding manufacturability is excellent.

Description

technical field [0001] The invention relates to the field of welding materials, in particular to a rutile flux-cored welding wire with a yield strength exceeding 890 MPa. Background technique [0002] With the enlargement of engineering equipment, the problem of increasing the structural weight caused by increasing the wall thickness and increasing the bearing capacity is becoming more and more prominent. Improving the strength of materials is an important way to reduce the weight of equipment. The development of high-end manufacturing The demand for ultra-high-strength steel is increasing, and low-alloy steel with a yield strength exceeding 890MPa, as a typical ultra-high-strength steel, has begun to be applied in batches. [0003] A breakthrough in the key technology of ultra-high-strength steel welding with a yield strength exceeding 890 MPa can effectively control the construction quality and precision of large-scale engineering equipment, reduce weight, save costs, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/02B23K35/30
CPCB23K35/0266B23K35/3053
Inventor 张晓王亚彬张文军
Owner 725TH RES INST OF CHINA SHIPBUILDING INDAL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products